US20050136772A1 - Composite structures containing tissue webs and other nonwovens - Google Patents

Composite structures containing tissue webs and other nonwovens Download PDF

Info

Publication number
US20050136772A1
US20050136772A1 US10/745,327 US74532703A US2005136772A1 US 20050136772 A1 US20050136772 A1 US 20050136772A1 US 74532703 A US74532703 A US 74532703A US 2005136772 A1 US2005136772 A1 US 2005136772A1
Authority
US
United States
Prior art keywords
web
fibers
wiping product
meltblown
tissue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/745,327
Inventor
Fung-Jou Chen
Jeffrey Lindsay
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kimberly Clark Worldwide Inc
Original Assignee
Kimberly Clark Worldwide Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kimberly Clark Worldwide Inc filed Critical Kimberly Clark Worldwide Inc
Priority to US10/745,327 priority Critical patent/US20050136772A1/en
Assigned to KIMBERLY-CLARK WORLDWIDE, INC. reassignment KIMBERLY-CLARK WORLDWIDE, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CHEN, FUNG-JOU, LINDSAY, JEFFREY DEAN
Priority to AU2004314114A priority patent/AU2004314114B2/en
Priority to EP20040778113 priority patent/EP1697122B1/en
Priority to CNA2004800385193A priority patent/CN1898081A/en
Priority to KR1020067012473A priority patent/KR101107492B1/en
Priority to PCT/US2004/022440 priority patent/WO2005068179A1/en
Priority to BRPI0418013-5A priority patent/BRPI0418013A/en
Publication of US20050136772A1 publication Critical patent/US20050136772A1/en
Abandoned legal-status Critical Current

Abstract

The present invention discloses a disposable scrubbing product for use in household cleaning or personal care applications. In one embodiment, the present invention is directed to a cleaning tool including a handle and a rigid base to which the scrubbing product of the present invention may be attached to form a convenient cleaning tool. The scrubbing product of the invention is a multi-layer laminate product and generally includes at least two distinct layers, an abrasive layer and an absorbent fibrous layer such as a tissue layer made from papermaking fibers. The abrasive layer is formed primarily of polymeric fibers in a disordered or random distribution as is typical of fibers deposited in meltblown or spunbond processes so as to form an open, porous structure. In one embodiment, an anchoring agent, such as synthetic fibers, are incorporated into the tissue layer that form a bond with the abrasive layer when forming a laminate in accordance with the present invention.

Description

    BACKGROUND OF THE INVENTION
  • Abrasive scrubbing pads are commonly used for many cleaning and personal care practices. In general, scrubbing pads include a naturally occurring or manufactured abrasive material. Examples of typical abrasive materials commonly used in the past include pumice, loofah, steel wool, and a wide variety of plastic materials. A non-absorbent abrasive material is often combined with an absorbent sponge-like backing material in these products. For example, the abrasive material often forms a layer on a multi-layer product which also includes an absorbent layer of natural sponge, regenerated cellulose, or some other type of absorbent foamed product.
  • These scrubbing pads tend to be expensive, making them unsuitable for a disposable or single-use product. Due to the nature of the product use, however, the products can become fouled with dirt, grease, bacteria, and other contaminants after only one or two uses. As a result, consumers must replace these expensive scrubbing pads quite often in order to feel secure in the knowledge that they are using an uncontaminated cleaning pad.
  • Examples of abrasive cleaning articles have been described in the past. See, for example, International Published Application Number WO 02/41748, U.S. Pat. No. 5,213,588, and U.S. Pat. No. 6,013,349.
  • The present invention addresses these and other problems encountered with scrubbing pads in the past and is directed to disposable scrubbing pads and related wiping products which can provide a wide variety in level of abrasiveness, may be thin, comfortable and easy to hold, may have good absorbency, and may provide benefits not previously supplied in abrasive cleaning articles of the past.
  • SUMMARY OF THE INVENTION
  • The present invention is directed to a disposable scrubbing product for use in household cleaning or personal care applications, as well as industrial cleaning and other applications.
  • The scrubbing product of the invention is a multi-layer product and generally includes at least two distinct layers, an abrasive layer and an absorbent fibrous layer such as a layer of tissue made from papermaking fibers, a layer of coform, an airlaid web, or combinations thereof or other known cellulosic webs. The abrasive layer is formed primarily of coarse polymeric fibers in a disordered or random distribution as is typical of fibers deposited in meltblown or spunbond processes.
  • The abrasive layer may comprise, for instance, multifilamentary aggregate fibers formed by the partial coalescence of a plurality of polymer strands (i.e. the individual fibers produced by the process) during a meltblown process or other fiber-forming process to form an integral, fiber-like, generally non-circular structure in which substantially parallel polymeric filaments are joined along their sides. Such multifilamentary aggregates may have an effective diameter much greater than the individual strands normally obtained in meltblown or spunbond processes, and a complex cross-sectional shape more suitable for providing abrasion than can be achieved with conventional circular fibers, and can contribute to effective cleaning and abrasion.
  • In one embodiment of the present invention, for instance, the scrubbing product or wiping product includes a tissue web that is bonded to a meltspun web, such as a meltblown web or a spunbond web. The tissue web may have a first side and a second and opposite side and may contain pulp fibers and synthetic fibers. The meltspun web is attached to the first side of the tissue web and comprises polymeric fibers. According to the present invention, the meltspun web and the tissue web are combined together in a manner that causes the polymeric fibers of the meltspun web to bond with the synthetic fibers of the tissue web. Thus, by incorporating synthetic fibers into the tissue web, a composite material is formed having good structural stability even when wet. In particular, the synthetic fibers allow the tissue web to more firmly bond to the meltspun web.
  • In one embodiment, the synthetic fibers can bond more readily to the meltblown fibers than can the cellulosic fibers of the tissue web, and, in related embodiments, may stay bonded even when wet. Both the meltblown web and the synthetic fibers may comprise polymers that share common properties not shared with the cellulosic fibers, such as having a melting point below 200° C. or below 150° C., or being hydrophobic, or comprising at least one common monomer such as a vinyl group or ethylene or a derivative of maleic acid. In one embodiment, both the meltblown web and the synthetic fibers comprise a common polymer such as polyethylene, polypropylene, a polyester, and the like. In another embodiment, both the meltblown web and the synthetic fibers comprise a polymer from a common category selected from the following categories: polyamides, styrene copolymers, polyesters, polyolefins, vinyl acetate copolymers, EVA polymers, polymers derived from butadiene, polyurethanes, and silicone polymers. Common polymers or polymers from a common category may be present in both the meltblown web and in the synthetic fibers at a level of about 5% or greater by weight or about 10% or greater by weight, or about 20% or greater by weight. In another embodiment, both the meltblown web and the synthetic fibers comprise an elastomer, which may be present at a level of about 5% or greater by weight or about 10% or greater by weight in both the meltblown web and the synthetic fibers.
  • In this embodiment, the tissue web may comprise, for instance, an uncreped through-air dried web. The synthetic fibers may be present in the web in an amount less than about 10% by weight. Alternatively, the synthetic fibers may be present in the web in an amount of about 50% or less by weight, or about 30% or less by weight. The synthetic fibers may be homogeneously mixed with the pulp fibers. In an alternative embodiment, the tissue web may be made from a stratified fiber furnish including a first outer layer that forms the first side of the web and a second outer layer that forms the second side of the web. The synthetic fibers may be incorporated into the first outer layer in order to be available for bonding with the meltspun web. The tissue web may have a basis weight, for instance, of from about 35 gsm to about 120 gsm. The pulp fibers present in the tissue web may comprise softwood fibers. The tissue web may have substantially uniform basis weight and other properties, or may have basis weight and other features that vary from region to region, such as the webs with multiple regions differing in one or more intensive properties as disclosed in U.S. Pat. No. 5,443,691, issued Aug. 22, 1995 to Phan.
  • As described above, the meltspun web may be a meltblown web or a spunbond web. The meltspun web may have a basis weight of from about 30 gsm to about 200 gsm.
  • In one embodiment, the synthetic fibers contained in the tissue web are thermally bonded with the polymeric fibers contained in the meltspun web. The fibers may be thermally bonded together, for instance, by attaching the meltspun web to the tissue web while the meltspun web is in a molten state. The meltspun web and the tissue web may also be embossed together under heat, thermally point bonded together, or by using any other suitable process. In an alternative embodiment, the two webs may be ultrasonically bonded together. In another embodiment, heated air is passed through the web after the meltblown is attached to the tissue web to thermally bond a portion of the synthetic fibers in the tissue web with the meltblown web. Other forms of heating may be applied, such as infrared radiation, microwaves or other radiofrequency energy, inductive heating, steam heating, and the like.
  • In still another embodiment of the present invention, the meltspun web and the tissue web may be combined together in a manner that produces mechanical bonds between the synthetic fibers and the polymeric fibers. For instance, crimping may be used in order to cause fiber entanglement.
  • Various different materials may be used to form the polymeric fibers of the meltspun web and the synthetic fibers of the tissue web. In one embodiment, for instance, the polymeric fibers and the synthetic fibers may be made from polyolefin polymers, which includes polyethylenes, polypropylenes, copolymers thereof, terpolymers thereof, polymeric mixtures, and the like. In particular examples, the polymeric fibers may comprise polyester fibers and the synthetic fibers may comprise nylon fibers. In another embodiment, the polymeric fibers may comprise polypropylene fibers and the synthetic fibers may comprise bicomponent fibers, such as polyethylene/polyester fibers, polyethylene/polypropylene fibers, polypropylene/polyethylene fibers and the like in a sheath/core arrangement.
  • In one embodiment, for either moncomponent, bicomponent, or other multicomponent fibers, at least one polymer in at least one of the synthetic fiber types present in the tissue web has a melting point less than about 150° C., such as a melting point of about any of the following or less: 130° C., 110° C., 105° C., 100° C., 95° C., 90° C., 85°, and 80° C., such as from about 50° C. to about 150° C. or from about 60° C. to about 105° C. For example, the synthetic fibers may comprise an EVA-based polymer selected from the BYNEL® Series 1100 resin series of DuPont (Wilmington, Del.), typically having melting points from about 70° C. to about 95° C.
  • In still another embodiment of the present invention, the tissue web may contain a different anchoring agent for bonding with the meltspun web. The anchoring agent may comprise a latex polymer that has been impregnated into the web. The latex polymer is then used to bond with the fibers of the meltspun web. In this embodiment, the meltspun web may comprise polymeric fibers formed from a block copolymer. The block copolymer may be, for instance, a styrene-butadiene block copolymer.
  • The scrubbing product of the present invention may be useful in many different applications. For instance, a scrubbing pad could be useful as a dishcloth, a scouring pad, a sponge, a polishing pad, a sanding pad, or a personal cleansing pad, such as an exfoliating pad. In addition, the scrubbing product can be part of a cleaning tool useful for cleaning floors, walls, windows, toilets, and the like. In certain embodiments, the product of the present invention may include the abrasive layer alone, without any absorbent layer. For example, a meltblown or spunbond abrasive layer alone may be utilized as a scouring pad, a polishing pad, a sanding pad, or a personal cleansing pad such as an exfoliating pad, for instance either with or without the attached absorbent layer.
  • DEFINITIONS
  • As used herein, the term “coform web” refers to a material produced by combining separate polymer and additive streams into a single deposition stream in forming a nonwoven web. Such a process is taught, for example, by U.S. Pat. No. 4,100,324 to Anderson, et al. which is hereby incorporated by reference.
  • As used herein the term “meltblown fibers” means fibers of a polymeric material which are generally formed by extruding a molten thermoplastic material through a plurality of fine, usually circular, die capillaries as molten threads or filaments into converging high velocity, usually hot, gas (e.g. air) streams which attenuate the filaments of molten thermoplastic material to reduce their diameter. Thereafter, the meltblown fibers may be carried by the high velocity gas stream and are deposited on a collecting surface to form a web of randomly dispersed meltblown fibers. Meltblown fibers may be continuous or discontinuous and are generally tacky when deposited onto a collecting surface. In some embodiments, however, low or minimal air flow is used to reduce fiber attenuation and, in some embodiments, to permit neighboring filaments of molten polymer to coalesce (e.g., to adhere along the respective sides of the strands), becoming joined at least in part along the proximate sides of the neighboring strands to form fibers that are multifilamentary aggregate fibers (i.e. an aggregate fiber formed of two or more polymer strands further defined herein).
  • As used herein, “high yield pulp fibers” are those papermaking fibers produced by pulping processes providing a yield of about 65 percent or greater, more specifically about 75 percent or greater, and still more specifically from about 75 to about 95 percent. Yield is the resulting amount of processed fiber expressed as a percentage of the initial wood mass. Such pulping processes include bleached chemithermomechanical pulp (BCTMP), chemithermomechanical pulp (CTMP) pressure/pressure thermomechanical pulp (PTMP), thermomechanical pulp (TMP), thermomechanical chemical pulp (TMCP), high yield sulfite pulps, and high yield kraft pulps, all of which leave the resulting fibers with high levels of lignin. High yield fibers are well known for their stiffness (in both dry and wet states) relative to typical chemically pulped fibers. The cell wall of kraft and other non-high yield fibers tends to be more flexible because lignin, the “mortar” or “glue” on and in part of the cell wall, has been largely removed. Lignin is also nonswelling in water and hydrophobic, and resists the softening effect of water on the fiber, maintaining the stiffness of the cell wall in wetted high yield fibers relative to kraft fibers. The preferred high yield pulp fibers may also be characterized by being comprised of comparatively whole, relatively undamaged fibers, high freeness (250 Canadian Standard Freeness (CSF) or greater, more specifically 350 CSF or greater, and still more specifically 400 CSF or greater, such as from about 500 to 750 CSF), and low fines content (less than 25 percent, more specifically less than 20 percent, still more specifically less that 15 percent, and still more specifically less than 10 percent by the Britt jar test). In addition to common papermaking fibers listed above, high yield pulp fibers also include other natural fibers such as milkweed seed floss fibers, abaca, hemp, cotton and the like.
  • As used herein, the term “cellulosic” is meant to include any material having cellulose as a significant constituent, and specifically comprising about 20 percent or more by weight of cellulose or cellulose derivatives, and more specifically about 50 percent or more by weight of cellulose or cellulose derivatives. Thus, the term includes cotton, typical wood pulps, nonwoody cellulosic fibers, cellulose acetate, cellulose triacetate, rayon, viscose fibers, thermomechanical wood pulp, chemical wood pulp, debonded chemical wood pulp, lyocell and other fibers formed from solutions of cellulose in NMMO, milkweed, or bacterial cellulose, lyocell, and may be viscose, rayon, and the like. Fibers that have not been spun or regenerated from solution may be used exclusively, if desired, or at least about 80% of the web may be free of spun fibers or fibers generated from a cellulose solution. Examples of cellulosic webs may include known tissue material or related fibrous web, such as wetlaid creped tissue, wetlaid uncreped tissue, pattern-densified or imprinted tissue such as Bounty® paper towels or Charmin® toilet paper made by Procter and Gamble (Cincinnati, Ohio), facial tissue, toilet paper, dry-laid cellulosic webs such as airlaid webs comprising binder fibers, coform webs comprising at least 20% papermaking fibers or at least 50% papermaking fibers, foam-formed tissue, wipes for home and industrial use, hydroentangled webs such as spunbond webs hydroentangled with papermaking fibers, exemplified by the webs of U.S. Pat. No. 5,284,703, issued Feb. 8, 1994 to Everhart et al., and U.S. Pat. No. 4,808,467, issued Feb. 28, 1989 to Suskind et al., and the like. In one embodiment, the cellulosic web can be a reinforced cellulosic webs comprising a synthetic polymer network such as a spunbond web to which papermaking fibers are added by lamination, adhesive bonding, or hydroentangling, or to which an adhesive such as latex has been impregnated into the web (e.g., by gravure printing or other known means, exemplified by the VIVA® paper towel of Kimberly-Clark Corp., Dallas, Tex.) to provide high wet or dry tensile strength to the web. The reinforcing polymer (including adhesive) may comprise at about 1% or greater of the mass of the cellulosic web, or any of the following: about 5% or greater, about 10% or greater, about 20% or greater, about 30% or greater, or about 40% or greater, of the mass of the cellulosic web, such as from about 1% to about 50% or from about 3% to about 35% of the mass of the cellulosic web.
  • As used herein, “synthetic fibers” refer to man-made, polymeric fibers that may comprise one or more polymers, each of which may have been generated from one or more monomers. The polymeric materials in the synthetic fibers may independently be thermoplastic, thermosetting, elastomeric, non-elastomeric, crimped, substantially uncrimped, colored, uncolored, filled with filler materials or unfilled, birefringent, circular in cross-section, multilobal or otherwise non-circular in cross-section, and so forth. Synthetic fibers can be produced by any known technique. Synthetic fibers can be monocomponent fibers such as filaments of polyesters, polyolefins or other thermoplastic materials, or may be bicomponent or multicomponent fibers. When more than one polymer is present in a fiber, the polymers may be blended, segregated in microscopic or macroscopic phases, present in side-by-side or sheath-core structures, or distributed in any way known in the art.
  • Bicomponent synthetic fibers suitable for use in connection with this invention and their methods of manufacture are well known in the polymer field, such as, such as fibers with polyester cores and polyolefin sheaths useful as heat-activated binder fibers. For example, U.S. Pat. No. 3,547,763, issued Dec. 15, 1970 to Hoffman, Jr., discloses a bicomponent fiber having a modified helical crimp; U.S. Pat. No. 3,418,199 issued Dec. 24, 1968 to Anton et al. discloses a crimpable bicomponent nylon filament; U.S. Pat. No. 3,454,460 issued Jul. 8, 1969 to Bosely discloses a bicomponent polyester textile fiber; U.S. Pat. No. 4,552,603 issued Nov. 12, 1985 to Harris et al. discloses a method for making bicomponent fibers comprising a latently adhesive component for forming interfilamentary bonds upon application of heat and subsequent cooling; and U.S. Pat. No. 4,278,634 issued Jul. 18, 1980 to Zwick et al. discloses a melt-spinning method for making bicomponent fibers. All of these patents are hereby incorporated by reference. Principles of incorporating synthetic fibers into a wetlaid tissue web are disclosed in U.S. Pat. No. 5,019,211, “Tissue Webs Containing Curled Temperature-Sensitive Bicomponent Synthetic Fibers,” issued May 28, 1991 to Sauer, herein incorporated by reference in its entirety, and U.S. Pat. No. 6,328,850, “Layered Tissue Having Improved Functional Properties,” issued Dec. 11, 2001 to Van Phan, herein incorporated by reference to the extent it is non-contradictory herewith.
