US20060057377A1 - Electrospun electroactive polymers - Google Patents

Electrospun electroactive polymers Download PDF

Info

Publication number
US20060057377A1
US20060057377A1 US11/017,546 US1754604A US2006057377A1 US 20060057377 A1 US20060057377 A1 US 20060057377A1 US 1754604 A US1754604 A US 1754604A US 2006057377 A1 US2006057377 A1 US 2006057377A1
Authority
US
United States
Prior art keywords
polymers
polymer
group
electroactive
pvdf
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/017,546
Inventor
Joycelyn Harrison
Kristin Burney
Zoubeida Ounaies
Cheol Park
Emilie Siochi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
National Aeronautics and Space Administration NASA
Original Assignee
National Aeronautics and Space Administration NASA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by National Aeronautics and Space Administration NASA filed Critical National Aeronautics and Space Administration NASA
Priority to US11/017,546 priority Critical patent/US20060057377A1/en
Assigned to ADMINISTRATOR OF THE NATIONAL AERONAUTICS AND SPACE ADMINISTRATION, UNITED STATED OF AMERICA AS REPRESENTED BY THE reassignment ADMINISTRATOR OF THE NATIONAL AERONAUTICS AND SPACE ADMINISTRATION, UNITED STATED OF AMERICA AS REPRESENTED BY THE ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: UNIVERSITIES SPACE RESEARCH ASSOCIATION
Assigned to ADMINISTRATOR OF THE NATIONAL AERONAUTICS AND SPACE ADMINISTRATION, AS REPRESENTED BY UNITED STATES OF AMERICA, THE reassignment ADMINISTRATOR OF THE NATIONAL AERONAUTICS AND SPACE ADMINISTRATION, AS REPRESENTED BY UNITED STATES OF AMERICA, THE ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: VIRGINIA COMMONWEALTH UNIVERSITY
Assigned to UNITED STATES OF AMERICA AS REPRESENTED BY THE ADMINISTRATOR OF THE NATIONAL AERONAUTICS AND SPACE ADMINISTRATION reassignment UNITED STATES OF AMERICA AS REPRESENTED BY THE ADMINISTRATOR OF THE NATIONAL AERONAUTICS AND SPACE ADMINISTRATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BURNEY, KRISTIN J., HARRISON, JOYCELYN S., SIOCHI, EMILIE J.
Publication of US20060057377A1 publication Critical patent/US20060057377A1/en
Abandoned legal-status Critical Current

Abstract

Electroactive polymers are produced via electrospinning. The induction of electroactivity via electrospinning can be utilized with one or more soluble polymers with polarizable moieties. Suitable polymer classes include but are not limited to polyimides, polyamides, vinyl polymers, polyurethanes, polyureas, polythioureas, polyacrylates, polyesters, and biopolymers. Any one or more solvents sufficient to dissolve the one or more polymers of interest and make a spinnable solution can be utilized. The polymer can be electrospun into fiber and fibrous nonwoven mat. The electroactive polymer can be doped with inclusions, such as nanotubes, nanofibers, and piezoceramic powders for dielectric enhancement The availability of electroactive polymer fibers and fibrous nonwoven mat will enable many new applications for electroactive polymers.

Description

    CLAIM OF BENEFIT OF PROVISIONAL APPLICATION
  • Pursuant to 35 U.S.C. § 119, the benefit of priority from provisional application having U.S. Ser. No. 60/530,637, filed on Dec. 19, 2003, is claimed for this nonprovisional application.
  • STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OF DEVELOPMENT
  • The invention described herein was made in part by employees of the United States Government and may be manufactured and used by and for the Government of the United States for governmental purposes without the payment of any royalties thereon or therefore.
  • BACKGROUND OF THE INVENTION
  • 1. Field of the Invention
  • The present invention relates generally to the production of electroactive polymers via electrospinning. It relates in particular to the induction of the polar phase in electroactive polymers, and the spontaneous orientation of dipoles in a single step process. These materials have widespread application in numerous fields, including aerospace, biomedical, clothing, and defense.
  • 2. Description of the Related Art
  • Due to their exceptional thermal, mechanical, and dielectric properties, polyimides are widely utilized, such as for matrix materials in composite aircraft components and as dielectric materials in microelectronic devices. Further, electroactive polymers have properties that are advantageous in numerous fields. Unfortunately, current methodology for producing electroactive polymers entails melt-pressing of the polymer at high temperatures, followed by stretching and corona-poling at high electric field strengths in order to produce the polar phase and electroactive behavior. This current process is labor-intensive and time-consuming, and requires large equipment that is complex to maintain.
