CN103553565A - Medical stone ceramic product and preparation method thereof - Google Patents
Medical stone ceramic product and preparation method thereof Download PDFInfo
- Publication number
- CN103553565A CN103553565A CN201310495276.7A CN201310495276A CN103553565A CN 103553565 A CN103553565 A CN 103553565A CN 201310495276 A CN201310495276 A CN 201310495276A CN 103553565 A CN103553565 A CN 103553565A
- Authority
- CN
- China
- Prior art keywords
- powder
- medical stone
- oxide content
- hours
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a medical stone ceramic product prepared from the following raw materials in percentage by weight: 41-45% of medical stone powder, 16-20% of potassium feldspar powder, 10-14% of soda feldspar powder, 8-10% of quartz powder and 12-17% of Laiyang soil. The preparation method comprises the following steps: weighing raw materials in percentage by weight, grinding and filtering the raw materials by a sieve with the granularity of 100-150 meshes, and uniformly mixing for later use; grinding the powder in a ball miller for 1-2 hours according to the condition that the ratio of the material to balls to water is 1:2:0.5, filtering mud through a sieve with the granularity of 32-35 meshes, and pugging to obtain a finished mud product; performing slip-casting, demoulding, correcting and grinding, and drying for 12-24 hours; sintering a dried mud blank in a furnace in steps and cooling to obtain the required product. The medical stone ceramic product is reasonable in material proportion and scientific in sintering method, so that the medical stone has improved performance, good air permeability and high plasticity, and the yield is up to 97%; the medical stone is free from toxicity and radiation, and has no change in original property and precipitated trace elements; the medical stone can be prepared into various beautiful new material tea sets, cups and other finished products.
Description
Affiliated technical field
The present invention relates to ceramic fabrication technique field, specifically a kind of Chinese medicine stone ceramic goods.
The invention still further relates to the preparation method of Chinese medicine stone ceramic goods.
Background technology
A host of facts show, contain the indispensable trace element of multiple human body and animals and plants in medical stone, and excellent adsorption, and dissolution rate is fast, very easily by animals and plants, is absorbed.Meanwhile, medical stone or a kind of Chinese medicinal materials of preciousness, can get rid of toxicant and harmful germs such as lead harmful in human body, mercury, tin, arsenic.Therefore, medical stone has special effect at aspects such as health care, disease preventing and treating, prevent cancer and delay sanility and purification of water qualitys.In order to utilize better the above-mentioned characteristic of medical stone, people are processed into various cups, pot for cooking rice by medical stone building stones in recent years, and by absorption of human body, its trace element releasing reaches the object of health care.But medical stone quality is more crisp, there is tomography the centre of most medical stone piece material, so the difficulty of processing and fabricating medical stone goods is large, cost is high, and this has affected the exploitation of medical stone to a certain extent.
In order to make full use of maifanshi resource, further improve the quality of medical stone apparatus, some contriver has proposed medical stone and other mineral materials to mix rear calcining in recent years, and trial substitutes MUSYUSHI with medical stone or purple clay is fired the Chinese medicine stone ceramic goods with nourishing function.If number of patent application is 200910118859.1, denomination of invention is < < medical stone sintering vessel and preparation method thereof > >; Number of patent application is 201210254431.1, and denomination of invention is < < medical stone fictile and preparation method thereof > >, etc.Yet, up to the present on market, there is not the Chinese medicine stone ceramic product that a technology is relatively ripe.Trace it to its cause and be mainly above-mentioned medical stone goods, its inadequate science of batching, preparation technology is not mature enough.Such as, with regard to medical stone and other mineral aggregate of selecting, the content difference of its various compositions is very large, if the purity of various mineral aggregates is not high, fusing point is different, is just difficult to burn out qualified Chinese medicine stone ceramic goods.
Summary of the invention
In order to make full use of maifanshi resource, further improve the characteristic of medical stone goods, the invention provides a kind of reasonable ratio, craft science, Chinese medicine stone ceramic goods that production cost is lower.
Another object of the present invention is to provide the preparation method of described Chinese medicine stone ceramic goods.
The technical solution adopted for the present invention to solve the technical problems is: this Chinese medicine stone ceramic goods, raw material by following weight percent is made: medical stone powder 41～45%, feldspar in powder 16～20%, albite in powder 10～14%, silica powder 8～12%, Laiyang soil 12～17%; Described medical stone powder, its dioxide-containing silica is greater than 60.00%, and alumina content is greater than 14.00%, and sodium oxide content is greater than 4.00%; Described feldspar in powder, its potassium oxide content is greater than 10.00%, and iron oxide content is less than 0.30%; Described albite in powder, its sodium oxide content is greater than 8.00%, and iron oxide content is less than 0.30%; Described silica powder, its dioxide-containing silica is greater than 98.00%, and iron oxide content is less than 0.10%; Described Laiyang soil, its dioxide-containing silica is less than 75.00%, and alumina content is greater than 13.00%, and iron oxide content is less than 1.00%.