  • As used herein, “void volume” refers to the volume of space occupied by a sample that does not comprise solid matter. When expressed as a percentage, it refers to the percentage of the overall volume occupied by the sample that does not comprise solid matter.
  • “Overall Surface Depth” is a measure of the topography of a surface, indicative of a characteristic height different between elevated and depressed portions of the surface. The optical technique used for measuring Overall Surface Depth is described hereafter.
  • BRIEF DESCRIPTION OF THE FIGURES
  • A full and enabling disclosure of the present invention, including the best mode thereof to one of ordinary skill in the art, is set forth more particularly in the remainder of the specification, including reference to the accompanying figures in which:
  • FIG. 1 is a schematic diagram of one embodiment of a process line for making the abrasive layer of the present invention;
  • FIG. 2 is a diagram of one embodiment of a process for forming uncreped throughdried paper webs as may be used in the present invention;
  • FIG. 3 is a schematic diagram of one embodiment of a process line for making the composite construction of the present invention;
  • FIG. 4 is an embodiment of a process for combining the layers of the composite construction of the present invention;
  • FIG. 5 is another embodiment of a process for combining the layers of the composite construction of the present invention;
  • FIG. 6 is a perspective view of one embodiment of a scrubbing pad of the present invention;
  • FIG. 7 is a cross-sectional view of one embodiment of the scrubbing pad of the present invention;
  • FIG. 8 is a cross-sectional view of another embodiment of the scrubbing pad of the present invention;
  • FIG. 9 is a cross-sectional view of another embodiment of the scrubbing pad of the present invention;
  • FIG. 10 is a perspective view of one embodiment of a cleaning tool of the present invention wherein the scrubbing pad is held on a rigid gripping device;
  • FIG. 11 depicts cross-sections of a fiber formed from a single polymeric strand and a multifilamentary aggregate formed from six coalesced strands;
  • FIG. 12 depicts a cut-away portion of a meltblown die;
  • FIG. 13 depicts a starting point for an Abrasive Index Test; and
  • FIG. 14 depicts a representative topographical profile for illustration of material line concepts.
  • Repeat use of reference characters in the present specification and drawings is intended to represent same or analogous features or elements of the present invention.
  • DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
  • Reference now will be made in detail to the embodiments of the invention, one or more examples of which are set forth below. Each example is provided by way of explanation of the invention, not limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and variations may be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment, may be used on another embodiment to yield a still further embodiment. Thus, it is intended that the present invention cover such modifications and variations as come within the scope of the appended claims and their equivalents.
  • In general, the present invention is directed to disposable scrubbing pads which are suitable for use in a wide variety of applications, including household cleaning and personal care applications. For example, the scrubbing products of the present invention may be suitable for use as a dishcloth, a general purpose cleaning cloth, a scouring or polishing pad, or a personal care product, such as an exfoliating pad, for instance. In certain embodiments, the scrubbing products of the present invention can be used to remove layers of a surface, for example in a sanding or polishing application.
  • The scrubbing pads of the present invention are generally of a multi-layer construction and include a nonwoven abrasive layer secured to an absorbent layer which includes one or more layers of a nonwoven paper web. For instance, the abrasive layer may be a porous, flexible, meltblown web and may be bonded to one or more plies of a high bulk, absorbent paper web, such as an uncreped, through-air dried (UCTAD) paper web.
  • The two distinct layers of the composite scrubbing pad may offer cleaning advantages beyond those known in other composite scrubbing articles, and may do so at a much lower cost. Other advantages are gained by the disposable scrubbing pads as well. For instance, the soft paper web and flexibility of the pad may make the article much more comfortable to hold during cleaning than previously known composite scrubbing articles. Additionally, the pads may be shaped so as to be attachable to a rigid gripping device, forming a convenient cleaning tool for either heavy or light scrubbing, as desired by the user. For example, a cleaning tool capable of holding the scrubbing product of the present invention could be used for cleaning floors, walls, windows, toilets, ceiling fans, and the like as well as for cleaning surfaces by polishing or sanding a surface.
  • If desired, the scrubbing pads may optionally include various additives, such as cleaning agents or medications, which may enhance the performance of the pads.
  • The nonwoven abrasive layer may be secured to the absorbent layer using various techniques and methods. In one particular embodiment, for instance, an anchoring agent may be incorporated into the absorbent layer for bonding with the abrasive layer. The anchoring agent may serve to increase the structural stability of the composite product, especially when the product is wet and in use.
  • The anchoring agent incorporated into the absorbent layer may be, for instance, a latex polymer impregnated into the absorbent layer or, alternatively, synthetic fibers present in the fiber furnish used to form the absorbent layer. The anchoring agent forms a bond with polymeric fibers contained in the abrasive layer. The bond may be a thermal bond, a chemical bond, or a mechanical bond. Mechanical bonds may be formed by fiber entanglement between the polymeric bonds of the abrasive layer and the anchoring agent of the absorbent layer.
  • Various examples of wiping products and scrubbing products made in accordance with the present invention follow. Specifically, first a discussion of exemplary abrasive layers is included followed by a discussion of exemplary absorbent layers. After describing abrasive layers and absorbent layers, the use of anchoring agents to secure the layers together is discussed in greater detail.
  • In general, the abrasive layer of the scrubbing pads of the present invention may include a material which is formed into an open, porous structure and has enough strength and hardness to form a rough, scratchy surface on the pad. Suitable materials are abundant and may be either natural or synthetic materials. Possible exemplary materials may include any known abrasive materials formed into the desired open structure. Possible synthetic materials may be polymeric materials, such as, for instance, meltspun nonwoven webs formed of molten or uncured polymer which may then harden to form the desired abrasive layer.
  • The materials and processes used to form the abrasive layer of the scrubbing pad may be chosen and designed with the desired end use of the product in mind. For example, a scrubbing pad designed as a personal care product, such as a face-washing pad, may include an abrasive layer which is softer and less abrasive than a scrubbing pad for use in household cleaning applications. Thus, the raw materials, additives, fiber diameter, layer density and stiffness, etc. may all vary depending on the desired characteristics of the final product.
  • In one embodiment, the abrasive layer of the scrubbing pad may include a meltspun web, such as may be formed using a thermoplastic polymer material. Generally, any suitable thermoplastic polymer that may be used to form meltblown nonwoven webs may be used for the abrasive layer of the scrubbing pads. A non-exhaustive list of possible thermoplastic polymers suitable for use include polymers or copolymers of polyolefins, polyesters, polypropylene, high density polypropylene, polyvinyl chloride, vinylidene chloride, nylons, polytetrafluoroethylene, polycarbonate, poly(methyl) acrylates, polyoxymethylene, polystyrenes, ABS, polyetheresters, or polyamides, polycaprolactan, thermoplastic starch, polyvinyl alcohol, polylactic acid, such as for example polyesteramide (optionally with glycerin as a plasticizer), polyphenylsulfide (PPS), poly ether ether ketone (PEEK), polyvinylidenes, polyurethane, and polyurea. For instance, in one embodiment, the abrasive layer may include meltblown nonwoven webs formed with a polyethylene or a polypropylene thermoplastic polymer. Polymer alloys may also be used in the abrasive layer, such as alloy fibers of polypropylene and other polymers such as polyester (PET). Compatibilizers may be needed for some polymer combinations to provide an effective blend. In one embodiment, the abrasive polymer is substantially free of halogenated compounds. In another embodiment, the abrasive polymer is not a polyolefin, but comprises a material that is more abrasive than say, polypropylene or polyethylene (e.g. having flexural modulus of about 1200 MPa and greater, or a Shore D hardness of 85 or greater).
  • In addition to being coarse, the fibers of the abrasive layer may have a high elastic modulus, such as an elastic modulus roughly equal to or greater than that of polypropylene such as about 1,000 MPa or greater, specifically about 2,000 MPa or greater, more specifically about 3,000 MPa or greater, and most specifically about 5,000 MPa or greater. By way of example, phenol plastics may have elastic moduli of about 8000 MPa, and a polyamide (nylon 6,6) reinforced with 15% glass fiber has a reported elastic modulus of about 4,400 MPa (whereas the elastic modulus is about 1,800 MPa without the glass reinforcement).
  • The fibers of the abrasive layers can be elastomeric or non-elastomeric, as desired (e.g., crystalline or semi-crystalline). In addition, the abrasive layer may comprise a mix of elastomeric fibers and non-elastomeric fibers.
  • For some polymer groups, an increased melting point may correlate with improved abrasive features. Thus, in one embodiment, the abrasive fibers may have a melting point greater than 120° C., such as about 140° C. or greater, about 160° C. or greater, about 170° C. or greater, about 180° C. or greater, or about 200° C. or greater, exemplified by the following ranges: from about 120° C. to about 350° C., from about 150° C. to about 250° C., or from about 160° C. to about 210° C.
  • In some embodiments, polymers with relatively high viscosity or low melt flow rates may be useful in producing coarse webs for effective cleaning. The melt flow rate of the polymer is measured according to ASTM D1238. While polymers typically used in meltblowing operations may have melt flow rates of about 1000 g/10 min or greater and may be considered in some embodiments of the present invention, in some embodiments the polymers used to produce an abrasive layer may have a melt flow rate according to ASTM D1238 less than 3000 g/10 min or 2000 g/10 min, such as less than about 1000 g/10 min or less than about 500 g/10 min, specifically less than 200 g/10 min, more specifically less than 100 g/10 min, and most specifically less than 80 g/10 min, such as from about 15 g/10 min to about 250 g/10 min, or from about 20 g/10 min to about 400 g/10 min.
  • Another measure that may be indicative of good abrasive properties is Shore Hardness D, as measured with standard test method ASTM D 1706. In general, suitable polymeric material of the abrasive layer may have a Shore Hardness D of about 50 or greater, such as about 65 or greater, or more specifically, about 70 or greater, or most specifically about 80 or greater. Polypropylene, for example, typically has Shore D hardness values from about 70 to about 80.
  • In one embodiment, the polymeric material in the abrasive layer may have a flexural modulus of about 500 MPa or greater and a Shore D hardness of about 50 or greater. In an alternative embodiment, the polymeric material may have a flexural modulus of about 800 MPa or greater and a Shore D hardness of about 50 or greater.
  • In one embodiment, the polymeric fibers of the abrasive layer are substantially free of plasticizers, or may have 33 weight percent plasticizer or less, more specifically about 20 weight percent plasticizer or less, more specifically about 3 weight percent plasticizer or less. The dominant polymer in the polymeric fibers may have a molecular weight of any of the following: about 100,000 or greater, about 500,000 or greater, about 1,000,000 or greater, about 3,000,000 or greater, and about 5,000,000 or greater.
  • The abrasive layer may comprise fibers of any suitable cross-section. For example, the fibers of the abrasive layer may include coarse fibers with circular or non-circular cross-sections. Moreover, non-circular cross-sectional fibers may include grooved fibers or multi-lobal fibers such as, for example, “4DG” fibers (specialty PET deep grooved fibers, with an eight-legged cross-section shape). Additionally, the fibers may be single component fibers, formed of a single polymer or copolymer, or may be multi-component fibers.
  • In an effort to produce an abrasive layer having desirable combinations of physical properties, in one embodiment, nonwoven polymeric fabrics made from multi-component or bicomponent filaments and fibers may be used. Bicomponent or multi-component polymeric fibers or filaments include two or more polymeric components which remain distinct. The various components of multi-component filaments are arranged in substantially distinct zones across the cross-section of the filaments and extend continuously along the length of the filaments. For example, bicomponent filaments may have a side-by-side or core and sheath arrangement. Typically, one component exhibits different properties than the other so that the filaments exhibit properties of the two components. For example, one component may be polypropylene which is relatively strong and the other component may be polyethylene which is relatively soft. The end result is a strong yet soft nonwoven fabric.
  • In one embodiment, the abrasive layer comprises metallocene polypropylene or “single site” polyolefins for improved strength and abrasiveness. Exemplary single-site materials are available from H.B. Fuller Company, Vadnais Heights, Minn.
  • In another embodiment, the abrasive layer includes a precursor web comprising a planar nonwoven substrate having a distribution of attenuated meltable thermoplastic fibers such as polypropylene fibers thereon. The precursor web may be heated to cause the thermoplastic fibers to shrink and form nodulated fiber remnants that impart an abrasive character to the resultant web material. The nodulated fiber remnants may comprise between about 10% and about 50% by weight of the total fiber content of the web and may have an average particle size of about 100 micrometers or greater. In addition to the fibers that are used to form nodulated remnants, the precursor web may contain cellulosic fibers and synthetic fibers having at least one component with a higher melting point than polypropylene to provide strength. The precursor web may be wet laid, air laid, or made by other methods. In one embodiment, the precursor web is substantially free of papermaking fibers. For example, the precursor web may be a fibrous nylon web containing polypropylene fibers (e.g., a bonded carded web comprising both nylon fibers and polypropylene fibers).
  • The material used to form the abrasive layer may also contain various additives as desired. For example, various stabilizers may be added to a polymer, such as light stabilizers, heat stabilizers, processing aides, and additives that increase the thermal aging stability of the polymer. Further, auxiliary wetting agents, such as hexanol, antistatic agents such as a potassium alkyl phosphate, and alcohol repellants such as various fluoropolymers (e.g., DuPont Repellent 9356H) may also be present. Desired additives may be included in the abrasive layer either through inclusion of the additive to a polymer in the die or alternatively through addition to the abrasive layer after formation, such as through a spraying process.
  • For exemplary purposes, one embodiment of a system for forming a meltblown nonwoven web as may be used in the abrasive layer of the scrubbing pad is illustrated in FIG. 1. As shown, the system includes a forming machine generally 110 which may be used to produce a meltblown web 32 in accordance with the present invention. Particularly, the forming machine 110 includes an endless foraminous-forming belt 114 wrapped around rollers 116 and 118 so that the belt 114 is driven in the direction shown by the arrows. The web may then pass over a guide roll 140 before further processing.
  • The forming belt 114 may be any suitable forming belt and, if desired, may provide additional three-dimensional texture to the meltblown layer. Added texture may affect the abrasiveness of the layer. For example, a high degree of surface texture in the meltblown layer may be achieved by forming a meltblown layer on a high dimension forming fabric, such as those available from Lindsay Wire Company.
  • If the meltblown fibers are still molten or partially molten when they impinge upon the wire, the texture of the wire may be imparted to the web, particularly with the assistance of hydraulic pressure across the wire to further press the meltblown fibers against the wire before they have fully solidified. Improved molding of meltblown fibers against a wire may be achieved by using a suitably high temperature of the polymer or of the temperature of the air jets, and/or by adjusting the distance between the meltblown die and the carrier wire. The carrier wire may have a repeating series of depressions which may correspond to elevated regions on the meltblown web useful for cleaning. A three-dimensional carrier wire may impart elevated structures to the meltblown that rise about 0.2 mm or greater from the surrounding meltblown fabric, more specifically about 0.4 mm or greater, depending upon the desired level of abrasiveness. A spectrum of scrubby pads from mildly abrasive to aggressively abrasive may be produced.
  • The repeating structures may be represented as the minimum characteristic unit cell of the carrier wire, and the unit cell may have a minimum in-plane length scale (e.g., for a unit cell that is a parallelogram, the length of the shorter side, or for more complex shapes such as a hexagon, smaller of the machine direction width and cross-direction width) of about 1 mm or greater, such as about 2 mm or greater, or may have an area of about 5 square millimeters or greater (e.g., a unit cell of dimensions 1 mm by 5 mm), or about 20 square millimeters or greater. A carrier wire may be treated with a release agent such as a silicone liquid or coated with Teflon® or other release agents to enhance removal of the textured meltblown web from the carrier wire.
  • FIG. 8 is a cross section of one embodiment of the present invention illustrating a highly textured meltblown layer 32 such as could be formed on a highly textured forming fabric. The highly textured meltblown layer may then be attached to an absorbent layer 34 in forming the scrubbing pad of the present invention.
  • The forming machine system of FIG. 1 may also include a die 120 which is used to form fibers 126. The throughput of the die 120 is specified in pounds of polymer melt per inch of die width per hour (PIH). As a thermoplastic polymer exits the die 120, high-pressure fluid, usually air, attenuates and spreads the polymer stream to form fibers 126. The fibers 126 may be randomly deposited on the forming belt 114 and form a meltblown layer 32.
  • In the manufacture of conventional meltblown materials, high velocity air is usually used to attenuate the polymeric strands to create fine, thin fibers. In the present invention, by adjusting the air flow system, such as by increasing the air flow area or otherwise decreasing the velocity of the air stream immediately adjacent the molten polymeric strands as they emerge from the meltblown die head, it is possible to prevent substantial attenuation of the fiber diameter (or reduce the degree of fiber attenuation). Limiting the attenuation of the fiber diameter may increase fiber coarseness, which may increase the abrasiveness of the layer formed by the fibers.
  • Additionally, the airflow near the die exit may be used to agitate and spread the polymeric fibers in a manner that may be highly non-uniform on the forming belt. The large degree of non-uniformity of the lay-down of coarse meltblown fibers on the belt may be manifest in a web which may display variations in thickness and variations in basis weight across the surface of the web, i.e., an uneven surface may be created on the web, which may increase the abrasiveness of the layer formed by the fibers.
  • In addition, non-uniform spread of the fibers during formation of the web may create a web with increased void space within the web. For example, an open network of fibers may be formed which may have open voids that occupy a substantial portion of the layer. For instance, the void volume of the abrasive layer may be greater than about 10%, particularly greater than about 50%, and more particularly greater than about 60% of the volume of the material. These open void materials may inherently have good scrubbing properties.