  • Currently, polyvinylidene fluoride (PVDF) is the only commercially available piezoelectric polymer. PVDF is ferroelectric, having a polar axis that can be reoriented when an electric field is applied, and piezoelectric, when subjected to mechanical stress, changing its electrical polarization, or vice versa, with a change in electrical polarization resulting in mechanical movement. PVDF exhibits piezoelectricity after being subjected to a poling process which applies a high electric field to force molecular dipole alignment. PVDF can exist in several solid state phases, α, β, δ, and γ. The β-phase is of most importance because it is this phase that shows the largest electroactive response. The different phases can be attained by application of mechanical, thermal, or electrical stress depending on the initial and desired state of the polymer. The process that leads to the β-phase formation is labor intensive and time consuming, requiring initial melt processing and drawing into a film, followed by further stretching of the film at an elevated temperature either uniaxially or biaxially to induce the polar phase. Finally, it is passed under corona wires at high voltage to cause the induced dipoles to orient. PVDF has the potential to be used in many applications due not only to its electroactive properties but also because it is lightweight, flexible, tough and conformable. In addition, it possesses significant resistance to fatigue, abrasion, deformation, chemicals, and solar radiation. These properties make it an attractive material for aerospace as well as medical applications.
  • In the fiber-spinning process known as electrospinning, a high voltage is applied to a polymer in solution to create nanofibers and nonwoven mats. The polymer solution is loaded into a syringe, and high voltage is applied to the needle of the syringe. Charge builds up on a droplet of solution that is suspended at the tip of the syringe needle. Gradually, as this charge overcomes the surface tension of the solution, this droplet elongates and forms a Taylor cone. Finally, the solution exits out of the tip of the Taylor cone as a jet, which travels through the air to its target medium. While traveling, the solvent evaporates, leaving fibers. Overall, electrospinning is advantageous for many reasons. It is simple, and the technique is fast and easy to run. Only a small amount of material is required, and there is very little waste. The products of this process also have advantages over currently available materials; the fibers are very thin and have a high length to diameter ratio, which provides a very large surface area per unit mass. Finally, the process is versatile. Fibers can be spun onto any shape using a wide range of polymers. While electrospinning is an advantageous processing method to apply to polymers, it has not been applied for the purpose of producing electroactive polymers. An additional advantage of electrospinning is the ability to produce fibers and fibrous nonwoven mats; current methods for the production of electroactive polymers generally produce films.
  • While electroactive polymers themselves embody many useful properties, doping electroactive polymers with inclusions, such as nanotubes, nanofibers, and piezoceramic powders for dielectric enhancement is advantageous. Carbon nanotubes have become increasingly interesting due to their very unique properties: high tensile strength and modulus, high electrical conductivity, and high thermal conductivity.
  • SUMMARY OF THE INVENTION
  • It is accordingly a primary object of the present invention to overcome the difficulties and avoid the inadequacies presented by existing processes for the production of electroactive polymers. The present invention produces electroactive polymers via electrospinning. The induction of electroactivity via electrospinning can be utilized with one or more soluble polymers with polarizable moieties. Suitable polymer classes include but are not limited to polyimides, polyamides, vinyl polymers, polyurethanes, polyureas, polythioureas, polyacrylates, polyesters, and biopolymers. The polyimides include but are not limited to 2,6-bis(3-aminophenoxy)benzonitrile ((β-CN)APB)/4,4′oxydiphthalic anhydride (ODPA) ((β-CN)APB-ODPA) and an amorphous polyimide such as amorphous polyetherimide (such as the commercially available Ultem®). The polyamides include but are not limited to odd-numbered nylons. The vinyl polymers include but are not limited to PVDF, PVDF/TrFE (copolymer of vinylidene fluoride and trifluoroethylene), poly(vinyl alcohol) (PVA), a graft elastomer such as that claimed in U.S. Pat. No. 6,515,077, and vinyl copolymers. The polyacrylates include but are not limited to poly(methyl methacrylate) (PMMA). The biopolmers include but are not limited to polypeptides and keratin. Any one or more solvents sufficient to dissolve the one or more polymers of interest and make a spinnable solution can be utilized. Suitable solvents include but are not limited to N,N-Dimethylformamide (DMF), N,N-Dimethylacetamide (DMAc), N-methylpyrrolidinone (NMP), toluene, and cosolvents including but not limited to DMF/acetone. The polymer can be electrospun into fiber and fibrous nonwoven mat forms. The availability of electroactive polymer fibers and fibrous nonwoven mat will enable many new applications for electroactive polymers.
