WO2014096416A2 - Bidirectional shape-memory polymer, method of its production and its use - Google Patents
Bidirectional shape-memory polymer, method of its production and its use Download PDFInfo
- Publication number
- WO2014096416A2 WO2014096416A2 PCT/EP2013/077831 EP2013077831W WO2014096416A2 WO 2014096416 A2 WO2014096416 A2 WO 2014096416A2 EP 2013077831 W EP2013077831 W EP 2013077831W WO 2014096416 A2 WO2014096416 A2 WO 2014096416A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- domains
- temperature
- shape
- polymer
- bsmp
- Prior art date
Abstract
Description
Claims