  • The abrasive layer may also have a relatively open structure that provides high permeability, allowing gas or liquid to readily pass through the abrasive layer. Permeability can be expressed in terms of Air Permeability measured with the FX 3300 Air Permeability device manufactured by Textest AG (Zürich, Switzerland), set to a pressure of 125 Pa (0.5 inches of water) with the normal 7-cm diameter opening (38 square centimeters), operating in a TAPPI conditioning room (73° F., 50% relative humidity). The abrasive layer may have an Air Permeability of any of the following: about 100 CFM (cubic feet per minute) or greater, about 200 CFM or greater, about 300 CFM or greater, about 500 CFM or greater, or about 700 CFM or greater, such as from about 250 CFM to about 1500 CFM, or from about 150 CFM to about 1000 CFM, or from about 100 CFM to about 800 CFM, or from about 100 CFM to about 500 CFM. Alternatively, the Air Permeability of the abrasive layer can be less than about 400 CFM. In cases wherein the abrasive layer has a basis weight less than 150 gsm, multiple plies of the abrasive layer having a combined basis weight of at least 150 gsm may display an Air Permeability of about 70 CFM or greater, or any of the aforementioned values or ranges given for a single abrasive layer.
  • In general, thermoplastic polymer fibers in the abrasive layer may be greater than about 30 microns in mean diameter. More specifically, thermoplastic fibers may be between about 40 microns and about 800 microns in mean diameter, such as from about 50 microns to 400 microns, more specifically still from about 60 microns to 300 microns, and most specifically from about 70 microns to about 250 microns. Such fibers are substantially coarser than the fibers of conventional meltblown webs, and the added coarseness is generally helpful in increasing the abrasive characteristics of the web.
  • The fibers forming the meltblown web may be long enough so as to support the open network of the layer. For example, the fibers may have a fiber length of at least about one centimeter. More specifically, the fibers may have a characteristic fiber length of greater than about 2 cm.
  • If desired, the fibers may optionally be formed to include abrasion enhancing features, such as inclusion of filler particles, for example microspheres, granules of pumice or metal, treatment with meltblown “shot”, and the like.
  • Microspheres may be from about 10 microns to about 1 mm in diameter and typically have a shell thickness of from about 1 to about 5 microns, while macrospheres (which may also be used in some embodiments) may have diameters greater than about 1 mm. Such materials may include microbeads of metal, glass, carbon, mica, quartz or other minerals, plastic such as acrylic or phenolic, including acrylic microspheres known as PM 6545 available from PQ Corporation of Pennsylvania, and hollow microspheres such as the cross-linked acrylate SunSpheres™ of ISP Corporation (Wayne, N.J.) and similar hollow spheres as well as expandable spheres such as Expancel® microspheres (Expancel, Stockviksverken, Sweden, a division of Akzo Nobel, Netherlands), and the like.
  • In one embodiment of the present invention, the abrasive layer may be made from a nonwoven meltspun web, such as a meltblown web treated with a meltblown “shot”. Meltblown shot is a coarse nonuniform layer applied in a meltblown process deliberately operated to generate random globules of the polymer (typically polypropylene or another thermoplastic) interconnected with strands. If desired, the shot may be distinctly colored to make the abrasive element readily visible.
  • Optionally, the abrasive layer of the present invention may be formed from two or more different fiber types. For instance, the abrasive layer may be formed of different fiber types formed of different polymers or different combinations of polymers. Additionally, the abrasive layer may be formed of different fiber types including fibers of different orientations, i.e. curled or straight fibers, or fibers having different lengths or cross sectional diameters from each other. For example, die 120 may be a multi-section die and include different polymer material in different sections which may be fed through the die 120 and form distinctly different fibers which may then be mixed and heterogeneously distributed on forming belt 114. Alternatively, two or more different meltblown sub-layers may be formed and bonded together to form an abrasive layer with a fairly uniform, homogeneous distribution of different fiber types.
  • In one embodiment, the abrasive layer of the present invention may include multifilamentary aggregates of individual polymeric strands.
  • As used herein, the term “multifilamentary aggregate” refers to a meltblown fiber that is actually an aggregate of two or more polymer strands formed by at least the partial coalescence (adhesion) of adjacent molten polymer strands ejected from adjacent holes on a meltblown die, which may be achieved, for example, under circumstances in which the turbulence created by air jets is substantially lower than in normal meltblown operation, thereby allowing two or more adjacent strands to come into contact and become joined together along at least a portion of the length of the strands. For instance, the individual strands forming the multifilamentary aggregate fiber may be joined side by side for a distance greater than about 5 mm, along the length of the fiber. As such, bicomponent fibers, multi-lobal fibers, and the like, which are extruded as a single fiber with multiple polymers or complex shapes are not to be confused with the mitifilamentary aggregate fibers of the present invention, which include adjacent polymer strands extruded or ejected from adjacent holes in a meltblown die and only adhere together after exiting the die.
  • The holes of the meltblown die may be in one or more rows. When more than one row of holes is present in a die, the holes may be staggered or aligned, or distributed in other ways known in the art. The die holes may be any desired shape in order to form individual strands of a desired cross sectional shape. In one embodiment, the die holes may be circular such that the polymer strands, before aggregation to form the aggregate fibers of the present invention are substantially circular in cross section. Even after adhesion together, the substantially circular individual polymer strands may retain elements of their individual circular cross sections.
  • Multifilamentary aggregates may be substantially ribbon-like in character, particularly when three or more strands from adjacent meltblown holes aligned in a line adhere to each other in a substantially parallel array (i.e., parallel to each other with the line formed by connecting the center points of consecutive strands being an approximately straight line). For example, FIG. 11 illustrates a multifilamentary aggregate formed of six individual polymer strands adhered in a substantially parallel array. The width of the multifilamentary aggregate may be nearly as great as the number of strands in the multifilamentary aggregates multiplied by the diameter of a single strand, though due to the fusion of portions of the joined strands and due to staggering of the strands in some cases, the width is generally a fraction of the product of the number of strands and the single strand diameter (or average single strand diameter). This fraction may be from about 0.2 to about 0.99, specifically from about 0.4 to about 0.97, more specifically from about 0.6 to about 0.95, and most specifically from about 0.7 to about 0.95. In one embodiment, the major axis of the non-circular multifilament aggregate fiber cross section can be greater than about 30 microns.
  • The number of strands in the multifilamentary aggregates may range from 2 to about 50, specifically from 2 to about 30, more specifically from 2 to about 20, and most specifically from about 3 to about 12. Multifilamentary aggregates may have a number-weighted average strand count of 3 or more, 4 or more, 5 or more, or 6 or more. A meltblown web comprising multifilamentary aggregates may have multifilamentary aggregates comprising 5% or greater of the mass of the web (such as multifilamentary aggregates with three strands or more comprising 5% or greater of the mass of the web). For example, the mass fraction of the web consisting of multifilamentary aggregates may be about 10% or greater, about 20% or greater, about 30% or greater, about 40% or greater, about 50% or greater, about 60% or greater, about 70% or greater, about 80% or greater, about 90% or greater, or substantially 100%. These ranges may apply to multifilamentary aggregates in general, or to multifilamentary aggregates having at least 3 strands, 4 strands, 5 strands, or 6 strands.
  • FIG. 11 depicts cross-sections of a polymeric fiber 126 formed from a single polymeric strand 238 in an operation such as meltblown, and for comparison depicts a cross-section of a multifilamentary aggregate 240 formed by the partial coalescence of six strands 238 to yield a ribbon-like structure. The region where two strands 238 are joined together may comprise a cusp 243.
  • The smallest rectangle 241 that may completely enclose the cross-section of the multifilamentary aggregate 240 has a width W and a height H. The width W is the width of the multifilamentary aggregate and the height H is the height of multifilamentary aggregate. For many applications, the width may be from about 50 microns to about 800 microns. In other embodiments, however, other widths may be achieved such as widths of about 100 microns or greater, about 200 microns or greater, about 400 microns or greater, about 600 microns or greater, and about 800 microns or greater.
  • The aspect ratio of the multifilamentary aggregate is the ratio W/H. The aspect ratio of multifilamentary aggregates in the present invention may be about 2 or greater, about 3 or greater, about 4 or greater, about 5 or greater, or about 6 or greater, such as from about 3 to about 12.
  • The strands 238 of the multifilamentary aggregate 240 may remain substantially parallel throughout the length of the fiber (a multifilamentary aggregate 240), or may persist for a distance and then split into two or more groups of smaller multifilamentary aggregates or individual strands 238. The strands 238 of the multifilamentary aggregate 240 may remain joined to one another along their sides for a distance of about 1 mm or greater, 5 mm or greater, 10 mm of greater, 20 mm or greater, or 50 mm or greater.
  • Referring back to FIG. 1, the forming belt 114 may be any suitable forming belt and, if desired, may provide texture to the meltblown layer, which may also affect the abrasiveness of the layer. For example, a high degree of surface texture in the meltblown layer may be achieved by forming the meltblown layer on a high dimension forming fabric, such as those available from the Lindsay Wire Company. In another embodiment, the abrasive layer may be formed directly on the fibrous absorbent web (not shown), such as a textured tissue web or other cellulosic web, which may be carried by a fabric. FIG. 8 is a cross section of one embodiment of the present invention with a highly textured meltblown layer 32 attached to a relatively flat absorbent layer 34. Alternatively, the forming belt 114 may be relatively flat and produce a flat meltblown layer 32, as is illustrated in FIG. 7.
  • The abrasive layer may have a suitable fiber basis weight and formation so as to provide good scrubbing characteristics to the composite pad structure while remaining flexible. For example, a meltblown web forming the abrasive layer may have a basis weight of greater than about 10 gsm. More specifically, the meltblown web may have a basis weight of between about 25 gsm and about 400 gsm, more specifically between about 30 gsm and about 200 gsm, and most specifically between about 40 gsm and 160 gsm. The meltblown web may have a density ranging from any of about 0.02 grams/cubic centimeter (g/cc), 0.04 g/cc, 0.06 g/cc, 0.1 g/cc, 0.2 g/cc, 0.4 g/cc, 0.6 g/cc, and 0.8 g/cc to any of about 0.1 g/cc, 0.3 g/cc, 0.5 g/cc, and 1 g/cc (other values and ranges known in the art may also be within the scope of the present invention). In one embodiment, the abrasive layer may be formed such that when the pad is put under pressure, as when a surface is being scrubbed by contact with the abrasive layer, the surface may be substantially in contact with only the meltblown layer of the pad.
  • As previously discussed, the web may be formed with variations in thickness and basis weight across the web so as to produce a web with an uneven, more abrasive surface. Thickness variations across the surface of the web may be measured with a platen 0.6 inches in diameter that is pressed against the sample with a load of 7.3 psi (applied pressure of 50 kPa) as it resides on a solid surface, wherein the displacement of the platen relative to the solid surface indicates the local thickness of the sample. Repeated measurements at different locations on the sample may be used to obtain a distribution of local thickness measurements from which a standard deviation may be calculated. Abrasive layers of the present invention may have a standard deviation in this thickness measurement of at least about 0.2 mm, specifically at least about 0.6 mm, more specifically at least about 0.8 mm, an most specifically at least 1.0 mm. Expressed on a percentage basis, the standard deviation of basis weight for data points averaged over 5-mm square sections, may be about 5% or greater, more specifically about 10% or greater, more specifically still about 20% or greater, and most specifically about 30% or greater, such as from about 8% to about 60%, or from 12% to about 50%.
  • The abrasiveness of the abrasive layer may further be enhanced by the topography of the abrasive layer. For example, the abrasive layer may have a plurality of elevated and depressed regions due to nonuniform basis weight, nonuniform thickness, or due to the three-dimensional topography of an underlying fibrous web such as a textured wetlaid tissue web. The elevated and depressed regions may be spaced apart substantially periodically in at least one direction such as the machine direction or the cross direction with a characteristic wavelength of about 2 mm or greater, more specifically about 4 mm or greater, and having a characteristic height difference between the elevated and depressed regions of at least 0.3 mm or greater, more specifically about 0.6 mm or greater, more specifically still about 1 mm or greater, and most specifically about 1.2 mm or greater.
  • In another embodiment, the abrasive layer may include a precursor web comprising a planar nonwoven substrate having a distribution of attenuated meltable thermoplastic fibers such as polypropylene fibers thereon. The precursor web may be heated to cause the thermoplastic fibers to shrink and form nodulated fiber remnants that impart an abrasive character to the resultant web material. The nodulated fiber remnants may comprise between about 10% and about 50% by weight of the total fiber content of the web and may have an average particle size of about 100 micrometers or greater. In addition to the fibers that are used to form nodulated remnants, the precursor web may contain cellulosic fibers and synthetic fibers having at least one component with a higher melting point than polypropylene to provide strength. The precursor web may be wet laid, air laid, or made by other methods. In one embodiment, the precursor web is substantially free of papermaking fibers. For example, the precursor may be a fibrous nylon web containing polypropylene fibers (e.g., a bonded carded web comprising both nylon fibers and polyproylene fibers).
  • The abrasive layer may also be apertured to improve fluid access to the absorbent layer of the article. Pin apertured meltblown webs, for example, may have increased abrasiveness due to the presence of the apertures.
  • In accordance with the present invention, an abrasive layer may be secured to one or more absorbent layers, such as that formed by a nonwoven paper web, to form a disposable scrubbing pad. When laminates according to the present invention are used for scrubbing or other demanding tasks, the durability of the product may be surprisingly high. At least part of the excellent performance may be due to a synergy in the material properties of the laminate, which may be superior to what one would expect based on the material properties of the individual components. For example, the tensile strength and stretch properties of an abrasive laminate comprising a meltblown layer bonded to a tissue web may have a substantially higher tensile strength than an unbonded combination of the same meltblown layer and tissue web together.
  • The paper web of the absorbent layer is generally a web that contains high levels of bulk. Further, the web may have a substantial amount of wet strength and wet resilience for use in wet environments. The paper web, if desired, may also be highly textured and have a three-dimensional structure, similar to the abrasive layer, as previously discussed. For instance, the paper web may have an Overall Surface Depth of greater than about 0.2 mm, and particularly greater than about 0.4 mm. In one embodiment, the paper web may be a commercial paper towel, such as a SCOTT® Towel or a VIVA® Towel, for instance. SCOTT® Towel, for example, has a wet:dry tensile strength ratio (ratio of the wet tensile strength to the dry tensile strength, taken in the cross direction) typically greater than 30% (e.g., one set of measurements gave a value of 38%), and VIVA® Towel has a wet:dry tensile strength ratio typically greater than 60% (e.g., one set of measurements gave a value of 71%). Wet:dry tensile strength ratios may also be greater than 10%, 20%, 40%, or 50%.
  • In one embodiment, the paper web may be a textured web which has been dried in a three-dimensional state such that the hydrogen bonds joining fibers were substantially formed while the web was not in a flat, planar state. For instance, the web may be formed while the web is on a highly textured through drying fabric or other three-dimensional substrate.
  • In general, the uncreped throughdried paper web may have a basis weight of greater than about 10 gsm. Specifically, the paper web may have a basis weight greater than about 20 gsm, more specifically greater than about 40 gsm. For instance, the paper web can have a basis weight of from about 20 gsm to about 150 gsm, such as from about 40 gsm to about 120 gsm. If desired, the web may include a wet strength agent and/or at least about five percent (5%) by weight of high-yield pulp fibers, such as thermomechanical pulp. In addition to high-yield pulp fibers, the web may contain papermaking fibers, such as softwood fibers and/or hardwood fibers. In one embodiment, the web is made entirely from high-yield pulp fibers and softwood fibers. The softwood fibers may be present in an amount from about 95% to about 70% by weight.
  • Referring to FIG. 2, a method is shown for making throughdried paper sheets in accordance with this invention. (For simplicity, the various tensioning rolls schematically used to define the several fabric runs are shown but not numbered. It will be appreciated that variations from the apparatus and method illustrated in FIG. 2 may be made without departing from the scope of the invention). Shown is a twin wire former having a layered papermaking headbox 10 which injects or deposits a stream 11 of an aqueous suspension of papermaking fibers onto the forming fabric 13 which serves to support and carry the newly-formed wet web downstream in the process as the web is partially dewatered to a consistency of about 10 dry weight percent. A second wire 12 may converge toward the forming fabric 13 to form a twin-wire section 15 for controlled formation of the wet web. Additional dewatering of the wet web may be carried out, such as by vacuum suction, while the wet web is supported by the forming fabric.
  • The wet web is then transferred from the forming fabric to a transfer fabric 17 traveling at a slower speed than the forming fabric in order to impart increased stretch into the web. This is commonly referred to as a “rush” transfer. Preferably the transfer fabric may have a void volume that is equal to or less than that of the forming fabric. The relative speed difference between the two fabrics may be from 0-60 percent, more specifically from about 10-40 percent. Transfer is preferably carried out with the assistance of a vacuum shoe 18 such that the forming fabric and the transfer fabric simultaneously converge and diverge at the leading edge of the vacuum slot.
  • The web is then transferred from the transfer fabric to the through drying fabric 19 with the aid of a vacuum transfer roll 20 or a vacuum transfer shoe, optionally again using a fixed gap transfer as previously described. The through drying fabric may be traveling at about the same speed or a different speed relative to the transfer fabric. If desired, the through drying fabric may be run at a slower speed to further enhance stretch. Transfer is preferably carried out with vacuum assistance to ensure deformation of the sheet to conform to the through drying fabric, thus yielding desired bulk and appearance.
  • In one embodiment, the through drying fabric contains high and long impression knuckles. For example, the through drying fabric may have from about 5 to about 300 impression knuckles per square inch which are raised at least about 0.005 inches above the plane of the fabric. During drying, the web is macroscopically arranged to conform to the surface of the through drying fabric.
  • The level of vacuum used for the web transfers may be from about 3 to about 15 inches of mercury (75 to about 380 millimeters of mercury), preferably about 5 inches (125 millimeters) of mercury. The vacuum shoe (negative pressure) may be supplemented or replaced by the use of positive pressure from the opposite side of the web to blow the web onto the next fabric in addition to or as a replacement for sucking it onto the next fabric with vacuum. Also, a vacuum roll or rolls may be used to replace the vacuum shoe(s).