  • The present invention allows for the production of electroactive polymers using a simple set-up and a processing method that is fast and easy to run. Additionally, electroactive fibers can be created that are only nanometers in diameter. In situ induction of polar phase and spontaneous dipolar orientation of electroactive polymers by a single step electrospinning process produces electroactive polymers from a polymer solution. The need for direct contact or corona filed poling is eliminated, resulting in arc-free processing. Further, nanofibers and fibrous nonwoven mats are produced with minimal pre- and post-processing. Enabling materials are provided for a wide expanse of applications in such fields as aerospace, biomedical, military and environmental.
  • Additional objects and advantages of the present invention are apparent from the drawings and specification which follow.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1 is a schematic of one embodiment of an electrospinning apparatus.
  • FIG. 2 is a schematic of one embodiment of an electrospinning apparatus.
  • FIG. 3 illustrates Differential Scanning Calorimetry (DSC) measurements for PVDF dissolved in DMF.
  • FIG. 4 illustrates X-ray Diffraction (XRD) results for PVDF dissolved in DMF.
  • FIG. 5 illustrates Infrared Spectroscopy (IR) results for PVDF dissolved in DMF.
  • FIG. 6 illustrates Thermally Stimulated Current (TSC) results for PVDF dissolved in DMF.
  • FIG. 7 illustrates the size and proportion of fibers versus droplets produced for PVDF dissolved in DMF, for varying PVDF concentrations.
  • FIG. 8 illustrates the results for voltage variation for PVDF dissolved in DMF.
  • FIG. 9 illustrates results for PVDF dissolved in DMF, for distance variation between needle and collector.
  • FIG. 10 illustrates results for PVDF dissolved in DMF, for varying infusion rates.
  • DETAILED DESCRIPTION OF THE INVENTION
  • According to the process of the present invention, a solution is provided which comprises one or more polymers having polarizable moieties dissolved in a solution. Polymers with polarizable moieties have asymmetric strong dipoles. Suitable polymer classes include but are not limited to polyimides, polyamides, vinyl polymers, polyurethanes, polyureas, polythioureas, polyacrylates, polyesters, and biopolymers. The polyimides include but are not limited to 2,6-bis(3-aminophenoxy)benzonitrile ((β-CN)APB)/4,4′oxydiphthalic anhydride (ODPA) ((β-CN)APB-ODPA) and amorphous polyimides such as amorphous polyetherimide (such as the commercially available Ultem®). The polyamides include but are not limited to odd-numbered nylons. The vinyl polymers include but are not limited to PVDF, PVDF/TrFE (copolymer of vinylidene fluoride and trifluoroethylene), poly(vinyl alcohol) (PVA), a graft elastomer such as that claimed in U.S. Pat. No. 6,515,077, and vinyl copolymers. The polyacrylates include but are not limited to poly(methyl methacrylate) (PMMA). The biopolmers include but are not limited to polypeptides and keratin. Any one or more solvents sufficient to dissolve the one or more polymers of interest and make a spinnable solution can be utilized. Suitable solvents include but are not limited to N,N-Dimethylformamide (DMF), N,N-Dimethylacetamide (DMAc), N-methylpyrrolidinone (NMP), toluene, and cosolvents including but not limited to DMF/acetone.
  • Doping the one or more polymers with inclusions, such as nanotubes, nanofibers, and piezoceramic powders for dielectric enhancement would be advantageous. The inclusions can be induced prior to electrospinning using processes known in the art.
  • Referring now to the drawings, and more particularly to FIG. 1, an electrospinning apparatus, generally known in the art, is referenced generally by numeral 10. A housing 110, such as a benchtop fume hood having a ventilated shell, encloses the entire electrospinning process, and ensures protection from hazardous solvent fumes as well as electric fields. A high voltage supply 120 (such as that manufactured by Spellman High Voltage Electronics Corp.) charges the polymer solution contained in a syringe (such as that manufactured by Becton Dickinson) with a voltage in the range of approximately 0 to 30 kilovolts (kV). The voltage can be applied to the syringe needle 130 via an alligator clip 140 or other suitable connection. At a predetermined distance from the needle 130 tip (generally approximately 3-10 inches), a grounded collector 150 is suspended so that the collector 150 is generally approximately perpendicular to the needle 130. The collector can be customized in size and shape depending on the particular morphology and pattern desired. Grounding is required, although the collector 150 may be positioned between the needle 130 tip and ground. Any material for the collector is suitable, including both conductive and nonconductive materials. Examples of suitable materials include but are not limited to glass and metals, wherein the metal may be coated, such as with Teflon®, to make material removal easier. The glass may also be coated, such as with Indium-Tin Oxide (ITO), for enhanced conductivity. Any material and associated coating is suitable, as long as a potential can be provided between the needle 130 tip and the collector 150 substrate. The charge on the solution eventually overwhelms the surface tension of the solution, and a jet is ejected from the needle 130 tip 140 in the direction of the collector 150. During jet travel, the solvent evaporates and the remaining solid polymer fiber is deposited on the collector 150. Fibers accumulate and spread on the collector 150, as long as the needle 130 tip is continually supplied with polymer solution, such as via a syringe infusion pump 160 (such as that manufactured by Fisher Scientific). It is advantageous for the solution to be infused at a selected rate automatically.