The method of preparing Chinese medicine stone ceramic goods comprises the following steps:
(1), by described weight percent, take raw material, pulverized 100～150 mesh sieves, mixed rear standby;
(2), according to material, ball, the water ratio of 1: 2: 0.5, above-mentioned powder is ground 1～2 hour in ball mill, mud filters, makes finished product mud after pugging through 320～350 eye mesh screen;
(3), injection forming, after the demoulding, revise polishing, dry in the air 12～24 hours;
(4), finally in stove, the mud embryo drying is carried out to multi-steps sintering, cooling, make desired product;
Described multi-steps sintering is: the first stage, from normal temperature to 900 ℃, temperature rise rate is 4.2～4.5 ℃/min, calcines 3 hours; Subordinate phase, from 900～1200 ℃, temperature rise rate is 2.4～2.6 ℃/min, calcines 2 hours; Phase III, from 1200～1300 ℃, temperature rise rate is 3.2～3.3 ℃/min, calcines 0.5 hour; Fourth stage, is cooled to normal temperature from 1300 ℃, 15～20 hours time, obtains desired product; Described normal temperature is 25～35 ℃.
Beneficial effect of the present invention: be mainly batching science, make the performance of medical stone obtain better improvement.Medical stone is silicate minerals, and chemical composition is close with silicon ash, and iron, titanium content are high, and bonding strength is low, and plasticity-is little.For this reason, in batching, add Laiyang soil that plasticity is good, added bonding strength is high, have consolute characteristic potassium felspar sand and albite simultaneously.When sintering temperature rises to 1200～1250 ℃, two kinds of mineral aggregates of potassium felspar sand and albite start gradually to melt, and have brought into play good gummed effect in whole raw material.Particularly guaranteeing that medical stone goods have on the basis of some strength, density, also make this product there are the many micropores larger than natural medical stone aperture, thereby this goods dissolution rate piece, excellent adsorption, makes this product than natural medical stone, have better effect aspect body-care, function of anti-cancer and cancer prevention.Shandong Center for Disease Control & Prevention of assert through country, shows the whole conformance with standard of institute's inspection project to the detected result of 15 projects such as the lead in Chinese medicine stone ceramic goods, mercury, arsenic, volatile phenol, chromium.The pH value of goods soak solution is 8.39, is weakly alkaline.Especially the various trace elements that the human bodies such as the iron that medical stone is separated out, copper, zinc, strontium need in sample soak solution, detected.
Secondly, take multi-steps sintering, improved the yield rate of Chinese medicine stone ceramic goods.The bag water-based of medical stone mud, moulded pottery not yet put in a kiln to bake is poor, drying shrinkage is little, in calcination process, easily ftracture, be out of shape, and long interval time for mineral aggregate melting, melt viscosity high, the way that take calcine by steps, progressively heats up, strictly grasps time and the temperature of sintering, make moulded pottery not yet put in a kiln to bake experience steadily shrink, melt gummed, porcelain and change into type, stage such as cooling progressively, guaranteed the quality of medical stone goods.By statistics, sintering finished rate of the present invention reaches more than 97%.
Embodiment
Embodiment 1
Chinese medicine stone ceramic teapot, it is comprised of the raw material of following weight percent: medical stone powder 45%, its dioxide-containing silica is greater than 60.00%, and alumina content is greater than 14.00%, and sodium oxide content is greater than 4.00%; Feldspar in powder 18%, its potassium oxide content is greater than 10.00%, and iron oxide content is less than 0.30%; Albite in powder 13%, its sodium oxide content is greater than 8.00%, and iron oxide content is less than 0.30%; Silica powder 9%, its dioxide-containing silica is greater than 98.00%, and iron oxide content is less than 0.10%; Laiyang soil 15%, its dioxide-containing silica is less than 75.00%, and alumina content is greater than 13.00%, and iron oxide content is less than 1.00%.
Preparation method, comprises the following steps:
(1), by described weight percent, take raw material, pulverized 100 mesh sieves, mixed rear standby;
(2), according to material, ball, the water ratio of 1: 2: 0.5, the powder after above-mentioned mixing is ground 1 hour in ball mill, mud filters through 320 eye mesh screens, makes finished product mud after pugging;
(3), injection forming, after the demoulding, revise polishing, dry in the air 20 hours;
(4), finally in high-temperature electric resistance furnace, the mud embryo drying is carried out to multi-steps sintering: the first stage, from 20～900 ℃ of normal temperature, temperature rise rate is controlled at 4.3 ℃/min, calcines 3 hours; Subordinate phase, from 900～1200 ℃, temperature rise rate is controlled at 2.5 ℃/min, calcines 2 hours; Phase III, from 1200～1300 ℃, temperature rise rate is controlled at 3.3 ℃/min, calcines 0.5 hour; Fourth stage, is cooled to 35 ℃ of normal temperature from 1300 ℃, 16 hours time, after coming out of the stove desired product.