  • While supported by the through drying fabric, the web is final dried to a consistency of about 94 percent or greater by the through dryer 21 and thereafter transferred to a carrier fabric 22. The dried basesheet 34 is transported to the reel 24 using carrier fabric 22 and an optional carrier fabric 25. An optional pressurized turning roll 26 may be used to facilitate transfer of the web from carrier fabric 22 to fabric 25. Suitable carrier fabrics for this purpose are Albany International 84M or 94M and Asten 959 or 937, all of which are relatively smooth fabrics having a fine pattern. Although not shown, reel calendering or subsequent off-line calendering may be used to improve the smoothness and softness of the basesheet 34.
  • In order to improve wet resiliency, the paper web may contain wet resilient fibers, such as high-yield fibers as described above. High-yield fibers include, for instance, thermomechanical pulp, such as bleached chemithermomechanical pulp (BCTMP). The amount of high-yield pulp fibers present in the sheet may vary depending upon the particular application. For instance, the high-yield pulp fibers may be present in an amount of about 5 dry weight percent or greater, or specifically, about 15 dry weight percent or greater, and still more specifically from about 15 to about 30%. In other embodiments, the percentage of high-yield fibers in the web may be greater than any of the following: about 30%, about 50%, about 60%, about 70%, and about 90%.
  • In one embodiment, the uncreped throughdried web may be formed from multiple layers of a fiber furnish. Both strength and softness are achieved through layered webs, such as those produced from stratified headboxes wherein at least one layer delivered by the headbox comprises softwood fibers while another layer comprises hardwood or other fiber types. Layered structures produced by any means known in the art are within the scope of the present invention.
  • In one embodiment, for instance, a layered or stratified web is formed that contains high-yield pulp fibers in the center. Because high-yield pulp fibers are generally less soft than other paper making fibers, in some applications it is advantageous to incorporate them in to the middle of the paper web, such as by being placed in the center of a three-layered sheet. The outer layers of the sheet may then be made from softwood fibers and/or hardwood fibers.
  • In addition to containing high-yield fibers, the paper web may also contain a wet strength agent to improve wet resiliency. In fact, the combination of non-compressive drying to mold a three-dimensional paper web, coupled with wet strength additives and applying wet resilient fibers produces webs that maintain an unusually high bulk when wet, even after being compressed.
  • “Wet strength agents” are materials used to immobilize the bonds between the fibers in the wet state. Any material that when added to a paper web or sheet results in providing the sheet with either a wet geometric mean tensile strength/dry geometric tensile strength ratio in excess of 0.1 (the GM wet:dry tensile ratio), or a wet tensile strength/dry tensile ratio in the cross-direction in excess of 0.1 (the CD wet:dry ratio), will, for purposes of this invention, be termed a wet strength agent. Typically these materials are termed either as permanent wet strength agents or as “temporary” wet strength agents. For the purposes of differentiating permanent from temporary wet strength, permanent will be defined as those resins which, when incorporated into paper or tissue products, will provide a product that retains more than 50% of its original wet strength after exposure to water for a period of at least five minutes. Temporary wet strength agents are those which show less than 50% of their original wet strength after being saturated with water for five minutes. Both classes of material find application in the present invention, though permanent wet strength agents are believed to offer advantages when a pad of the present invention is to be used in a wet state for a prolonged period of time.
  • The amount of wet strength agent added to the pulp fibers may be at least about 0.1 dry weight percent, more specifically about 0.2 dry weight percent or greater, and still more specifically from about 0.1 to about 3 dry weight percent based on the dry weight of the fibers.
  • Permanent wet strength agents will provide a more or less long-term wet resilience to the structure. In contrast, the temporary wet strength agents would provide structures that had low density and high resilience, but would not provide a structure that had long-term resistance to exposure to water. The mechanism by which the wet strength is generated has little influence on the products of this invention as long as the essential property of generating water-resistant bonding at the fiber/fiber bond points is obtained.
  • Suitable permanent wet strength agents are typically water soluble, cationic oligomeric or polymeric resins that are capable of either crosslinking with themselves (homocrosslinking) or with the cellulose or other constituent of the wood fiber. The most widely used materials for this purpose are the class of polymer known as polyamide-polyamine-epichlorohydrin (PAE) type resins. Examples of these materials have been sold by Hercules, Inc., Wilmington, Del., as KYMENE 557H. Related materials are marketed by Henkel Chemical Co., Charlotte, N.C. and Georgia-Pacific Resins, Inc., Atlanta, Ga.
  • Polyamide-epichlorohydrin resins are also useful as bonding resins in this invention. Materials developed by Monsanto and marketed under the SANTO RES label are base-activated polyamide-epichlorohydrin resins that may be used in the present invention. Although they are not as commonly used in consumer products, polyethylenimine resins are also suitable for immobilizing the bond points in the products of this invention. Another class of permanent-type wet strength agents is exemplified by the aminoplast resins obtained by reaction of formaldehyde with melamine or urea.
  • Suitable temporary wet strength resins include, but are not limited to, those resins that have been developed by American Cyanamid and are marketed under the name PAREZ 631 NC (now available from Cytec Industries, West Paterson, N.J.). Other temporary wet strength agents that could find application in this invention include modified starches such as those available from National Starch and marketed as CO-BOND 1000. With respect to the classes and the types of wet strength resins listed, it should be understood that this listing is simply to provide examples and that this is neither meant to exclude other types of wet strength resins, nor is it meant to limit the scope of this invention.
  • Although wet strength agents as described above find particular advantage for use in connection with this invention, other types of bonding agents may also be used to provide the necessary wet resiliency. They may be applied at the wet end of the basesheet manufacturing process or applied by spraying or printing, etc. after the basesheet is formed or after it is dried.
  • Wet and dry tensile strengths of the absorbent layer can be measured with a universal testing machine device such as an Instron apparatus, and using a crosshead speed of 10 inches per minute with a 4-inch gage length and a 3-inch jaw width under TAPPI standard conditions (samples conditioned 4 hours at 50% relative humidity and 73° F.). The dry tensile strength (taken either in the machine direction, the cross direction, or the geometric mean of the cross and machine directions) of the absorbent layer may be any of the following: about 500 g/3 in or greater, about 1000 g/3 in or greater, about 1500 g/3 in or greater, about 2000 g/3 in or greater, about 2500 g/3 in or greater, and about 3000 g/3 in or greater, such as from about 800 g/3 in to about 3000 g/3 in. The wet tensile strength (taken either in the machine direction, the cross direction, or the geometric mean of the cross and machine directions) of the absorbent layer may be any of the following: about 200 g/3 in or greater, about 500 g/3 in or greater, about 700 g/3 in or greater, about 800 g/3 in or greater, about 1000 g/3 in or greater, about 1500 g/3 in or greater, and about 2000 g/3 in or greater, such as from about 500 g/3 in to about 2500 g/3 in.
  • Optionally, the absorbent layer of the present invention may include a multi-ply paper sheet, formed of two or more similar or different paper plies. For example, a laminate of two or more tissue layers or a laminate of an airlaid web and a wetlaid tissue may be formed using adhesives or other means known in the art. It may be necessary, however, when forming a multi-ply absorbent layer, to provide a secure attachment between the plies to ensure good product performance under expected conditions. For example, an adhesive such as a hot melt adhesive or other known secure attachment means may be used to securely bind the separate plies together to form the absorbent layer of the scrubbing pad. Exemplary hot melt adhesives may include, without limitation, EVA (ethylene vinyl acetate) hot melts (e.g., copolymers of EVA), polyolefin hotmelts, polyamide hotmelts, pressure sensitive hot melts, styrene-isoprene-styrene (SIS) copolymers, styrene-butadiene-styrene (SBS) copolymers; ethylene ethyl acrylate copolymers (EEA); polyurethane reactive (PUR) hotmelts, and the like. In one embodiment, poly(alkyloxazoline) hotmelt compounds may be used. Isocyanates, epoxies, and other known adhesives may also be used. Specific examples of adhesives that may be suitable for some embodiments of the present invention include SUNOCO CP-1500 (an isotactic polypropylene) of Sunoco Chemicals (Philadelphia, Pa.); Eastman C10, Eastman C18, and Eastman P1010 (an amorphous polypropylene) of Eastman Chemical (Longview, Tex.); Findley H1296 and Findley H2525A of Bostik Findley; HM-0727, HM-2835Y, and 8151-XZP of H.B. Fuller Company (St. Paul, Minn.); and National Starch 34-1214 and other adhesives of the National Starch 34 series, made by National Starch and Chemical Corp. (Bridgewater, Conn.). Useful adhesives comprising EVA may include, by way of example, the EVA HYSOL® hotmelts of Henkel Loctite Corporation (Rocky Hill, Conn.), including 232 EVA HYSOL®, 236 EVA HYSOL®, 1942 EVA HYSOL®, 0420 EVA HYSOL® SPRAYPAC®, 0437 EVA HYSOL® SPRAYPAC®, CoolMelt EVA HYSOL®, QuikPac EVA HYSOL®, SuperPac EVA HYSOL®, and WaxPac EVA HYSOL®. EVA-based adhesives can be modified through the addition of tackifiers and other conditioners, such as Wingtack 86 tackifying resin manufactured by Goodyear Corporation (Akron, Ohio).
  • In one embodiment, the adhesive material may be a bicomponent fiber disposed between two adjacent layers such as a sheath-core bicomponent fiber. In addition to conventional bicomponent binder fibers, a fiber comprising two different varieties of polylactic acid may be used, for polylactic acid may have melting points ranging from about 120° C. to 175° C., allowing one form with a high melting point to serve as the core with a lower melting point variety serving as the sheath.
  • Latex materials may also serve as the adhesive joining two layers in the product of the present invention. Examples of latex adhesives include latex 8085 from Findley Adhesives. In some embodiments, however, the product is substantially latex free, or may have less than 10 weight percent latex, more specifically less than 5 weight percent latex, and most specifically about 2 weight percent latex or less. The latex referred to for any purpose in the present specification may be any latex, synthetic latex (e.g., a cationic or anionic latex), or natural latex or derivatives thereof.
  • When hot melt is used as a binder material to join adjacent layers of material, any known device for applying hot melt may be used, including melt blown devices, ink jet printer heads, spray nozzles, and pressurized orifices.
  • The dry absorbent layer may have an Air Permeability value greater than 30 cubic feet per minute (CFM), such as about 40 CFM or greater, about 60 CFM or greater, and about 80 CFM or greater. Alternatively, the absorbent layer may have an Air Permeability between about 15 and 30 CFM, or from about 20 CFM to about 80 CFM. Much higher values are also possible. For example the Air Permeability of the absorbent layer may be about 150 CFM or greater, 200 CFM or greater, 300 CFM or greater, or 400 CFM or greater. By way of example, uncreped through-air dried tissue comprising high-yield fibers has been measured to have 615 CFM in a 20 gsm web; a sample of Scott® Towel (Kimberly-Clark Corp., Dallas, Tex.) was measured to have a permeability of 140 CFM; a sample of VIVA® paper towel (Kimberly-Clark Corp., Dallas, Tex.) was measured to have a permeability of 113 CFM.
  • A dry scrubbing product comprising an abrasive layer and an absorbent layer need not be substantially gas permeable, but nevertheless may have an Air Permeability of any of the following: about 10 CFM or greater, about 50 CFM or greater, about 80 CFM or greater, about 100 CFM or greater, about 200 CFM or greater, about 300 CFM or greater, and about 350 CFM or greater, such as from about 10 CFM to about 500 CFM, or from about 20 CFM to about 350 CFM, or from about 30 CFM to about 250 CFM, or from about 40 CFM to about 400 CFM.
  • The abrasive layer and the absorbent layer may be combined to form the scrubbing pad of the present invention by any suitable method. In general, the abrasive layer and the absorbent layer are combined in a manner that provides integrity to the final product not only in a dry state but in a wet state. For instance, meltspun layers deposited on tissue webs, for example, may readily attach to each other when dry, but when wetted, may have a tendency to delaminate.
  • In this regard, various methods can be used in order to attach the abrasive layer to the absorbent layer. For instance, bonding between the layers can be accomplished by applying an adhesive, thermal point bonding, ultrasonic bonding, hot nip pressing, crimping, embossing, and combinations thereof.
  • In one particular embodiment, in order to better adhere or bond a meltspun layer to a tissue web, various anchoring agents may be incorporated into the tissue web for bonding with the polymeric material used to form the meltspun web. In general, the anchoring agent may be any suitable material that is compatible with the polymeric material used to form the meltspun fibers. For example, in one embodiment, the anchoring agent may comprise synthetic fibers that are incorporated into the tissue web. The synthetic fibers may be incorporated into the tissue web in an amount less than about 10% by weight, such as in an amount from about 3% to about 6% by weight. When present, the synthetic fibers bond to the meltspun fibers while remaining buried in the web to help anchor the meltspun web to the tissue web. The synthetic fibers may comprise, for instance, polyolefin fibers such as polyethylene fibers and/or polypropylene fibers, polyester fibers, nylon fibers, and the like. The synthetic fibers may be made from a copolymer or terpolymer of any of the above listed polymers or may comprise a blend of polymers. The synthetic fibers may also comprise multicomponent fibers such as sheath and core bicomponent fibers. Such bicomponent fibers may include, for instance, polyethylene/polypropylene fibers, polypropylene/polyethylene fibers, or polyethylene/polyester fibers.
  • The synthetic fibers can have any suitable fiber length that allows the fibers to be incorporated into the tissue web. Thus, the fiber length may be dependent upon how the web is formed, such as whether the web is formed in a wetlaid process or in an airforming process. In general, longer fiber lengths may increase the ability of the synthetic fibers to anchor the abrasive layer to the absorbent layer. In one embodiment, for instance, the synthetic fibers may have a length of up to about 50 mm, such as from about 1 mm to about 25 mm. For instance, in one embodiment, the fibers may have a length of from about 3 mm to about 10 mm.
  • In order to make the anchoring agent available to the meltspun fibers, the anchoring agent may also be incorporated into the tissue web so as to be present in greater amounts on at least one surface of the web. For instance, in one embodiment, a stratified fiber furnish may be used to form the tissue web. The stratified fiber furnish may include at least one outer layer that contains the anchoring agent, such as synthetic fibers.
  • Once present in the tissue web, the anchoring agent may bond to the meltspun web in different ways depending upon the anchoring agent chosen and the material used to form the abrasive layer. For example, in one embodiment, synthetic fibers may be present in the tissue web that are thermally bonded to the fibers in a meltspun web. In this embodiment, the meltspun web may be deposited onto the tissue web in a molten state causing fiber bonding to occur. In fact, in one embodiment, the tissue web may be likewise preheated prior to contact with the meltspun web in order to place the synthetic fibers in a molten state.
  • In addition to thermal bonding, however, it should be understood that various other bonds may form. For example, in an alternative embodiment, the anchoring agent forms a mechanical bond with the abrasive layer. In this embodiment, the anchoring agent may comprise synthetic fibers having a relatively long length that are entangled with the fibers contained in the abrasive layer that causes mechanical bonds to form.
  • In still another embodiment, a chemical bond may form between the anchoring agent and the abrasive layer. The chemical bond may be, for instance, covalent or ionic.
  • FIG. 3 illustrates one possible method of combining the layers wherein a meltblown layer 32 is formed directly on the paper web 34 at forming machine 110. In this embodiment, an anchoring agent such as synthetic fibers may be incorporated into the paper web 34. The synthetic fibers may then thermally bond with the meltblown layer 32 as the meltblown layer solidifies on the web.
  • In an embodiment such as that illustrated in FIG. 3, it may be desirable to maintain an elevated temperature of the meltblown as it hits the tissue such that the meltblown material may bond with the fibers of the tissue layer. Without wishing to be bound by theory, it is believed that for good adhesion of the meltblown layer to the tissue during use, i.e., when the laminate is wet and subjected to scrubbing action, a portion of the meltblown material may be bonded and/or entangled with the fibers of the tissue web or may have penetrated within the porous matrix of the tissue web enough to prevent delamination of the meltblown layer from the tissue when the tissue is wetted. Achieving such results may be done through the use of heated air to carry the meltblown from the meltblown spinnerets to the tissue web, and/or the use of vacuum beneath the tissue web to pull a portion of the viscous meltblown material into the porous matrix of the tissue web. For example, vacuum may be applied in the formation zone to help pull the polymer fibers into the web for better bonding with the synthetic fibers and possible entanglement with the cellulosic fibers. When vacuum is used, however, care should be taken to prevent excessive airflow in the vicinity of the tissue that could solidify the meltblown fibers prior to contacting the tissue. Narrow vacuum boxes, controlled air flow rates, pulsed vacuum, and other means, optionally coupled with radiative heating or other means of temperature control of the materials or fluids (e.g., air), may be used by those skilled in the art to optimize the bonding between the abrasive layer and the absorbent layer.
  • In one embodiment, the cellulosic web may be preheated or heated as the polymeric fibers are deposited thereon (whether by meltblown or spunbond formation directly on the cellulosic web, or by joining a previously formed layer of polymeric fibers to the cellulosic web). For example, an IR lamp or other heating source may be used to heat the cellulosic web in the vicinity where polymeric fibers contact the cellulosic web. By heating the surface of the cellulosic web, better bonding between the synthetic fibers in the tissue web and the polymeric fibers may be achieved, especially when the fibers are newly formed, cooling meltblown fibers. A combination of heating and suction beneath the cellulosic web may be helpful.
  • In addition to the above techniques, if desired, an adhesive may also be applied in between the paper web 34 and the meltblown layer 32. The adhesive may further bond the layers together in addition to the bond that is formed between the synthetic fibers and the meltblown fibers. Further, heat and/or pressure may be applied to the composite product to fuse the layers together by a thermal bonding process. Pressure may be applied using a mechanical press. For instance, point bonding, roll pressing and stamping may be used in order to further ensure that the polymeric fibers of the meltblown layer 32 are bonded to the synthetic fibers contained within the paper web 34.