  • The spun product is allowed to dry until solvent-free. Drying time should be sufficient to allow solvent evaporation to occur. Drying may occur in a vacuum oven or at room temperature.
  • In an alternate embodiment, referenced generally in FIG. 2 by the numeral 200, the electrospinning apparatus comprises a rotating collector 210. The collector 210 is attached to base 220 and rotates about its longitudinal axis, such as via a motor 230 and shaft 240 coupling. Alternatively, the collector 210 can move laterally along the base, such as by a lead screw 250 attached to a second motor 260 to allow for full coverage of the collector 210. Again, various collector 210 geometries can be utilized as needed for particular morphology and pattern applications. Examples include but are not limited to a rotating plate, cylinder, or patterned substrate. Rotation can occur at steady or variable speed, and can be utilized to induce preferential alignment of the fibers.
  • An additional embodiment of the electrospinning apparatus includes the incorporation of a heater to regulate temperature of the electrospinning environment.
  • The polymer solution is electrospun to produce fibers of approximately 10 nm to approximately 10 μm in diameter, as well as fibrous nonwoven mats of customizable size, shape, fiber orientation, and thickness. Depending on the spun product desired, the collector 160 is designed accordingly. Parameters in the processing include infusion rate, applied voltage, collector's material and rotation and/or translation speed, distance between the needle 140 tip and collector 160, and drying time.
  • Parameters sufficient to form dry, uniform diameter solid fibers are preferred, and are customized based on the polymer of interest. The concentration of polymer in solution generally correlates with fiber size, with lower concentrations producing smaller diameter fibers. Additionally, the size and proportion of fibers versus droplets generally increase with increase in concentration. Voltage will generally be in the approximate range of 5 to 30 kV, and is adjusted to achieve the volume and diameter of fibers desired. Distance between the needle 140 tip and collector 160 will generally be 3-10 inches. It is desirable to have an infusion rate that delivers the appropriate amount of solution, with balancing of the infusion rate and applied voltage to maintain a pendant drop of solution at the tip of the nozzle. Infusion rates will generally be approximately between 3 and 10 mL/hr.
  • The following examples are illustrative of the present invention, and are not intended to limit the ambit thereof.
  • EXAMPLE 1 (PVDF/DMF)
  • PVDF pellets (MW 530,000, Aldrich Chemical Company, Inc.) were dissolved into solvent DMF at a concentration of 30 weight percent (wt %) PVDF. The solutions were electrospun into fibers using the apparatus illustrated in FIG. 2. The polymer resins were delivered to the system using a plastic syringe (Becton Dickinson) equipped with an 18-gauge blunt needle tip. Metered infusion of the solution into the system was accomplished with a digitally-controlled syringe pump (KD Scientific, model 100). Voltage was applied to this supply system via an alligator clip connected to the needle and to a high voltage power supply unit (Spellman High Voltage Electronics Corporation, model CZE 1000R). The grounded target was a rotating drum, which imparted some degree of fiber orientation to the collected mat. For these experiments, the infusion pump was set to deliver polymer resin at a rate of 6.0 milliliters per hour (mL/hr). Distance between the needle tip and the grounded target was held constant at approximately 23 centimeters (cm). The applied voltage was varied at 10 kV, 15 kV, and 20 kV, resulting in applied electric fields of 0.44 kV/cm, 0.66 kV/cm, and 0.87 kV/cm, respectively. Fiber morphology and size were assessed by optical microscopy (OM) and scanning electron microscope (SEM) (JEOL, model 6400).
  • Differential Scanning Calorimetry Analysis (DSC)
  • Differential scanning calorimetry (DSC) measurements were completed using a Perkin Elmer Pyris 1 calorimeter. Film and electrospun mat samples ranged in mass from 3.0 to 6.0 milligrams (mg); PVDF pellet and commercial film samples were 5.0 to 11.4 mg. The thermal program consisted of heating from −65° C. to 250° C. at a rate of 10° C./min. Heat flow was recorded for all samples. Melt temperature (Tm), defined as the temperature at the maximum of the endotherm, and heat of fusion (ΔH), defined as the area of the melt peak, were determined from the first heat.