Embodiment 2
Chinese medicine stone ceramic cup, it is comprised of the raw material of following weight percent: medical stone powder 41%, its dioxide-containing silica is greater than 60.00%, and alumina content is greater than 14.00%, and sodium oxide content is greater than 4.00%; Feldspar in powder 20%, its potassium oxide content is greater than 10.00%, and iron oxide content is less than 0.30%; Albite in powder 12%, its sodium oxide content is greater than 8.00%, and iron oxide content is less than 0.30%; Silica powder 10%, its dioxide-containing silica is greater than 98.00%, and iron oxide content is less than 0.10%; Laiyang soil 17%, its dioxide-containing silica is less than 75.00%, and alumina content is greater than 13.00%, and iron oxide content is less than 1.00%.
Preparation method, comprises the following steps:
(1), by described weight percent, take raw material, pulverized 130 mesh sieves, mixed rear standby;
(2), according to material, ball, the water ratio of 1: 2: 0.5, the powder after above-mentioned mixing is ground 2 hours in ball mill, mud filters, makes finished product mud after pugging through 340 eye mesh screen;
(3), injection forming, after the demoulding, revise polishing, dry in the air 15 hours;
(4), finally the mud embryo drying is carried out to multi-steps sintering in high-temperature electric resistance furnace: the first stage, from 20～900 ℃ of normal temperature, temperature rise rate is controlled at 4.3 ℃/min, calcines 3 hours; Subordinate phase, from 900～1200 ℃, temperature rise rate is controlled at 2.5 ℃/min, calcines 2 hours; Phase III, from 1200～1300 ℃, temperature rise rate is controlled at 3.3 ℃/min, calcines 0.5 hour; Fourth stage, is cooled to 30 ℃ of normal temperature from 1300 ℃, 20 hours time, after coming out of the stove desired product.
The medical stone raw material of above-mentioned two products is from Shandong Province's Mengyin area.Through Silicate Research and Design Inst., Shandong Prov, the content of the medical stone raw material of above-mentioned two products is detected, the content of its silicon-dioxide reaches 62.59%, the content of aluminum oxide reaches 16.43%, the content of sodium oxide reaches 4.80%, magnesian content reaches 4.62%, iron oxide content only has 2.67%, and the content of titanium oxide only has 0.74%.
Claims (4)
1. Chinese medicine stone ceramic goods, is characterized in that: it is made by the raw material of following weight percent: medical stone powder 41～45%, feldspar in powder 16～20%, albite in powder 10～14%, silica powder 8～12%, Laiyang soil 12～17%.
2. Chinese medicine stone ceramic goods according to claim 1, is characterized in that: described medical stone powder, and its dioxide-containing silica is greater than 60.00%, and alumina content is greater than 14.00%, and sodium oxide content is greater than 4.00%; Described feldspar in powder, its potassium oxide content is greater than 10.00%, and iron oxide content is less than 0.30%; Described albite in powder, its sodium oxide content is greater than 8.00%, and iron oxide content is less than 0.30%; Described silica powder, its dioxide-containing silica is greater than 98.00%, and iron oxide content is less than 0.10%; Described Laiyang soil, its dioxide-containing silica is less than 75.00%, and alumina content is greater than 13.00%, and iron oxide content is less than 1.00%.
3. the method for preparing Chinese medicine stone ceramic goods described in claim 1, is characterized in that comprising the following steps:
(1), by described weight percent, take raw material, pulverized 100～150 mesh sieves, mixed rear standby;
(2), according to material, ball, the water ratio of 1: 2: 0.5, above-mentioned powder is ground 1～2 hour in ball mill, mud filters, makes finished product mud after pugging through 320～350 eye mesh screen;
(3), injection forming, after the demoulding, revise polishing, dry in the air 12～24 hours;
(4), finally in stove, the mud embryo drying is carried out to multi-steps sintering, cooling, make desired product;
Described multi-steps sintering is: the first stage, from normal temperature to 900 ℃, temperature rise rate is 4.2～4.5 ℃/min, calcines 3 hours; Subordinate phase, from 900～1200 ℃, temperature rise rate is 2.4～2.6 ℃/min, calcines 2 hours; Phase III, from 1200～1300 ℃, temperature rise rate is 3～3.2 ℃/min, calcines 0.5 hour; Fourth stage, is cooled to normal temperature from 1300 ℃, 15～20 hours time, after coming out of the stove desired product.
4. the method for Chinese medicine stone ceramic goods according to claim 3, is characterized in that: described normal temperature is 25～35 ℃.