  • Alternatively, the paper web and the abrasive layer of the scrubbing pad may be separately formed, and then attached later, after formation. For example, as illustrated in FIG. 4, paper web 34 and meltblown web 32 may be guided together with guide rolls 102 and 104 and brought in contact between roll 100 and roll 80.
  • When a thermoplastic-containing abrasive layer has been previously formed and is no longer hot enough to readily bond to the synthetic fibers of the absorbent layer, heat may be applied to cause joining of the abrasive layer with the absorbent layer as the two are brought into contact or after the two are brought into contact. For example, the absorbent layer may be preheated sufficiently to cause partial fusion of the abrasive layer as it touches the paper web, optionally with the assistance of mechanical compression. Alternatively, heat may be applied to the tissue and/or the abrasive layer after the two have been brought into contact to cause at least partial fusion of the meltblown layer with the absorbent layer. The heat may be applied conductively, such as by contacting the tissue layer against a heated surface that heats the synthetic fibers sufficiently to cause fusion of parts of the abrasive layer in contact with the tissue, preferably without heating the polymeric layer too much. Radiative heating, radio frequency heating (e.g., microwave heating), inductive heating, convective heating with heated air, steam, or other fluids, and the like may be applied to heat the tissue layer and the polymeric layer while in contact with each other, or to independently heat either layer prior to being joined to the other.
  • Ultrasonic bonding and pattern bonding may also be applied. For example, a rotary horn activated by ultrasonic energy may compress parts of the abrasive layer against the tissue web and cause fusion of the synthetic fibers and the polymeric fibers of the meltspun layer due to a welding effect driven by the ultrasound. Likewise, a patterned heated plate or drum may compress portions of the abrasive layer in contact with the tissue to cause the compressed portions such that good attachment of the compressed portions to the tissue web is achieved.
  • In an alternative embodiment, as shown in FIG. 5, the layers of the present invention may be brought together after formation, using thermal bonding in combination with an adhesive 82. The adhesive 82 may be applied to one or both layers of the pad prior to contact with each other. In this embodiment, the paper web 34 and the meltblown web 32 are brought into contact with each other between roll 100 and roll 80. At least one of the rolls 100 or 80 is heated for causing thermal bonding to occur between the meltblown web 32 and synthetic fibers contained within the paper web 34. As shown in FIG. 5, an adhesive applicator 82 sprays an adhesive in between the layers prior to the hot embossing or calender process.
  • An adhesive may be applied to one or both of the layers of the scrubbing pad by any method. For example, in addition to a spray method, as illustrated in FIG. 5, an adhesive may be applied through any known printing, coating, or other suitable transfer method. In addition, the adhesive may be any suitable adhesive which may firmly bond the layers of the pad together. The basis weight of the adhesive may be about 5 gsm or greater, such as from about 10 gsm to about 50 gsm, more specifically about 15 gsm to about 40 gsm. Alternatively, the basis weight of the added adhesive may be less than about 5 gsm.
  • As described above, in addition to synthetic fibers, the anchoring agent of the present invention may comprise other suitable materials. For instance, in one embodiment, instead of incorporating synthetic fibers into the tissue web, a polymer latex may be impregnated into the web that is compatible with the material used to form the abrasive layer. The latex polymer impregnated into the tissue web may be, for instance, a hot melt material. Such materials include, but are not limited to, anionic styrene-butadiene copolymers, polyvinyl acetate homopolymers, vinyl-acetate ethylene copolymers, vinyl-acetate acrylic copolymers, ethylene-vinyl chloride copolymers, ethylene-vinyl chloride-vinyl acetate terpolymers, acrylic polyvinyl chloride polymers, acrylic polymers, nitrile polymers, and any other suitable anionic latex polymers known in the art. The charge (e.g., anionic or nonionic) of the hot melt polymers described above can be readily varied, as is well known in the art, by utilizing a stabilizing agent having the desired charge during preparation of the latex. Other examples of suitable latexes may be described in U.S. Pat. No. 3,844,880 to Meisel, Jr., et al., which is incorporated herein in its entirety by reference thereto for all purposes.
  • Particular examples of polymeric materials that may be used in accordance with the present invention include ethylene vinyl acetate copolymers and ethylene vinyl alcohol polymers.
  • The above latex polymers may be incorporated into the tissue web using any suitable method. For instance, the polymers may be sprayed onto the tissue web or printed onto the web using a flexographic printer, an ink jet printer, or a rotogravure printer.
  • The above latex polymers are particularly well suited to bonding with meltspun webs made from block copolymers. The block copolymers may be, for instance, styrene-butadiene block copolymers, such as styrene-ethylene-butylene-styrene (SEBS), styrene-butadiene-styrene (SBS), styrene-isoprene-styrene (SIS), and the like. The block copolymers may also be polyether block copolymers (e.g., PEBAX), copolyester polymers, polyester/polyether block polymers, and the like.
  • The most suitable method of joining the layers of the scrubbing pad together may depend at least in part on the textures of the layers. As previously discussed, the meltblown layer and/or the paper web may be formed on relatively smooth forming surfaces and therefore display little three dimensional surface texture, or alternatively, one or both of the layers may be formed on highly texturized surfaces. For instance, FIGS. 6 and 7 illustrate a scrubbing pad 30 formed of an abrasive layer 32 joined to a paper web 34, both of which are have relatively smooth surface textures. In such an embodiment, any of a number of methods could be used to join the layers together including methods involving adhesives, heat, pressure, or any combination thereof.
  • In an alternative embodiment, one or both of the layers may exhibit a high degree of surface texture. For example, as illustrated in FIG. 8, the meltblown layer 32 may be a highly textured meltblown layer and the paper web 34 may be relatively flat. In such an embodiment, a spot bonding method may be preferred to firmly bond the layers at those points where the meltblown layer 32 and the paper web 34 contact while maintaining the texture of the meltblown layer 32. Any of a variety of known spot bonding methods may be used, including those methods involving various heat and optionally adhesives, without subjecting the composite structure to excessive pressure which could damage the texture of the meltblown layer 34. Of course, the scrubbing pad may optionally be formed of a highly textured paper web bonded to a relatively flat abrasive layer. Alternatively, both of the layers may be highly textured, and may have the same or different texturing patterns.
  • FIG. 9 illustrates another embodiment of the scrubbing pad wherein both the absorbent layer 34 and the abrasive layer 32 display a high degree of three-dimensional texture. In the embodiment illustrated in FIG. 9, both layers have the same, nested texturing pattern. Alternatively, the layers may have different texturing patterns. As with the other embodiments, the only limitation in the method of joining the two layers together is that the desired surface texture of a layer not be destroyed in the attachment method. For example, when the two layers display different, overlapping texturing patterns, a spot bonding method may be preferred.
  • In an embodiment such as that illustrated in FIG. 9, the surface texture in one of the layers may be formed when the two layers are attached together. For example, the absorbent layer 34 may be a highly textured cellulosic fibrous web, such as an uncreped through dried paper web, and the abrasive layer 32 may be formed on or bonded to the absorbent layer and may conform to the texturing pattern of the absorbent layer at the time the two layers are combined. For instance, heat may be applied to the composite article as a part of the bonding process. This may cause the abrasive layer to soften and take on the texturing pattern of the absorbent layer, and the abrasive layer may continue to display the same texture pattern as the absorbent layer after the layers are attached together.
  • Increasing the surface texture of the abrasive layer in such a manner may increase the overall abrasiveness of the composite product. Thus, a synergy may exist between the two layers, and the overall abrasiveness of the composite scrubbing article at the abrasive surface may be greater than the abrasiveness of either layer prior to the attachment.
  • Moreover, in those embodiments wherein the absorbent layer of the web can exhibit a high degree of wet resilience, the added texture of the abrasive layer can endure, even after the scrubbing article has been saturated with water or some other cleaning fluid.
  • The composite scrubbing pad may exhibit a synergy between the layers in other ways as well. For example, the fibers of the two layers may be physically entangled or fused together in the attachment process, such that there is a fairly strong bond between the layers. In such an embodiment, the tensile strength of the composite product may be greater than the sum of the tensile strengths of the two layers prior to attachment, or, alternatively, greater than the tensile strength measured when the two layers are coextensively disposed adjacent to one another but not bonded together, and tested together for combined tensile strength.
  • The composite scrubbing pads of the present invention may exhibit desired cleaning characteristics, such as good abrasiveness and wet resiliency, for example while requiring less raw material and having good flexibility for easy handling. For example, in one embodiment, the scrubbing pads of the present invention may have an overall basis weight of less than 150 gsm. The scrubbing pads of the present invention may also be less than about 7 mm in thickness. More particularly, the scrubbing pads may be less than about 4 mm in thickness. The abrasive layer may have a thickness of about 0.5 mm or greater, as measured with the equipment used in the Thickness Variation test, or the thickness may be any of the following values: about 1 mm or greater, about 2 mm or greater, about 3 mm or greater, about 4 mm or greater, about 5 mm or greater, such as from about 0.5 mm to 10 mm, or from about 1 mm to 5 mm. Alternatively, the thickness of the abrasive layer can be less than 3 mm.
  • Additional layers may also be included in the scrubbing pad of the present invention, if desired. For instance, the scrubbing pad of the present invention may include two abrasive layers on opposite surfaces of the pad, both attached to one or more absorbent layers which are sandwiched in the middle of the pad.
  • In one embodiment of the present invention, a barrier layer formed of a barrier material or sizing agent may be included in or on either side of the absorbent layer. This may be useful when small quantities of a cleaning compound are used (e.g., a furniture polish, a window washer, or a harsh agent such as an oven cleaning agent), wherein wetting the entire pad is undesirable. For example, a barrier layer may be placed on the absorbent layer, opposite the abrasive layer. In one embodiment, the barrier material may be removable. For example, in one embodiment of the present invention a barrier layer may include a water impervious barrier material on the outer surface of the absorbent layer that may allow the hand to remain dry during use.
  • The barrier material, in one embodiment, may be a hydrophobic film. It should be understood, however, that any suitable water impermeable material may be used. For instance, suitable moisture barrier materials include films, wovens, nonwovens, laminates, or the like. The barrier material may be a liquid impermeable web or sheet of plastic film such as polyethylene, polypropylene, polyvinylchloride or similar material. Moreover, the barrier material may occupy only a portion of the surface area of the paper web or may substantially cover an entire surface of the paper web.
  • In addition to the paper web and the abrasive layer, the scrubbing pad of the present invention may also contain additional materials within either layer as well as additional functional layers or components. For example, a portion of the pad may provide a soap, detergent, waxes or polishing agents such as furniture polish, metal cleaners, leather and vinyl cleaning or restoration agents, stain removers for rubbing on clothing, laundry pre-treatment solutions, enzymatic solutions for improved cleaning or fabric conditioning, odor control agents such as the active ingredients of Fabreze® odor removing compound (Procter and Gamble, Cincinnati, Ohio), water proofing compounds, shoe polish, dyes, glass cleaner, antimicrobial compounds, wound care agents, lotions and emollients, and the like. Other possible additives that may be added to the scrubbing pad include buffering agents, antimicrobials, skin wellness agents such as lotions, medications (i.e. anti-acne medications), or hydrophobic skin barriers, odor control agents, surfactants, mineral oil, glycerin and the like.
  • The active ingredients may be present in a solution on the wipe as it is packaged or in a solution that is added to the wipe prior to use. Active ingredients can also be present as a dry powder attached to fibers in the wipe, or as a dry compound impregnated in the fibers or in void spaces between the fibers of the wipe, or encapsulated in water-soluble capsules, encapsulated in waxy or lipid-rich shells to permit escape upon mechanical compression or shear, or in a container attached to or cooperatively associated with the wipe that may be opened during use or prior to use.
  • Application of the additives may be by any suitable method, such as:
      • Direct addition to a fibrous slurry prior to formation of the paper web.
      • A spray applied to a layer or the composite pad. For example, spray nozzles may be mounted over the moving paper web or the meltblown web to apply a desired dose of a solution to the layer that may be moist or substantially dry. Printing onto the web, such as by offset printing, gravure printing, flexographic printing, ink jet printing, digital printing of any kind, and the like.
      • Coating onto one or both surfaces of a layer, such as blade coating, air knife coating, short dwell coating, cast coating, and the like.
      • Extrusion from a die head of an agent in the form of a solution, a dispersion or emulsion, or a viscous mixture such as one comprising a wax, softener, debonder, oil, polysiloxane compound or other silicone agent, an emollient, a lotion, an ink, or other additive.
      • Application to individualized fibers. For example, prior to deposit on the forming surface, the meltblown fibers may be entrained in an air stream combined with an aerosol or spray of the compound to treat individual fibers prior to incorporation into the meltblown layer.
      • Impregnation of the wet or dry paper web with a solution or slurry, wherein the compound penetrates a significant distance into the thickness of the web, such as more than 20% of the thickness of the web, more specifically at least about 30% and most specifically at least about 70% of the thickness of the web, including completely penetrating the web throughout the full extent of its thickness.
      • Foam application of an additive to a layer (e.g., foam finishing), either for topical application or for impregnation of the additive into the paper web under the influence of a pressure differential (e.g., vacuum-assisted impregnation of the foam).
      • Padding of a chemical agent in solution into an existing fibrous web.
      • Roller fluid feeding of the additive for application to the web.
      • Application of the agent by spray or other means to a moving belt or fabric which in turn contacts the layer to apply the chemical to the layer.
  • The application level of an additive may generally be from about 0.1 weight % to about 10 weight % solids relative to the dry mass of the layer to which it is applied. More specifically, the application level may be from about 0.1% to about 4%, or from about 0.2% to about 2%. Higher and lower application levels are also within the scope of the present invention. In some embodiments, for example, application levels of from 5% to 50% or higher may be considered.
  • Printing, coating, spraying, or otherwise transferring a chemical agent or compound on one or more sides of the pad, or of any layer or material in the pad may be done uniformly or heterogeneously, as in a pattern, using any known agent or compound (e.g., a silicone agent, a quaternary ammonium compound, an emollient, a skin-wellness agent such as aloe vera extract, an antimicrobial agent such as citric acid, an odor-control agent, a pH control agent, a sizing agent; a polysaccharide derivative, a wet strength agent, a dye, a fragrance, and the like). Any known method may be used for application of such additives.
  • In one embodiment, the scrubbing pad may be provided and the desired additive compound may be held in a separate container or dispenser. In this embodiment, the additive may be applied to the pad by the consumer in the desired amount at the time of use.
  • The layers of the scrubbing pad of the present invention may be combined to form a product of any desired size or shape and suited for any particular purpose. For example, FIG. 6 illustrates one embodiment of the present invention wherein a meltblown layer 32 substantially covers the surface of a paper web 34 to form a rectangular scrubbing pad such as may be held in the hand during use. In such an embodiment, the scrubbing pad may be reversed to provide both abrasive and non-abrasive type cleaning.
  • Alternatively, the meltblown layer may only partially cover the surface of the paper web, creating a single scrubbing surface on a scrubbing pad which may have both a coarse abrasive region and a smooth, absorbent region. Thus, the user may control the abrasiveness of the cleaning action during cleaning by, for instance, adjusting the angle of the pad or the region of the pad to which pressure is applied and may have different levels of scrubbing action on the same side of a single scrubbing pad.
  • The scrubbing pads of the present invention may be provided in any shape or orientation. For example, the pads may be square, circular, rectangular, or the like. They may be formed into mitts, such as hand-shaped mitts for scrubbing with the hand or foot-shaped covers for the feet. The pads may be packaged and sold in either a wet or dry form, and may optionally be shaped to be attached to a handle or gripper to form a convenient cleaning tool such as a wiper with a squeegee, a mop, a toilet cleaning tool, a dishwashing wipe, a scouring pad, a scrubbing tool for cleaning metal, ceramic, or concrete surfaces, a polishing or sanding tool, and the like.
  • For example, one embodiment of the invention, as illustrated in FIG. 10, shows the scrubbing pad of the present invention 30 shaped so as to be attachable to a base 220 of a rigid gripping device. The base 220 is attached to a handle 210 shaped to be comfortably held by a user, such as is found on a mop or smaller, hand-held scrubbing device. The scrubbing pad 30 may be held onto the base 220 by any method that can firmly hold the pad, yet, in one embodiment, can release the pad for replacement quickly and easily. For example, the pad 30 may be held onto base 220 at gripping slots 225. In another embodiment, the scrubbing pad 30 may be permanently attached to the base 220, and the entire device can be disposable.
  • The cleaning tool of the present invention can be used to clean or scrub many different surfaces, and can be designed for a specific use. For example, the cleaning tool can have a handle including a long wand and be used to clean floors, walls, ceilings, ceiling fans, light fixtures, windows and the like. In certain embodiments, such as when the cleaning tool is used to clean windows, for example, the cleaning tool can have a squeegee attachment, such as a rubber material squeegee attached to a surface as is generally known in the art. In other embodiments, the abrasive layer on the cleaning tool can be used for sanding or polishing a surface to be cleaned.
  • TEST METHODS
  • “Gurley Stiffness” refers to measurements of the stiffness of a web made with a Gurley™ Bending Resistance Tester, Model 4171-D (Precision Instruments, Troy, N.Y.). Tests are made with samples conditioned for at least four hours under TAPPI conditions (50% relative humidity, 23° C.). A suitable method for determining Gurley stiffness values follows that set forth in TAPPI Standard Test T 543 OM-94, but modified to use sample lengths of 1.5 inches instead of 2 inches, and sample widths of 1.0 inches instead of 2 inches. Using a 1-inch wide sample that is 1.5 inches long, the formula to convert the Gurley reading to Gurley Stiffness with units of milligrams is:
    Stiffness=Gurley reading*11.1 mg*(inches from center/1 inch)*(weight/5 g).
  • Thus, a Gurley reading of 8 taken when a 25 g weight was used 2 inches from center would be converted to a stiffness of 8*11.1 mg*2*(25 g/5 g)=888 mg.