  • DSC analysis was used to indicate degree of crystallinity and specific crystal form present in the PVDF samples. Table 1 summarizes the DSC results for β-phase PVDF (commercially-purchased stretched and poled film), α-phase PVDF (commercially purchased pellets), and electrospun fibers. It was observed that the value of the main melting point Tm for the 15 kV and 20 kV electrospun fibers was higher than that of the pellets and closer to that of the commercial PVDF films. Tm of the 10 kV electrospun fibers was similar to that of the α-phase pellets. This indicates that the 15 kV and 20 kV electrospun fibers exhibit β-phase. The same was true for the ΔH, where all three electrospun cases showed values comparable to the stretched and poled β-phase commercial films. DSC results for the three spun cases are summarized in FIG. 3, where samples are identified by applied voltage during electrospin processing.
    TABLE 1
    DSC results.
    First heat
    Material Form Tm (° C.) ΔH (J/g)
    MSI Poled β-form 165.763 53.954
    melt-cast, Film
    poled
    MSI Unpoled β- 168.270 59.687
    melt-cast, form Film
    unpoled
    Aldrich α-form Pellets 158.950 26.14
    Pellets
    30 wt % electrospun 154.260* 51.900
    Aldrich fibers (10 kV) 158.123
    in DMF
    30 wt % electrospun 156.099* 49.294
    Aldrich fibers (15 kV) 166.084
    in DMF
    30 wt % electrospun 157.083* 53.360
    Aldrich fibers (20 kV) 165.100
    in DMF

    *Shoulder on lower side of Tm.
  • As illustrated in FIG. 3, the DSC of the electrospun fibers exhibits a shoulder on the melt peak. This shoulder present on the low side of the melting temperature was more pronounced for the 15 kV and 20 kV cases and may indicate the co-existence of both α-phase and β-phase in varying proportion in the electrospun fibers. Since both processing conditions and thermal history influence melting temperature and heat of fusion of a polymer sample, other characterization techniques (such as FTIR, XRD and TSC below) were used to make more definitive conclusions.
  • X-Ray Diffraction Analysis (XRD)
  • X-ray diffraction (XRD) was performed using a Philips Analytical X'Pert Pro X-ray Diffraction System with a step size of 0.0080° 2θ and scan step time of 120 seconds. The range of interest for the measurements was for 2θ between 10 and 40°. The phases present in the films were determined by examining the characteristic absorption bands of the respective crystalline phases.
  • An assessment of the degree and type of crystallinity of the three electrospun samples using XRD data supports the findings of the DSC data. FIG. 4 illustrates that the peaks in all four cases (pellets, 10 kV, 15 kV, and 20 kV) suggest that both a-phase and β-phase are present in the fibers. The data also show that the 2θ peak location and intensity depend on polymer processing conditions. Characteristic α-phase peaks are seen at 2θ values of 18°, 20°, and 27°. Characteristic β-phase peaks are located at 2θ values of 20.4° and 37°. All three electrospun cases show a decrease in α-phase character in favor of β-phase. In the 10 kV case, the 18° peak disappeared. The peak that was at 20° shifted to 20.4°, indicating a transformation from α to β. In comparison, the 15 kV case shows a much smaller β-phase peak at 20.4°, still displays a large α-phase peak at 18°, and exhibits no hint of a β-peak at 37°. Furthermore, none of the electrospun cases exhibit the characteristic α-phase peak 27°.
  • XRD data clearly confirm the DSC results. The presence of a shoulder on the low end of the melt peak seen in DSC corresponds to the finding by XRD that a second crystalline form is present in the electrospun fibers. This shoulder is attributed to β-form. In mixed systems, β form has smaller reflections than α-form, which are dominant, so detecting small amounts of β-form becomes difficult.
  • Fourier Transform Infrared Spectroscopic Analysis (FTIR)
  • Infrared spectroscopy (IR) was performed on the samples using a ThermoNicolet IR 300 Spectrometer. Data analysis was performed with Omnic version 6.2 software. The measurements were taken from 600-1500 wavenumbers (cm−1) with 128 scans performed per sample. Data analysis consisted of qualitative visual comparison of intensities of characteristic transmittance peaks for PVDF crystalline phases.
  • FIG. 5 further confirms that electrospinning induces formation of the β-phase in PVDF and suggests orientation of the β-phase. Characteristic α-phase peaks at 614, 762, 795, and 975 cm−1 are evident in only the α-phase and unpoled β-phase film samples. For clarity, peaks at 762, 795, and 975 cm−1 are detailed in the insets. α-phase peaks are absent in all three electrospun cases. Strong peaks at 840 and 1280 cm−1, which indicate β-phase PVDF, are present in all samples except the α-phase film sample. These peaks are nearly as strong for the electrospun cases as they are for the poled β-phase film sample. The similarity between the poled β-phase film and all three fiber cases suggests that electrospin processing causes orientation of the poled β-phase. Note that evidence of some α-phase in the unpoled β-phase film sample is unexpected but indicates incomplete conversion from α to β phase during stretching.