  • The abrasive layers of the present invention and/or the laminated products of the present invention may have a Gurley stiffness of about 2500 mg or less, specifically about 1500 mg or less, more specifically about 800 mg or less, more specifically still about 400 mg or less, and most specifically about 200 mg or less, such as from about 40 mg to 350 mg or from about 80 mg to about 400 mg. These stiffness values may be the maximum value obtainable for measurements in any direction of the web or product (the maximum stiffness), or in the machine direction or cross-direction (MD or CD stiffness, respectively).
  • “Thickness Variation” refers to the nonuniformity of the thickness of an abrasive layer. The measurement involves taking spaced apart measurements of sample thickness with a TMI Model 49-62 Precision Micrometer (Testing Machines, Inc., Amityville, N.Y.) having a 0.63-inch diameter foot that applies a pressure of 7.3 psi (50 kPa). Testing is done after the instrument has warmed up for one hour and is done under TAPPI standard conditions. Strips of the material to be tested are measured at spots on one-inch centers to provide multiple measurements per strip. At least 3 strips of material are used, and at least 9 readings per strip are taken. The thickness variation is the standard deviation of the thickness results, reported in millimeters.
  • “Wet Opacity” and “Dry Opacity” refer to measurements of the optical opacity of a sample in the dry or wet state, respectively, using a Technibrite™ Micro TB-1 C device (Technidyne Corp., New Albany, Ind.), according to manufacturer directions for ISO opacity, with testing done for samples with the abrasive layer up. Testing is done under TAPPI standard conditions. Wet Opacity is the measurement of opacity of a sample that has been wetted by immersing and soaking the sample for one minute deionized water at 23° C. The sample is then removed from the water, holding it by one corner to allow excess water to drain for three seconds. The sample is then placed on dry blotter paper for 20 seconds, then turned over and placed on another dry blotter and allowed to sit for another 20 seconds, then immediately tested for opacity.
  • In some embodiments, the articles of the present invention have a relatively low Wet Opacity, such that the user can observe the presence of spots or other objects through the wetted article during cleaning. Conventional sponges and other cleaning articles tend to be substantially opaque, but the translucent nature of the articles in some embodiments of the present invention may be of use in some cleaning situations. Thus, the articles of the present invention may have a Wet Opacity less than about any of the following: 95%, 90%, 80%, 70%, 60%, 50%, and 40%, with exemplary ranges of from 30% to 95%, or from 50% to 90%, or from 40% to 80%. Dry Opacity may be greater than 96%, such as about 100%, or may be less than 96%, such as from 80% to about 95%, or from 50% to 90%, or from 40% to 85%. In one embodiment, the difference between dry opacity and wet opacity of the article can be at least about 10%.
  • “Overall Surface Depth”. A three-dimensional basesheet or web is a sheet with significant variation in surface elevation due to the intrinsic structure of the sheet itself. As used herein, this elevation difference is expressed as the “Overall Surface Depth.” The basesheets useful for this invention may possess three-dimensionality and may have an Overall Surface Depth of about 0.1 mm. or greater, more specifically about 0.3 mm. or greater, still more specifically about 0.4 mm. or greater, still more specifically about 0.5 mm. or greater, and still more specifically from about 0.4 to about 0.8 mm. However, products made substantially flat tissue are within the scope of certain embodiments of the present invention as well.
  • The three-dimensional structure of a largely planar sheet may be described in terms of its surface topography. Rather than presenting a nearly flat surface, as is typical of conventional paper, three-dimensional sheets useful in producing the present invention have significant topographical structures that, in one embodiment, may derive in part from the use of sculptured through-drying fabrics such as those taught by Chiu et al. in U.S. Pat. No. 5,429,686, previously incorporated by reference. The resulting basesheet surface topography typically comprises a regular repeating unit cell that is typically a parallelogram with sides between about 2 and 20 mm in length. For wetlaid materials, these three-dimensional basesheet structures may be created by molding the moist sheet or may be created prior to drying, rather than by creping or embossing or other operations after the sheet has been dried. In this manner, the three-dimensional basesheet structure is more likely to be well retained upon wetting, helping to provide high wet resiliency and to promote good in-plane permeability. For airlaid basesheets, the structure may be imparted by thermal embossing of a fibrous mat with binder fibers that are activated by heat. For example, an airlaid fibrous mat containing thermoplastic or hot melt binder fibers may be heated and then embossed before the structure cools to permanently give the sheet a three-dimensional structure.
  • In addition to the regular geometrical structure imparted by the sculptured fabrics and other fabrics used in creating a basesheet, additional fine structure, with an in-plane length scale less than about 1 mm, may be present in the basesheet. Such a fine structure may stem from microfolds created during differential velocity transfer of the web from one fabric or wire to another prior to drying. Some of the materials of the present invention, for example, appear to have fine structure with a fine surface depth of 0.1 mm or greater, and sometimes 0.2 mm or greater, when height profiles are measured using a commercial moiré interferometer system. These fine peaks have a typical half-width less than 1 mm. The fine structure from differential velocity transfer and other treatments may be useful in providing additional softness, flexibility, and bulk. Measurement of the surface structures is described below.
  • An especially suitable method for measurement of Overall Surface Depth is moiré interferometry, which permits accurate measurement without deformation of the surface. For reference to the materials of the present invention, surface topography should be measured using a computer-controlled white-light field-shifted moiré interferometer with about a 38 mm field of view. The principles of a useful implementation of such a system are described in Bieman et al. (L. Bieman, K. Harding, and A. Boehnlein, “Absolute Measurement Using Field-Shifted Moiré,” SPIE Optical Conference Proceedings, Vol.1614, pp. 259-264, 1991). A suitable commercial instrument for moiré interferometry is the CADEYES® interferometer produced by Medar, Inc. (Farmington Hills, Mich.), constructed for a nominal 35-mm field of view, but with an actual 38-mm field-of-view (a field of view within the range of 37 to 39.5 mm is adequate). The CADEYES® system uses white light which is projected through a grid to project fine black lines onto the sample surface. The surface is viewed through a similar grid, creating moiré fringes that are viewed by a CCD camera. Suitable lenses and a stepper motor adjust the optical configuration for field shifting (a technique described below). A video processor sends captured fringe images to a PC computer for processing, allowing details of surface height to be back calculated from the fringe patterns viewed by the video camera.
  • In the CADEYES moiré interferometry system, each pixel in the CCD video image is said to belong to a moiré fringe that is associated with a particular height range. The method of field-shifting, as described by Bieman et al. (L. Bieman, K. Harding, and A. Boehnlein, “Absolute Measurement Using Field-Shifted Moiré,” SPIE Optical Conference Proceedings, Vol. 1614, pp. 259-264, 1991) and as originally patented by Boehnlein (U.S. Pat. No. 5,069,548, herein incorporated by reference), is used to identify the fringe number for each point in the video image (indicating which fringe a point belongs to). The fringe number is needed to determine the absolute height at the measurement point relative to a reference plane. A field-shifting technique (sometimes termed phase-shifting in the art) is also used for sub-fringe analysis (accurate determination of the height of the measurement point within the height range occupied by its fringe). These field-shifting methods coupled with a camera-based interferometry approach allows accurate and rapid absolute height measurement, permitting measurement to be made in spite of possible height discontinuities in the surface. The technique allows absolute height of each of the roughly 250,000 discrete points (pixels) on the sample surface to be obtained, if suitable optics, video hardware, data acquisition equipment, and software are used that incorporates the principles of moiré interferometry with field shifting. Each point measured has a resolution of approximately 1.5 microns in its height measurement.
  • The computerized interferometer system is used to acquire topographical data and then to generate a grayscale image of the topographical data, said image to be hereinafter called “the height map.” The height map is displayed on a computer monitor, typically in 256 shades of gray and is quantitatively based on the topographical data obtained for the sample being measured. The resulting height map for the 38-mm square measurement area should contain approximately 250,000 data points corresponding to approximately 500 pixels in both the horizontal and vertical directions of the displayed height map. The pixel dimensions of the height map are based on a 512×512 CCD camera which provides images of moiré patterns on the sample which can be analyzed by computer software. Each pixel in the height map represents a height measurement at the corresponding x- and y-location on the sample. In the recommended system, each pixel has a width of approximately 70 microns, i.e. represents a region on the sample surface about 70 microns long in both orthogonal in-plane directions). This level of resolution prevents single fibers projecting above the surface from having a significant effect on the surface height measurement. The z-direction height measurement must have a nominal accuracy of less than 2 microns and a z-direction range of at least 1.5 mm. (For further background on the measurement method, see the CADEYES Product Guide, Integral Vision (formerly Medar, Inc.), Farmington Hills, Mich., 1994, or other CADEYES manuals and publications of Medar, Inc.)
  • The CADEYES system can measure up to 8 moiré fringes, with each fringe being divided into 256 depth counts (sub-fringe height increments, the smallest resolvable height difference). There will be 2048 height counts over the measurement range. This determines the total z-direction range, which is approximately 3 mm in the 38-mm field-of-view instrument. If the height variation in the field of view covers more than eight fringes, a wrap-around effect occurs, in which the ninth fringe is labeled as if it were the first fringe and the tenth fringe is labeled as the second, etc. In other words, the measured height will be shifted by 2048 depth counts. Accurate measurement is limited to the main field of 8 fringes.
  • The moiré interferometer system, once installed and factory calibrated to provide the accuracy and z-direction range stated above, can provide accurate topographical data for materials such as paper towels. (Those skilled in the art may confirm the accuracy of factory calibration by performing measurements on surfaces with known dimensions.) Tests are performed in a room under TAPPI conditions (73° F., 50% relative humidity). The sample must be placed flat on a surface lying aligned or nearly aligned with the measurement plane of the instrument and should be at such a height that both the lowest and highest regions of interest are within the measurement region of the instrument.
  • Once properly placed, data acquisition is initiated using CADEYES® PC software and a height map of 250,000 data points is acquired and displayed, typically within 30 seconds from the time data acquisition was initiated. (Using the CADEYES® system, the “contrast threshold level” for noise rejection is set to 1, providing some noise rejection without excessive rejection of data points.) Data reduction and display are achieved using CADEYES® software for PCs, which incorporates a customizable interface based on Microsoft Visual Basic Professional for Windows (version 3.0), running under Windows 3.1. The Visual Basic interface allows users to add custom analysis tools.
  • The height map of the topographical data may then be used by those skilled in the art to identify characteristic unit cell structures (in the case of structures created by fabric patterns; these are typically parallelograms arranged like tiles to cover a larger two-dimensional area) and to measure the typical peak to valley depth of such structures. A simple method of doing this is to extract two-dimensional height profiles from lines drawn on the topographical height map which pass through the highest and lowest areas of the unit cells. These height profiles may then be analyzed for the peak to valley distance, if the profiles are taken from a sheet or portion of the sheet that was lying relatively flat when measured. To eliminate the effect of occasional optical noise and possible outliers, the highest 10% and the lowest 10% of the profile should be excluded, and the height range of the remaining points is taken as the surface depth. Technically, the procedure requires calculating the variable which we term “P10,” defined at the height difference between the 10% and 90% material lines, with the concept of material lines being well known in the art, as explained by L. Mummery, in Surface Texture Analysis: The Handbook, Hommelwerke GmbH, Mühlhausen, Germany, 1990. In this approach, which will be illustrated with respect to FIG. 14, the surface 531 is viewed as a transition from air 532 to material 533. For a given profile 530, taken from a flat-lying sheet, the greatest height at which the surface begins—the height of the highest peak—is the elevation of the “0% reference line” 534 or the “0% material line,” meaning that 0% of the length of the horizontal line at that height is occupied by material. Along the horizontal line passing through the lowest point of the profile, 100% of the line is occupied by material, making that line the “100% material line” 535. In between the 0% and 100% material lines (between the maximum and minimum points of the profile), the fraction of horizontal line length occupied by material will increase monotonically as the line elevation is decreased. The material ratio curve 536 gives the relationship between material fraction along a horizontal line passing through the profile and the height of the line. The material ratio curve is also the cumulative height distribution of a profile. (A more accurate term might be “material fraction curve.”)
  • Once the material ratio curve is established, one may use it to define a characteristic peak height of the profile. The P10 “typical peak-to-valley height” parameter is defined as the difference 537 between the heights of the 10% material line 538 and the 90% material line 539. This parameter is relatively robust in that outliers or unusual excursions from the typical profile structure have little influence on the P10 height. The units of P10 are mm. The Overall Surface Depth of a material is reported as the P10 surface depth value for profile lines encompassing the height extremes of the typical unit cell of that surface. “Fine surface depth” is the P10 value for a profile taken along a plateau region of the surface which is relatively uniform in height relative to profiles encompassing a maxima and minima of the unit cells. Measurements are reported for the most textured side of the basesheets of the present invention, which is typically the side that was in contact with the through-drying fabric when airflow is toward the through-dryer.
  • Overall Surface Depth is intended to examine the topography produced in the tissue web, especially those features created in the sheet prior to and during drying processes, but is intended to exclude “artificially” created large-scale topography from dry converting operations such as embossing, perforating, pleating, etc. Therefore, the profiles examined should be taken from unembossed regions if the tissue web has been embossed, or should be measured on an unembossed tissue web. Overall Surface Depth measurements should exclude large-scale structures such as pleats or folds which do not reflect the three-dimensional nature of the original basesheet itself. It is recognized that sheet topography may be reduced by calendering and other operations which affect the entire basesheet. Overall Surface Depth measurement may be appropriately performed on a calendered basesheet.
  • The CADEYES® system with a 38-mm field of view may also be used to measure the height of material on an abrasive layer relative to the underlying tissue web, when there are openings in the abrasive layer that permit optical access to and measurement of the surface of the tissue web. When the abrasive layer comprises a translucent material, obtaining good optical measurements of the surface topography may require application of white spray paint to the surface to increase the opacity of the surface being measured.
  • Test for Abrasive Index
  • As used herein, the “Abrasiveness Index” is a measure of the ability of an abrasive layer to abrade away material from a block of a foam that is moved over the surface of the abrasive layer in a prescribed manner under a fixed load. The Abrasiveness Index is reported as the lost mass in grams per foot of travel of a weighted foam block, multiplied by 100, when the foam is moved through a complete sixteen-inch test cycle. The procedure used is a modified form of ASTM F1015, “Standard Test Method for Relative Abrasiveness of Synthetic Turf Playing Surfaces.” A higher Abrasiveness Index is taken to be indicative of a more abrasive surface.
  • To prepare for measurement of the Abrasiveness Index, foam test blocks are cut from a phenolic foam material to have dimensions of 1 inch by 1 inch by 1.25 inches. The foam is a well known commercial green foam marketed as “Dry Floral Foam,” product code 665018/63486APP, manufactured by Oasis Floral Products, a division of Smithers-Oasis Company of Kent, Ohio (UPC 082322634866), commonly used for floral arrangements for silk flowers and dried flowers.
  • A sample is cut from the material to be tested and taped to a flat, rigid table surface using two-sided Manco® Indoor/Outdoor Carpet Tape, marketed by Manco, Inc. of the Henkel Group of Avon, Ohio (UPC 075353071984). The tape is first placed on the table surface, avoiding overlapping of tape segments to ensure that a substantially uniform adhesive surface is provided having dimensions of at least 4 inches by 4 inches. The sample is then centered over the taped region and gently pressed into place. A 3-inch by 3-inch square plastic block with a thickness of 1 -inch and mass of 168 grams is placed on the sample to define a test area that is centered within at least a 4-inch by 4-inch region of the table having the double-sided tape. A brass cylinder, 2-inches in diameter with a mass of 1 kg is centered on the plastic block and allowed to reside for 10 seconds to secure the sample to the taped region. A marker is used to trace around the border of the plastic block to draw the test area. The block and weight are removed from the sample. The sides of the drawn square (3-inches by 3-inches) should be aligned with the machine-direction and cross-direction of the material being tested, when such directions are defined (e.g., the shute direction for a woven abrasive layer).
  • FIG. 13 is a schematic of the set-up for the Abrasiveness Index test for the sample 280 to be tested. The sample 280 may have an upwardly facing abrasive layer 32 which may be joined to an underlying tissue web (not shown). Double-sided tape 270 joins the sample 280 to a table surface (not shown). A foam block 274 is placed in the lower right-hand corner 282A of the square test region 272 marked on the upper surface of the sample 280. The dimensions of the surface of the foam block 274 contacting the sample 280 are 1-inch by 1-inch. On top of the foam block 274 is placed a 100 g brass weight 276 having a circular footprint 1-inch in diameter. Two sides of the foam block 274 on the sample 280 are substantially superimposed over the inside boundary of the corner 282A of the marked test region 272.
  • To conduct the test, the foam block 274 is steadily moved by hand from the lower right-hand corner 282A (the initial corner) to the upper right-hand corner 282B of the test region 272, and then to the other corners 282C, 282D, and back to 282A again, ensuring that the foam block 274 travels along but not outside of the boundaries of the marked test area 272. Care is taken not to apply downward or upward force by hand, but to apply only steady lateral force to move the foam block 274 successively from one corner to another as indicated by the arrows 278A-278D. Both hands of the operator may be used as necessary to maintain the uprightness of the weighted foam block 274. The block is moved at a steady rate of about 5 seconds per side (a side being the path from one corner to the next corner). The path traced by the foam block 274 defines a square, ending at the initial corner 282A.
  • To achieve a smooth, steady motion, one finger (e.g., the thumb) should be on the “rear” vertical surface of the foam block 274 to push the block in the desired direction, and another finger should be on the “forward” vertical surface to maintain a steady position of the foam block 274.
  • After the block 274 has returned to the initial corner 282A, the path is reversed, again without lifting the weighted block 274. The block 274 thus follows the same path it once traced but in reverse order, going from the initial corner 282A to the lower left-hand corner 282D to the upper left-hand corner 282C to the upper right-hand corner 282B back to the initial lower right-hand corner 282A, being moved by steady lateral pressure and maintaining a rate of 5 seconds per side.
  • During this process, a portion of the foam block 274 will have been removed by abrasion during the 16-inch total path it travels (two eight-inch cycles). The 100-gram weight 276 is removed and the foam block 274 is then weighed and the amount of the foam block 274 removed by abrasion is determined by difference and recorded. This process is repeated two more times, using new materials (new double-sided tape 270, new samples 280 of the same material being tested, and new foam blocks 274), allowing the lost mass to be determined three times. The average of the three measurements is taken and converted to mass lost per 12 inches by multiplication with the correction factor of 12/16 (i.e., normalized to a path of 12 inches), and then multiplied by 100. The resulting parameter is reported as the Abrasiveness Index for the material being tested.
  • The abrasive layers of the present invention may have an Abrasiveness Index of about 1 or greater, about 2 or greater, about 3 or greater, about 4 or greater, or about 5 or greater, such as from about 1.5 to 10, or from about 2 to about 7.
  • EXAMPLE 1 Preparation of an Uncreped Through Dried Basesheet
  • To demonstrate an example of a textured, wet resilient absorbent web with improved dry feel, a suitable basesheet was prepared. The basesheet was produced on a continuous tissue-making machine adapted for uncreped through-air drying. The machine comprises a Fourdrinier forming section, a transfer section, a through-drying section, a subsequent transfer section and a reel. A dilute aqueous slurry at approximately 1% consistency was prepared from 100% bleached chemithermomechanical pulp (BCTMP), pulped for 45 minutes at about 4% consistency prior to dilution. The BCTMP is commercially available as Millar-Western 500/80/00 (Millar-Western, Meadow Lake, Saskatchewan, Canada). Kymene 557LX wet strength agent, manufactured by Hercules, Inc. (Wilmington, Del.) was added to the aqueous slurry at a dosage of about 16 kg of Kymene per ton of dry fiber, as was carboxymethylcellulose at a dose of 1.5 kg per ton of dry fiber. The slurry was then deposited on a fine forming fabric and dewatered by vacuum boxes to form a web with a consistency of about 12%. The web was then transferred to a transfer fabric (Lindsay Wire T-807-1) using a vacuum shoe at a first transfer point with no significant speed differential between the two fabrics, which were traveling at about 5.0 meters per second (980 feet per minute). The web was further transferred from the transfer fabric to a woven through-drying fabric at a second transfer point using a second vacuum shoe. The through drying fabric used was a Lindsay Wire T-1 16-3 design (Lindsay Wire Division, Appleton Mills, Appleton, Wis.). The T-116-3 fabric is well suited for creating molded, three-dimensional structures. At the second transfer point, the through-drying fabric was traveling more slowly than the transfer fabric, with a velocity differential of 27%. The web was then passed into a hooded through dryer where the sheet was dried. The dried sheet was then transferred from the through-drying fabric to another fabric, from which the sheet was reeled. The basis weight of the dry basesheet was approximately 30 gsm (grams per square meter). The sheet had a thickness of about 1 mm, an Overall Surface Depth of about 0.4 mm, a geometric mean tensile strength of about 1000 grams per 3 inches (measured with a 4-inch jaw span and a 10-inch-per minute crosshead speed at 50% relative humidity and 22.8° C.), a wet:dry tensile ratio of 45% in the cross-direction, an MD:CD tensile ratio of 1.25, and 17% MD stretch, 8.5% CD stretch.
  • The Air Permeability of the web was measured at 440 CFM.
  • EXAMPLE 2 A Laminate With a First Meltblown Polypropylene Web
  • High molecular weight isotactic polypropylene, Achieve 3915 manufactured by ExxonMobil Chemical Comp. (Houston, Tex.) was used in a pilot meltblown facility to make a polymer network by meltblown fiberization. The molecular weight range of the polymer is about 130,000 to 140,000. According to the manufacturer, the melt flow rate of the polymer according to ASTM D1238 is 70 g/10 min, which is believed to be below the range of melt flow rates for polymers typically used in a meltblown operation; the polymer is normally used for a spunbond operation or other applications other than meltblowing. (For example, a typical meltblown polymer such as polypropylene PP3546G of ExxonMobil Chemical Corp. has a melt flow rate of 1200 g/10 min, measured according to ASTM D1238, and polypropylene PP3746G of the same manufacturer has a melt flow rate of 1500 g/10 min.) The high viscosity material was found to be surprisingly useful for producing the coarse meltblown web according to the present invention.
  • The polypropylene was extruded through a meltblown die at 485° F. on a porous Teflon conveyor web with an underlying vacuum. The web speed was 10 ft/min. A meltblown polypropylene network with a basis weight of 85 to 120 gsm was generated by adjusting the temperature, air pressure, and the distance between the blown head to the forming table, as well as the flow rate of the polymer.
  • FIG. 12 is a schematic drawing of a central cutaway portion of the meltblown die 120 drawn according to the meltblown die used in this Example. The primary portion of the die comprises two side blocks 242, 242′, and a triangular central feed block 244 through which polymer is injected into an internal chamber 250. The central feed block 244 is substantially an isosceles triangle in cross-section, converging to an apex 246 at a 60-degree angle. Along the apex 246 are drilled a series of evenly spaced holes 248 in fluid communication with the internal chamber 250. The internal chamber 250 is also in fluid communication with a pressurized source of molten polymer (not shown) which forces molten polymer through the holes 248 of the central feed block 244 to form strands of polymer (not shown). Air jets 258, 258′ flow through the gaps 252, 252′, respectively, between the side blocks 242, 242′ and the central feed block 244. The gaps 252, 252′ are in fluid communication with a source of pressurized air (not shown) which generates the flow of the air jets 258, 258′ toward the apex 246 of the central feed block 244. The air in the jets 258, 258′ is typically heated well above the melting point of the polymer to prevent premature cooling of the polymer strands. For this Example, the air temperature was about 480° F. In conventional meltblown operation, the air jets 258, 258′ provide a high level of shear that may cause extensional thinning of the polymer strands and also provide a high level of turbulence to separate the strands and create isolated, randomly positioned fibers. For purposes of the present invention, however, the air flow rate may be decreased to reduce turbulence, allowing some adjacent polymer strands from adjacent holes 248 to coalesce into multifilamentary aggregates, which still provide enough air flow and turbulence to deposit the polymer strands as a network of fibers on an underlying carrier web (not shown).
  • The holes 248 have a diameter of 0.015 inches and were drilled at 30 per inch. The width of the active region of the die 120 (the region provided with holes 248 for formation of polymer strands) was 11.5 inches. The entire die 120 was 14 inches wide. The gaps 252, 252′ had a width of 0.055 inches, determined by shims placed between the central feed block 244 and the side blocks 242, 242′ at the outside ends of the die 120 (not shown), away from the active region. The drill depth 256 of the holes 248 is the distance into the central feed block 244 that had to be penetrated during drilling to each the central chamber 250. In this case, the drill depth was about 4 mm. The height of the central feed block 244 (the distance from the base 254 to the apex 246) was 52 mm, and the depth of the internal chamber 250 (the height of the central feed block 244 minus the drill depth 256) was about 48 mm.
  • Not shown is a backing plate for the die block 120 through which pressurized polymer melt was injected, the air injection lines, and supporting structures for the die. Such features are well known and easily provided by those skilled in the art. (It should be recognized that numerous alternatives to the meltblown die of FIG. 12 are still within the scope of the present invention, such as a die with two or more rows of holes 248 that may be arranged in a staggered array, parallel lines, and the like, or dies in which annular jets or air surround the exiting polymer strand.)
  • In producing the meltblown web with coarse multifilamentary aggregates, it was found that the “normal” elevation of the meltblown die relative to the carrier wire, namely, 11 inches, was too high for the modified run conditions according to the present invention. At this normal height, the strands had become too cool when they hit the wire for good fiber to fiber bonding (here the term “fiber” encompasses multifilamentary aggregates), and the resulting web lacked integrity. The head was then lowered several inches, allowing good fiber-fiber bonding to occur. The distance from the die's apex to the carrier wire was about 7 inches. In practice, the optimum height for a given polymer will be a function of web speed (and thus the flow rate of the polymer) and the temperatures of both the polymer and the heated air.
  • For the system shown in FIG. 12, conventional meltblown operation is achieved when the pressurized air source applied to the air gaps 252, 252′ is about 40 to 50 psig. For the present Example, however, when lower airflow rates were desired to produce coarser fibers, the pressurized air source was set to about 12 psig to 20 psig during the runs to yield a durable abrasive network with good material properties for the purposes of the present invention. Thus, less than about half the air flow rate of conventional meltblown operation was used.
  • A micrometer (Fowler Precision Tools, Model S2-550-020) was used to measure the diameter of the polypropylene fibers in the meltblown material. Twenty fibers were randomly selected and measured. A range of 70 microns to 485 microns was obtained, with a mean of 250 microns and a standard deviation of 130 microns. Multifilamentary aggregates formed a significant portion of the meltblown web.
  • Testing of Thickness Variation, as previously described, in one set of samples (measured basis weight of 120 gsm) gave a standard deviation of 0.25 mm (mean thickness was 1.18 mm) for the meltblown web. By way of comparison, a more conventional meltblown web produced at Kimberly-Clark for commercial use with a basis weight of 39 gsm was measured to have a standard deviation of 0.03 mm (mean thickness was 0.29 mm).
  • Gurley stiffness measurements of the meltblown web gave an average MD stiffness of 138.8 mg, with a standard deviation of 35.9 mg. The CD stiffness was 150 mg, with a standard deviation of 34.0 mg. The basis weight of the measured samples was 120 gsm.
  • The Air Permeability of the meltblown web with multifilamentary aggregates was measured at 1130 CFM (mean of 6 samples). When two layers of the meltblown were superimposed, the Air Permeability for the two layers together was measured at 797 CFM (mean of three measurement locations).
  • The meltblown web was joined to the uncreped tissue web of Example 1. In a first run (Run 2-A), the meltblown web was joined to a cut section of the uncreped through-dried tissue web to make a first laminate using a hot melt adhesive (NS-5610, National Starch Chemical Company of Berkeley, Calif.) applied in a swirl spray pattern at 320° F. with a hot melt applicator. The meltblown web showed excellent adhesion and performed well in scrubbing (high scratch resistance).
  • In a second run (Run 2-B), the meltblown web was joined to the tissue web to make a second laminate using thermal bonding achieved with a Sunbeam® Model 3953-006 1200 Watt iron on the highest (“linen”) heat setting. The tissue web, cut to three-inches by six-inches, was placed over a meltblown web cut to the same size, and the iron was placed on the tissue web and pressed with mild pressure (ca. 10 lbs of force) for about two to three seconds, then lifted and placed on an adjacent spot. This was repeated several times, with each spot of the tissue typically being contacted with the iron for two or three times, until the meltblown web became well bonded with the tissue without the meltblown web losing its abrasive characteristics. (In practice, temperature, application pressure, and duration of heating may all be optimized for the particular product being made.)
  • The Air Permeability of a cut sample of the laminate was measured at 316 CFM.
  • The surface topography of the second laminate was measured using moiré interferometry, as previously described. A 38-mm field of view optical head (nominally 35-mm) was used. To improve the opacity of the polypropylene fibers, the sample was lightly sprayed with a flat white spray paint, using a can of Krylon® 1502 flat white paint (Sherwin-Williams, Cleveland, Ohio), sprayed from a distance of about 6 inches with a sweeping motion and about 2 seconds of residence time for most portions of the painted laminate. The applied paint did not appear to fill or block pores that were visible to the eye on the tissue, and did not appear to significantly modify the topography of the surface. The Air Permeability of the lightly painted laminate was measured at 306 CFM.
  • The multifilamentary aggregates had widths ranging from about 100 to about 500 microns. Several of the multifilamentary aggregates twisted 180 degrees or more over a short distance. Without wishing to be bound by theory, it is believed that the common twisting of the multifilamentary aggregates presents a more abrasive surface than if the multifilamentary aggregates remain substantially flat (relative to the paper web) and untwisted. In one embodiment, a region of 3 centimeters square (3 cm×3 cm) will have, on the average (based on sampling at least 20 representative 3 cm square regions), at least one multifilamentary aggregate making a twist of at least 180 degrees about its axis. More specifically, there may be at least 5, at least 10, at least 15, or at least 50 multifilamentary aggregates that each undergo a twist along their respective axes of at least 180 degrees, and in one embodiment, at least 360 degrees or at least 720 degrees. In one embodiment, at least one multifilamentary aggregate in the 3 cm square area has a helically twisted structure such that a 360 degree twist occurs within a distance of no more than 3 cm, more specifically no more than 1 cm, along the length of the fiber (following the path of the fiber).
  • For the laminate of Run 2-B, the topography of the abrasive layer on the underlying uncreped through-dried tissue was measured using the CADEYES® system. The profile showed a variety of peaks and valleys corresponding to elevated and depressed regions, respectively, along a profile line. The surface depth along the profile line across the height map was 1.456 mm.
  • Ten samples made from Run 2-B were tested for Wet and Dry Opacity. Average Dry Opacity was 67.65% (standard deviation 1.14%), and the average Wet Opacity was 53.97% (standard deviation 3.1%), with an average of 1.60 grams of water per gram of fiber in the wetted samples (standard deviation 0.15 grams of water per gram of fiber). By way of comparison, a Chore Boy® Golden Fleece™ Scouring Cloth (UPC # 0 26600 30316 7), marketed by Reckitt & Colman Inc. Wayne, N.J., showed Dry Opacity of 95.1% for three samples, a Wet Opacity of 95.83%, and a water pickup of 0.54 grams of water per gram of solid (standard deviation of 0.16 gram of water per gram of solid).
  • In a third run (Run 2-C), the meltblown web was thermally bonded to plain white SCOTT® Towel (UPC 054000173431—core code JE2 11 290 01) produced by Kimberly-Clark Corp. (Dallas, Tex.) by ironing, as described for Run 2-B above. The Air Permeability was measured at 118 CFM, while two samples of the SCOTT® Towel tissue alone taken from different rolls were measured at 140 CFM and 135 CFM. A sample of the meltblown web simply placed on top of the SCOTT® Towel tissue sample with an Air Permeability value of 135 CFM, overlaid without thermal bonding of the two layers, yielded an Air Permeability of 134 CFM, suggesting that the process of thermal bonding causes obstruction of some pores in the tissue web to slightly reduce the Air Permeability relative to an unbonded combination of the tissue and the abrasive layer.
  • In a fourth run (Run 2-D), the meltblown web was thermally bonded to commercially available VIVA® towel, produced by Kimberly-Clark Corp. (Dallas, Tex.) by ironing, as described for Run 2-B above. The VIVA® towel was produced according to a double recrepe process using a latex adhesive. The Air Permeability was measured at 97.1 CFM.
  • In a related trial, a similar polymer was used to create another meltblown polymer web according to the methods described in this Example. Instead of Achieve 3915 polypropylene by ExxonMobil Chemical Corp., Achieve 3825 polypropylene was used to produce a meltblown web with similar properties to that obtained with the Achieve 3915 polymer. The Achieve 3825 polypropylene is a metallocene grade polypropylene having a melt flow rate of 32 g/10 min. Multifilamentary aggregates were also produced with similar characteristics to those obtained with the Achieve 3915 polymer. Higher back pressure was required to extrude the molten Achieve 3825 polymer, requiring about 400 psig in comparison to 280 psig for the Achieve 3915, due to the lower melt flow rate.
  • EXAMPLE 3 A Second Meltblown Polypropylene Web
  • Bassell PF015 polypropylene manufactured by Bassell North America (Wilmington, Del.) having a nominal processing temperature of about 221° C. was used to produce a second meltblown polypropylene web to be used in making laminates with tissue. A pilot facility distinct from that of Example 2 was used. The meltblown web was produced through a meltblown tip (30 holes per inch, hole diameter 0.0145 inches) producing 4 pounds per inch of machine width per hour (4 PIH). Coarseness in the fiber was achieved by progressively lowering processing temperatures and primary air pressure while targeting basis weights varying between about 50 gsm and 100 gsm. For 50 gsm meltblown, the line speed was 78 feet per minute, and for 100 gsm meltblown, the line speed was 39 feet per minute. Initial processing temperatures of about 500° F. (260° C.) were lowered to between about 392° F. (200° C.) to about 410° F. (210° C.), with the die tip at 410° F. (210° C.). Primary air pressure was lowered from the normal range of 3.5-4 psig to less than 0.5 psig. Dietip and spinpump pressures were about 170-190 psig and 340-370 psig, respectively. These settings were reached iteratively in order to obtain a coarse meltblown web, with good abrasiveness by virtue of being molded against the carrier wire. In conventional operation, meltblown fibers are relatively solidified when they land on the carrier wire and are not molded to a significant degree against the carrier wire, but in this case the meltblown fibers were still soft enough that they could conform to the texture of the carrier wire such that the meltblown web received a molded, abrasive texture.
  • The meltblown was formed at basis weights of about 50 gsm and at about 100 gsm as a stand-alone product, and also deposited directly on the uncreped through-dried tissue of Example 1 and on commercial VIVA® paper towels. The meltblown web alone was measured to have an average MD Gurley Stiffness value of 113.7 mg (standard deviation of 34.5 mg) and an average CD Gurley Stiffness value of 113.0 mg (standard deviation of 41.9 mg). The tested samples had a basis weight of 100 gsm.
  • Testing of Thickness Variation in one set of high-basis weight samples (measured basis weight of 100 gsm) gave a standard deviation of 0.07 mm (mean thickness was 0.99 mm) for the meltblown web.
  • Measurement of Air Permeability for a single layer of the meltblown gave a value in excess of 1500 CFM. Two superimposed plies of the meltblown web gave an Air Permeability of 1168 CFM (mean of measurements at six locations).
  • In one run (Run 3-A), the same uncreped through-dried tissue made in Example 1 was used, with 50 gsm meltblown being formed directly on the tissue web. The meltblown layer yielded a Surface Depth of about 0.728 mm. A repeating structure was seen corresponding with the topography of the carrier wire against which the meltblown web was molded during formation. A unit cell of the repeating structure, which was a parallelogram, had sides of about 9.5 mm and 1.5 mm.
  • The laminate had an Air Permeability measured at 381 CFM (mean of measurements at six locations).
  • Some runs were also conducted by inverting the web after the meltblown layer had been formed on one surface, and again applying a meltblown layer to the opposing surface such that the tissue had an abrasive layer on both sides.