  • Thermally Stimulated Current Analysis (TSC)
  • A SETARAM TSC 3000, automated Thermally Stimulated Current (TSC) equipment, was used to track the relaxation processes in the polymeric films and fibers. Heating of the sample at a constant rate accelerates the real charge decay, which can be observed as a current release. The current as a function of temperature was measured by a sensitive electrometer connected to the electrodes. No additional poling was performed on any of the samples between initial electrospin processing and TSC analysis. All samples were subjected to the same cycle. The samples were heated from 25° C. to 150° C. at a rate of 2° C./min.
  • Thermally Stimulated Current (TSC) measures the release of stored dielectric polarization in the form of charge or current. Because piezoelectricity in PVDF arises from orientation polarization of the —CF2— dipoles in the polar phase, TSC analysis can be used to reveal the presence of this orientation polarization current peak. The peak was shown to shift from 90° C. to 130° C. as more perfect and thermally stable crystallites are formed [13]. A second peak, due to space charge release, typically occurs at higher temperatures.
  • FIG. 6 shows the depolarization current spectrum of the electrospun 15 kV fibers next to the current spectrum of a stretched, poled PVDF film (MSI). The depolarization current spectrum of the 15 kV sample is consistent with poled and stretched PVDF films. The peak centered at 120° C. is consistent with orientation polarization in β-phase PVDF, and is due to relaxation of dipoles in the crystalline regions. A second peak centered around 145° C. is most likely due to space charge, coupled with onset of crystallite melting.
  • To assess the potential piezoelectricity of the 15 kV fibers, the pyroelectric coefficient, p, was calculated using the following equation: p = I A T t
    where I is the depolarization current, A is the area of the electrode, and dT/dt is the heating rate during TSC. The pyroelectric coefficient was measured with respect to current released up to 140° C., since the peak of interest is the orientation polarization peak located below this temperature. The measured pyroelectric coefficient was 1.5×10−5 C./° C.−m2 for the 15 kV fibers. Values for stretched, poled PVDF are typically in the range of 2.0−3.5×10−5 C./° C.−m2.
  • EXAMPLE 2
  • PVDF solutions in the solvent DMF with and without single wall nanotubes (SWNTs) were electrospun at various concentrations, as outlined in Table 2. PVDF pellets (MW 530,000, Aldrich Chemical Company, Inc.) were dissolved into DMF at a concentration of 30 weight percent (wt %) PVDF. A SWNT stock solution (1% w/w) in DMF was prepared to mix with PVDF/DMF solution to prepare various compositions of SWNT/PVDF/DMF solutions. The solutions were electrospun into fibers using the apparatus illustrated in FIG. 2. The polymer resins were delivered to the system using a plastic syringe (Becton Dickinson) equipped with an 18-gauge blunt needle tip. Metered infusion of the solution into the system was accomplished with a digitally-controlled syringe pump (KD Scientific, model 100). Voltage was applied to this supply system via an alligator clip connected to the needle and to a high voltage power supply unit (Spellman High Voltage Electronics Corporation, model CZE 1000R). The grounded target was a rotating drum, which imparted some degree of fiber orientation to the collected mat. For these experiments, the infusion pump was set to deliver polymer resin at a rate of 6.0 milliliters per hour. Distance between the needle tip and the grounded target was held constant at approximately 23 centimeters (cm). The applied voltages were 10 kV, 15 kV, and 20 kV, resulting in applied electric fields of 0.44 kV/cm, 0.66 kV/cm, and 0.87 kV/cm, respectively. Fiber morphology and size were assessed by optical microscopy (OM) and scanning electron microscope (SEM) (JEOL, model 6400).
    TABLE 2
    Concentrations in wt % of solutions in DMF
    PVDF SWNT
    Wt % WT %
    15 0
    20 0
    25 0
    30 0
    35 0
    15 0.1
    15 1.0
    25 0.1
    25 0.2
  • The varying concentrations of PVDF and PVDF with SWNT shown in Table 2 were spun onto Indium-Tin Oxide (ITO) coated glass plates and standard glass microscope slides utilizing the electrospinning apparatus illustrated in FIG. 1. Numerous trials were competed with varying concentrations of PVDF and SWNTs. Voltage, distance between nozzle and grounding plate, infusion rate, and collection medium type were varied.
  • The 30 wt % PVDF was also spun onto a rotating roller to produce an oriented fibrous mat, using the apparatus of FIG. 2. The roller was a hollow metal cylinder fixed on an axis that rotated at varying speeds. The cylinder was moved from side to side as well, to ensure complete coverage of the length of the roller.