  • Another set of samples (Run 3-B) were prepared by ironing the meltblown web with the tissue of Example 1, following the ironing procedures given in Example 2. Eight samples were tested for Wet and Dry Opacity. Average Dry Opacity was 64.0% (standard deviation 0.82%), and the average Wet Opacity was 47.2% (standard deviation 2.2%), with an average of 1.59 grams of water per gram of fiber in the wetted samples (standard deviation 0.10 grams of water per gram of fiber).
  • Another laminate (Run 3-C) was produced by forming the meltblown web directly on a VIVA® paper towel.
  • Laminates were also made by joining the abrasive layer to a hydroentangled wiper using a hotmelt adhesive applied in a swirl pattern. The wiper, manufactured by Kimberly-Clark Corporation (Dallas, Tex.), was WypAll®) Teri® wipes, whose package is marked with U.S. Pat. No. 5,284,703, issued Feb. 8, 1994 to Everhart et al., which discloses a composite fabric containing more than about 70 percent, by weight, pulp fibers which are hydraulically entangled into a continuous filament substrate (e.g., a spunbond web).
  • EXAMPLE 4 Variation of the Second Meltblown Web
  • A meltblown web was made according to Example 3, but with several variations such that little molding against the carrier wire could occur (lower air temperature and larger distance from the die tip to the carrier wire, allowing the meltblown fibers to cool more quickly). Though fibers were still coarser than conventional meltblown fibers, the abrasive character of the meltblown web was tangibly reduced due to the lack of large-scale topography imparted to the meltblown web. (The meltblown web appeared to be free of multifilamentary aggregates, which, it is believed, if present, would have contributed to a higher abrasive characteristic regardless of the macroscopic topography imparted by molding against a carrier wire.)
  • EXAMPLE 5 Synergistic Material Properties
  • To demonstrate the Strength Synergy and Stretch Synergy of several embodiments of the present invention, tensile testing was done of laminates and unbonded layers using the first meltblown web of Example 2. Results are shown in Table 1 below, where tests are reported as averages for multiple samples (five samples per measurement). The meltblown web alone had a mean tensile strength of 3393 grams per 3 inches (measured with a 4-inch gage length and 10-in-per-minute crosshead speed with an Instron Universal Testing Machine). When placed adjacent to a sample of Scott® towel (a commercial uncreped through-air dried tissue web comprising about 25% high-yield pulp fibers and wet strength resins) but not bonded thereto (the two webs were superimposed and tested together), the tensile strength was 3707 g/3-in. When the meltblown web was thermally bonded (as described in Example 2) to the Scott® towel, the tensile strength increased to 5385 g/3-in, an increase of 45%, giving a Strength Synergy of 1.45. The Stretch Synergy was 2.06.
  • In another run, the meltblown web was tested together with the uncreped through-air dried tissue web of Example 1 (labeled as “30 gsm UCTAD”), giving an average tensile strength of 3565 g/3-in when the two webs were unbonded, but an average tensile strength 3915 g/3-in for webs that were thermally bonded, for a Strength Synergy of about 1.10. The Stretch Synergy was 1.36.
  • In a third run, VIVA® towel was used as the tissue. The Strength Synergy was 1.22, and the Stretch Synergy was 1.44.
    TABLE 1
    Measurements of Strength and Stretch Synergy
    Sample Basis Tensile
    Descrip- Wt., Strength, St. Strength Stretch, St. Stretch
    tion gsm g/3 in. Dev Synergy % Dev Synergy
    Meltblown
    120 3393 461 3.26 0.51
    MB alone
    SCOTT ® 43.5 2763 65 18.65 0.56
    Towel
    Towel + 163.5 3707 750 3.18 0.80
    MB,
    Unbonded
    Towel + 163.5 5385 1099 1.45 6.54 0.88 2.06
    MB,
    Bonded
    30 gsm 32.5 1136 36 17.19 0.72
    UCTAD
    UCTAD + 152.5 3565 787 2.94 0.53
    MB,
    Unbonded
    UCTAD + 152.5 3915 575 1.10 4.00 0.49 1.36
    MB,
    Bonded
    VIVA ® 67 2092 60 26.66 0.28
    Towel
    VIVA + 187 3460 1092 3.27 0.86
    MB,
    Unbonded
    VIVA + 187 4228 838 1.22 4.72 1.2 1.44
    MB,
    Bonded
  • EXAMPLE 6 Abrasive Properties
  • To illustrate the abrasiveness of products of the present invention and commercially available scrubbing materials, Abrasive Index tests were conducted for a variety of samples made according to the present invention, as described in Examples 2 through 4, as well as for five commercial products marketed for scrubbing and cleaning, the products each comprising an abrasive layer of material.
  • The five commercial products were: A) the O-CEL-O® Heavy Duty Scrub Pad (UPC 053200072056), marketed by 3M Home Care Products (St. Paul, Minn.); B) SCOTCH BRITE® Heavy Duty Scrub Pad (UPC 051131502185), also marketed by 3M Home Care Products (St. Paul, Minn.), a product having a dark maroon-colored reticulated polymeric material believed to comprise polypropylene and other materials, C) the SCOTCH BRITE® Delicate Duty Scrub Sponge (UPC 021200000027), also marketed by 3M Home Care Products (St. Paul, Minn.)—the abrasive layer of this product was detached from the sponge for testing; D) CHORE BOY® Golden Fleece™ Scouring Cloth (UPC 026600313167), marketed by Reckitt & Colman, Inc. (Wayne, N.J.), and E) a SANI-TUFF® wiper, marketed by Kimberly-Clark Corp. (Houston, Tex.), which comprises a green colored meltblown layer on asynthetic polymer web (a heavier meltblown web), with a basis weight of about 33 gsm. The dry SANI-TUFF® wiper had an Air Permeability of 98.5 CFM (mean of three measurements).
  • Table 2 displays the Abrasive Index results. Interestingly, the meltblown web of Example 2, comprising a significant number of multifilamentary aggregates, displayed the highest Abrasiveness Index (about 5.5). The material of Run 2-D, wherein the meltblown web of Example 2 had been ironed onto a relatively smooth VIVA® paper towel, displayed a high Abrasiveness Index as well (about 4.25). The slightly lower Abrasiveness Index compared to the isolated meltblown web itself may be due to a slight decrease in surface depth of the meltblown caused by the attachment process.
  • The isolated meltblown web of Example 3 displayed a high Abrasiveness Index (about 4.5), though not as high as the meltblown web of Example 2 with multifilamentary aggregates. This abrasive material had a macroscopic topography imparted by a coarse carrier fabric, which, it is believed, contributed to its abrasiveness. For Run 3-A, the meltblown web was no longer able to receive texture from the carrier wire, for it was formed directly on the tissue of Example 1. However, the highly textured tissue is believed to have provided a macroscopic topography to the meltblown web that provided good abrasiveness nevertheless, possibly accounting for the high Abrasiveness Index (about 4) for the material of Run 3-A. However, when the meltblown web in Example 2 was formed on a relatively smooth VIVA® paper towel, which lacks the distinctive topography and high surface depth of the UCTAD tissue, the resulting Abrasiveness Index was relatively low (about 1.25), thus pointing to the importance of the topography of the meltblown web, wherein useful topographical features may be imparted by effective molding against a suitable carrier wire, or by formation of the meltblown web directly on a tissue web having good topography (e.g., a surface depth of about 0.2 mm or greater, and optionally having a repeating pattern of peaks and valleys with a characteristic unit cell having an area of about 5 square millimeters or greater, or about 8 square millimeters or greater).
  • The isolated meltblown web of Example 4 was formed on the same carrier wire as in Example 3, but under conditions that did not effectively mold the meltblown web against the topography of the carrier wire, resulting a relatively flat meltblown structure. This is believed to account for the relatively low Abrasiveness Index (about 1) found for the meltblown web of Example 4. This meltblown web yielded an Air Permeability of 973 CFM (mean of 6 measurements on different locations of the web).
  • The well-known abrasive features of commercial products A, B, and D are reflected in relatively high Abrasiveness Index values. Commercial product E, though intended for wiping purposes, employs a meltblown layer lacking the coarseness or abrasive properties of many embodiments of the present invention, and displayed a relatively low Abrasiveness Index of about 0.75.
    TABLE 2
    Comparative Abrasive Index Values
    Foam Weight,
    g Abrasiveness Index
    Sample Initial Final Specimen Avg.
    Meltblown of Example 2 0.68 0.61 5.25 5.5
    0.69 0.62 5.25
    0.68 0.6 6
    Ex. 2 Meltblown on VIVA 0.68 0.62 4.5 4.25
    (Run 2-D) 0.67 0.6 5.25
    0.68 0.64 3
    Meltblown of Example 3 0.63 0.58 3.75 4.5
    0.62 0.55 5.25
    0.68 0.62 4.5
    Ex. 3 Meltblown on UCTAD 0.58 0.53 3.75 4
    (Run 3-A) 0.65 0.59 4.5
    0.67 0.62 3.75
    Ex. 3 Meltblown on VIVA ® 0.63 0.62 0.75 1.25
    (Run 3-C) 0.57 0.55 1.5
    0.62 0.6 1.5
    Meltblown of Example 4 0.64 0.63 0.75 1
    0.65 0.64 0.75
    0.64 0.62 1.5
    Commercial Product A 0.69 0.63 4.5 4.75
    0.65 0.58 5.25
    0.66 0.6 4.5
    Commercial Product B 0.64 0.57 5.25 4
    0.65 0.6 3.75
    0.74 0.7 3
    Commercial Product C 0.66 0.63 2.25 2.5
    0.66 0.62 3
    0.64 0.61 2.25
    Commercial Product D 0.66 0.59 5.25 5
    0.64 0.58 4.5
    0.67 0.6 5.25
    Commercial Product E 0.65 0.64 0.75 0.75
    0.67 0.66 0.75
    0.66 0.65 0.75
  • These and other modifications and variations to the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention, which is more particularly set forth in the appended claims. In addition, it should be understood that aspects of the various embodiments may be interchanged both in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims.

Claims (50)

1. A wiping product comprising:
a tissue web having a first side and a second and opposite side, the tissue web containing pulp fibers and synthetic fibers;
a meltspun web attached to the first side of the tissue web, the meltspun web comprising synthetic polymeric fibers; and
wherein the meltspun web and the tissue web are combined together in a manner that causes the polymeric fibers of the meltspun web to bond with the synthetic fibers of the tissue web.
2. A wiping product as defined in claim 1, wherein the synthetic fibers are present in the tissue web in an amount of from about 30% or less based on the weight of the tissue web.
3. A wiping product as defined in claim 1, wherein the tissue web is formed from a stratified fiber furnish including a first outer layer forming the first side of the web and a second outer layer, the synthetic fibers being contained in the first outer layer.
4. A wiping product as defined in claim 1, wherein the synthetic fibers of the tissue web are thermally bonded to the fibers of the meltspun web.
5. A wiping product as defined in claim 4, wherein the tissue web and meltspun web are combined together while the meltspun web is in a molten state.
6. A wiping product as defined in claim 4, wherein the tissue web and the meltspun web are point bonded together.
7. A wiping product as defined in claim 1, wherein the tissue web comprises an uncreped through-air dried web.
8. A wiping product as defined in claim 1, wherein the tissue web has a basis weight of from about 35 gsm to about 120 gsm.
9. A wiping product as defined in claim 1, wherein the meltspun web comprises a meltblown web.
10. A wiping product as defined in claim 1, wherein the meltspun web comprises a spunbond web.
11. A wiping product as defined in claim 1, wherein the meltspun web has a basis weight of from about 30 gsm to about 200 gsm.
12. A wiping product as defined in claim 1, wherein the polymeric fibers of the meltspun web are mechanically bonded with the synthetic fibers of the tissue web.
13. A wiping product as defined in claim 1, wherein the polymeric fibers of the meltspun web are ultrasonically bonded with the synthetic fibers of the tissue web.
14. A wiping product as defined in claim 1, wherein the synthetic fibers comprise multicomponent fibers.
15. A wiping product as defined in claim 1, wherein the synthetic fibers are homogeneously mixed with the pulp fibers within the tissue web.
16. A wiping product as defined in claim 1, wherein the synthetic fibers are made from a material comprising a polyolefin and wherein the polymeric fibers are made from a material comprising a polyolefin.
17. A wiping product as defined in claim 1, wherein the synthetic fibers comprise bicomponent fibers and wherein the polymeric fibers comprise a polyolefin.
18. A wiping product as defined in claim 1, wherein the polymeric fibers comprise polyester fibers and wherein the synthetic fibers comprise nylon fibers.
19. A wiping product as defined in claim 17, wherein the polymeric fibers comprise polypropylene fibers and wherein the synthetic bicomponent fibers comprise polyethylene/polyester fibers, polyethylene/polypropylene fibers, or polypropylene/polyethylene fibers.
20. A wiping product as defined in claim 1, wherein the tissue web and the meltspun web are embossed together.
21. A wiping product as defined in claim 1, further comprising abrasive materials selected from filler particles, microspheres, mineral granules, metallic granules, and meltblown shot.
22. A wiping product as defined in claim 1, wherein both the meltblown web and the synthetic fibers comprise a hydrophobic polymer.
23. A wiping product as defined in claim 1, wherein both the meltblown web and the synthetic fibers comprise a polymer having a melting point below about 200° C.
24. A wiping product as defined in claim 1, wherein both the meltblown web and the synthetic fibers comprise a polymer derived from at least one common monomer.
25. A wiping product as defined in claim 1, wherein both the meltblown web and the synthetic fibers comprise a polymer selected from a common category, the category selected from polyamides, styrene copolymers, polyesters, polyolefins, vinyl acetate copolymers, EVA polymers, polymers derived from butadiene, polyurethanes, and silicone polymers.
26. A wiping product comprising:
a tissue web having a first side and a second and opposite side, the tissue web containing pulp fibers and an anchoring agent, the anchoring agent being present in the tissue web in an amount less than about 10% by weight;
a meltspun web attached to the first side of the tissue web, the meltspun web comprising polymeric fibers; and
wherein the anchoring agent comprises a polymer compatible with the polymeric fibers and wherein the meltspun web and the tissue web are combined together in a manner that causes the polymeric fibers of the meltspun web to bond with the anchoring agent contained in the tissue web.
27. A wiping product as defined in claim 26, wherein the anchoring agent comprises a latex polymer incorporated into the tissue web.
28. A wiping product as defined in claim 27, wherein the polymeric fibers of the meltspun web are made from a material comprising a block copolymer.
29. A wiping product as defined in claim 28, wherein the block copolymer comprises a styrene-butadiene block copolymer.
30. A wiping product as defined in claim 26, wherein the anchoring agent comprises synthetic fibers.
31. A wiping product as defined in claim 30, wherein the tissue web is formed from a stratified fiber furnish including a first outer layer forming the first side of the web and a second outer layer, the synthetic fibers being contained in the first outer layer.
32. A wiping product as defined in claim 30, wherein the tissue web and the meltspun web are point bonded together.
33. A wiping product as defined in claim 26, wherein the tissue web comprises an uncreped through-air dried web.
34. A wiping product as defined in claim 26, wherein the meltspun web comprises a meltblown web.
35. A wiping product as defined in claim 30, wherein the synthetic fibers comprise bicomponent fibers and wherein the polymeric fibers comprise a polyolefin.
36. A wiping product as defined in claim 30, wherein the polymeric fibers comprise polyester fibers and wherein the synthetic fibers comprise nylon fibers.
37. A wiping product as defined in claim 35, wherein the polymeric fibers comprise polypropylene fibers and wherein the synthetic bicomponent fibers comprise polyethylene/polyester fibers, polyethylene/polypropylene fibers, or polypropylene/polyethylene fibers.
38. A wiping product comprising:
a tissue web having a first side and a second and opposite side, the tissue web containing pulp fibers and synthetic fibers, the synthetic fibers being present in the tissue web in an amount less than about 50% by weight, the tissue web having a basis weight of from about 15 gsm to about 150 gsm;
a meltblown web attached to the first side of the tissue web, the meltblown web comprising polymeric fibers; and
wherein the meltblown web and the tissue web are combined together in a manner that causes the polymeric fibers of the meltblown web to thermally bond with the synthetic fibers of the tissue web.
39. A wiping product as defined in claim 38, wherein the tissue web is formed from a stratified fiber furnish including a first outer layer forming the first side of the web and a second outer layer, the synthetic fibers being contained in the first outer layer.
40. A wiping product as defined in claim 38, wherein the tissue web and meltblown web are combined together while the meltblown web is in a molten state.
41. A wiping product as defined in claim 38, wherein the tissue web and the meltblown web are point bonded together.
42. A wiping product as defined in claim 38, wherein the tissue web comprises an uncreped through-air dried web.
43. A wiping product as defined in claim 38, wherein the meltblown web has a basis weight of from about 30 gsm to about 200 gsm.
44. A wiping product as defined in claim 38, wherein the synthetic fibers comprise multicomponent fibers.
45. A wiping product as defined in claim 38, wherein the synthetic fibers are made from a material comprising a polyolefin and wherein the polymeric fibers are made from a material comprising a polyolefin.
46. A wiping product as defined in claim 38, wherein the synthetic fibers comprise bicomponent fibers and wherein the polymeric fibers comprise a polyolefin.
47. A wiping product as defined in claim 38, wherein the polymeric fibers comprise polyester fibers and wherein the synthetic fibers comprise nylon fibers.
48. A wiping product as defined in claim 46, wherein the polymeric fibers comprise polypropylene fibers and wherein the synthetic bicomponent fibers comprise polyethylene/polyester fibers, polyethylene/polypropylene fibers, or polypropylene/polyethylene fibers.
49. A wiping product as defined in claim 38, wherein the tissue web and the meltblown web are embossed together.
50. A wiping product as defined in claim 38, wherein the synthetic fibers have an average fiber length of from about 3 mm to about 25 mm.
US10/745,327 2003-12-23 2003-12-23 Composite structures containing tissue webs and other nonwovens Abandoned US20050136772A1 (en)