  • Once spun, on either plates or the roller, optical microscopy was completed at 100× and 200× magnification using an Olympus BH-2 optical microscope in conjunction with Scion Image, v. 1.62, software. These images were utilized to compare and observe trends as a function of electrospinning parameters.
  • Mats spun on a roller were dried in a vacuum oven at 60° C. overnight or over a weekend. The vacuum oven removed any remaining DMF solvent from the fibers. Solvent vapors were allows to flow over dry ice, were condensed into liquid form, and were then contained in a liquid trap. Once dried, the PVDF mats were prepared for Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TGA), and Dynamic Mechanical Analysis (DMTA) by cutting to appropriate size.
  • The concentration of PVDF in DMF solution correlated with fiber size. The lowest concentration, 15 wt %, produced wet fibers with a small diameter. The size and proportion of fibers versus droplets produced increased as concentration was increased, as shown in FIG. 7. It was determined that a concentration of 30 wt % PVDF produced the best quality fibers as determined by desirable morphological features such as the fiber dryness and the number of fibers present as compared to solution droplets. FIG. 7 also indicates that the substrate material had little effect on fiber formation.
  • Various electrospinning parameters were examined for the 30 wt % PVDF in DMF solution to determine the optimal conditions. Voltage was varied from 5 kilovolts (kV) to 30 kV. As is illustrated in FIG. 8, voltage affected the amount of fibers spun, the amount of solvent that was splattered on the slide, and the diameter of the fibers. Optimum fibers were produced at 10 kV.
  • FIG. 9 illustrates results for distance variation. Distance was varied from 5 to 13 inches. When the collecting plate was close to the syringe, the slides and the fibers growing off of the edges of the slides were wet. Solution splattering was also evident with short distances. As the distance was increased, the plate and fibers were less wet and splattering was minimized. In addition, fibers were thick and prominent. As a maximum distance of 13 inches between collecting plate and nozzle was exceeded, fewer fibers attached to the collecting plate; instead attaching to some other surface in the hood.
  • Infusion rate was not a dramatic factor in determining fiber morphology. However, in choosing an infusion rate, it was desirable to have a rate that delivered the appropriate amount of solution. The infusion rate must be balanced with applied voltage to maintain a pendant drop of solution at the tip of the nozzle. In addition, the appropriate infusion rate varied with solution viscosity. The infusion rate was varied from 3 to 10 mL/hr for 30 wt % PVDF. As can be seen in FIG. 10, an infusion rate between 6 mL/hr and 9 mL/hr produced fibers that did not exhibit excessive amounts of wet solution droplets. If infusion rate exceeded 9 mL/hr, the solution dripped out of the needle. Furthermore, if the infusion rate exceeded 6 mL/hr, the fibers produced were wet. For these reasons, 6 mL/hr was an optimal infusion rate.
  • Optimal conditions for 30 wt % PVDF were found to be a voltage of 10 kV, an infusion rate of 6 mL/hr, and a distance of 9 inches from the needle point to the collecting plate.
  • EXAMPLE 3
  • PVDF combined with carbon nanotubes was tested beginning with 0.1% SWNT in 15 wt % PVDF and 1.0% SWNT in 15 wt % PVDF. Small and few fibers formed. When the 1.0% SWNT was electrospun, black drops fell out of the solution as a result of the excessive concentration of SWNTs. A 0.1 % SMNT in 25 wt % PVDF spun well and was able to be spun onto a rotating roller, producing a nonwoven mat which was vacuum-dried at 60° C. A nonwoven mat was also produced from 0.2% SWNT in 25 wt % PVDF. Optimal conditions for the PVDF solutions with carbon nanotubes were slightly different depending on amount of carbon nanotubes and concentration of PVDF.
  • Although the present invention has been described relative to specific embodiments thereof, there are numerous variations and modifications that will be readily apparent to those skilled in the art in light of the above teachings. It is therefore to be understood that, within the scope of the appended claims, the invention may be practiced other than as specifically described.

Claims (33)

1. An electrospun electroactive polymer.
2. The electroactive polymer of claim 1, wherein said polymer is a fiber.
3. The electroactive polymer of claim 2, wherein said fiber has a diameter between approximately 10 nm and approximately 10 μm.
4. The electroactive polymer of claim 1, wherein said polymer is a fibrous nonwoven mat.
5. The electroactive polymer of claim 1, wherein said polymer is electrospun from a solution comprising one or more polymers having polarizable moieties dissolved in one or more solvents, wherein said one or more solvents dissolves the one or more polymers of interest to make a spinnable solution.
6. The electroactive polymer of claim 5, wherein said one or more polymers having polarizable moieties is selected from the group consisting of polymides, polyamides, vinyl polymers, polyurethanes, polyureas, polythioureas, polyacrylates, polyesters and biopolymers.
7. The electroactive polymer of claim 6, wherein said one or more polyimides is selected from the group consisting of 2,6-bis(3-aminophenoxy)benzonitrile ((β-CN)APB)/4,4′oxydiphthalic anhydride (ODPA) ((β-CN)APB-ODPA) and amorphous polyimide.
8. The electroactive polymer of claim 7, wherein said amorphous polyimide is amorphous polyetherimide.
9. The electroactive polymer of claim 6, wherein said one or more polyamides is an odd-numbered nylon.
10. The electroactive polymer of claim 6, wherein said one or more vinyl polymers are selected from the group consisting of polyvinylidene fluoride (PVDF), copolymer of vinylidene fluoride and trifluoroethylene (PVDF/TrFE), poly(vinyl alcohol) (PVA), graft elastomer, and vinyl copolymer.
11. The electroactive polymer of claim 6, wherein said one or more polyacrylates is poly(methyl methacrylate) (PMMA).
12. The electroactive polymer of claim 6, wherein said one or more biopolmers is selected from the group consisting of polypeptide and keratin.
13. The electroactive polymer of claim 5, wherein said one or more solvents is selected from the group consisting of N,N-Dimethylformamide (DMF), N,N-Dimethylacetamide (DMAc), N-methylpyrrolidinone (NMP), toluene, and cosolvent.
14. The electroactive polymer of claim 13, wherein said cosolvent is DMF/acetone.
15. The polymer of claim 1, further comprising inclusions for dielectric enhancement.
16. The polymer of claim 15, wherein said inclusions are selected from the group consisting of nanotubes, nanofibers, and piezoceramic powders.
17. The polymer of claim 16, wherein said nanotubes are selected from the group consisting of single-walled carbon nanotubes and multi-walled carbon nanotubes.
18. A process for producing polymeric materials for electroactive applications comprising electrospinning of a solution comprising one or more polymers having polarizable moieties dissolved in one or more solvents, wherein said one or more solvents dissolves the one or more polymers of interest to make a spinnable solution.
19. The process of claim 18, wherein said one or more polymers having polarizable moieties is selected from the group consisting of polyimides, polyamides, vinyl polymers, polyurethanes, polyureas, polythioureas, polyacrylates, polyesters and biopolymers.
20. The process of claim 19, wherein said one or more polyimides is selected from the group consisting of 2,6-bis(3-aminophenoxy)benzonitrile ((β-CN)APB)/4,4′oxydiphthalic anhydride (ODPA) ((β-CN)APB-ODPA) and amorphous polyimide.
21. The process of claim 20, wherein said amorphous polyimide is amorphous polyetherimide.
22. The process of claim 19, wherein said one or more polyamides is an odd-numbered nylon.
23. The process of claim 19, wherein said one or more vinyl polymers are selected from the group consisting of polyvinylidene fluoride (PVDF), copolymer of vinylidene fluoride and trifluoroethylene (PVDF-/TrFE), poly(vinyl alcohol) (PVA), graft elastomer, and vinyl copolymer.
24. The process of claim 19, wherein said one or more polyacrylates is poly(methyl methacrylate) (PMMA).
25. The process of claim 19, wherein said one or more biopolmers is selected from the group consisting of polypeptide and keratin.
26. The process of claim 18, wherein said one or more solvents is selected from the group consisting of N,N-Dimethylformamide (DMF), N,N-Dimethylacetamide (DMAc), N-methylpyrrolidinone (NMP), toluene, and cosolvent.
27. The process of claim 26, wherein said cosolvent is DMF/acetone.
28. The process of claim 18 wherein said solution further comprises inclusions for dielectric enhancement.
29. The process of claim 28, wherein said inclusions are selected from the group consisting of nanotubes, nanofibers, and piezoceramic powders.
30. The process of claim 18, wherein said polymeric material is a fiber.
31. The process of claim 30, wherein said fiber has a diameter between approximately 10 nm and approximately 10 μm.
32. The process of claim 18, wherein said polymeric material is a fibrous nonwoven mat.
33. A process for producing polymeric materials for electroactive applications, comprising the in situ induction of polar phase and spontaneous dipolar orientation of electroactive polymers via electrospinning a polymer solution, wherein said solution comprises one or more polymers having polarizable moieties dissolved in one or more solvents, wherein said one or more solvents dissolves the one or more polymers of interest to make a spinnable solution.
US11/017,546 2003-12-19 2004-12-18 Electrospun electroactive polymers Abandoned US20060057377A1 (en)