CN103396093B - A kind of red soil pottery and preparation method thereof - Google Patents
A kind of red soil pottery and preparation method thereof Download PDFInfo
- Publication number
- CN103396093B CN103396093B CN201310341334.0A CN201310341334A CN103396093B CN 103396093 B CN103396093 B CN 103396093B CN 201310341334 A CN201310341334 A CN 201310341334A CN 103396093 B CN103396093 B CN 103396093B
- Authority
- CN
- China
- Prior art keywords
- parts
- red soil
- pottery
- raised
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of red soil pottery, obtained by the raw material of following weight: red soil 48 parts, 6 parts, black earth, 3 parts, grey black stone, rhombspar 3 parts, diatom ooze 40 parts and water glass adhesive 0.5 ~ 1.5 part.From the above-mentioned description of this invention, compared with prior art, the red soil pottery ecological, environmental protective of the present invention by adopting above-mentioned formula obtained, weathering voluntarily after the discarded several years, be suitable for making household pottery series products, as vase, flowerpot, money cylinder, animal or human's thing artwork etc., can temperature adjustment moisturizing voluntarily, eliminate peculiar smell, can effectively absorb the objectionable impuritiess such as free formaldehyde, benzene and ammonia.
Description
Technical field
The invention belongs to ceramic field, relate to a kind of red soil pottery and preparation method thereof.
Background technology
Pottery is the general name of pottery and porcelain.Chinese have just invented pottery as far back as about B.C. 8000-2000 (Neolithic Age).Stupalith is oxide compound, nitride, boride and carbide etc. mostly.Common stupalith has clay, aluminum oxide, kaolin etc.The general hardness of stupalith is higher, but plasticity-is poor.Except in the use of feeder, decoration, also play an important role in the development of science, technology.Ceramic raw material is that the original ample resources clay of the earth forms through quenching to get.And the character tool toughness of clay, it is plastic that normal temperature meets water, micro-ly dry can to carve, and absolutely dryly grinds; Burning can become pottery to fill water to 700 degree; Burn to 1230 degree of then porcelain, can not absorb water completely and corrosion-and high-temp-resistant.The elasticity of its usage, still has the application of various intention in culture today science and technology.
Summary of the invention
Main purpose of the present invention is to provide a kind of red soil pottery and preparation method thereof, not only energy-conservation in technique, and Products Eco environmental protection.
The present invention adopts following technical scheme:
A red soil pottery, is obtained by the raw material of following weight: red soil 48 parts, 6 parts, black earth, 3 parts, grey black stone, rhombspar 3 parts, diatom ooze 40 parts and water glass adhesive 0.5 ~ 1.5 part.
A making method for red soil pottery, is made up of following steps:
1), by the raw material of following weight: red soil 48 parts, 6 parts, black earth, 3 parts, grey black stone and rhombspar 3 parts, after mixing, add water and put into ball mill grinding 36 hours pulpings;
2) in the slurry of step 1) gained, add the diatom ooze of 40 weight parts, stir, then add the water glass adhesive of 0.5 ~ 1.5 weight part, again stirring obtains mud;
3) by step 2) mud of gained injects mould, and then the demoulding becomes base, then natural air drying 1 ~ 2 day, finally carries out repaired biscuit, swabbing and enters kiln;
4) after entering kiln, fire, first with 2h, temperature is raised to 200 DEG C, then with 3.5h, temperature is raised to 800 DEG C from 200 DEG C, finally with 2h, temperature is raised to 1080 DEG C from 800 DEG C, namely cooling kiln discharge obtains red soil pottery.
From the above-mentioned description of this invention, compared with prior art, the red soil pottery ecological, environmental protective of the present invention by adopting above-mentioned formula obtained, weathering voluntarily after the discarded several years, be suitable for making household pottery series products, as vase, flowerpot, money cylinder, animal or human's thing artwork etc., can temperature adjustment moisturizing voluntarily, eliminate peculiar smell, effectively can absorb the objectionable impuritiess such as free formaldehyde, benzene and ammonia; Making method of the present invention adopts 1080 DEG C of easy fireds, energy-conservation and production cost is low, and by coordinating of above-mentioned formula and making method, the red soil pottery yield rate produced is more than 96%.
Embodiment
Below by way of embodiment, the invention will be further described.
A red soil pottery, is obtained by the raw material of following weight: red soil 48 parts, 6 parts, black earth, 3 parts, grey black stone, rhombspar 3 parts, diatom ooze 40 parts and water glass adhesive 0.5 ~ 1.5 part.
A making method for red soil pottery, is made up of following steps:
1), by the raw material of following weight: red soil 48 parts, 6 parts, black earth, 3 parts, grey black stone and rhombspar 3 parts, after mixing, add water and put into ball mill grinding 36 hours pulpings;
2) in the slurry of step 1) gained, add the diatom ooze of 40 weight parts, stir, then add the water glass adhesive of 0.5 ~ 1.5 weight part, again stirring obtains mud;
3) by step 2) mud of gained injects mould, and then the demoulding becomes base, then natural air drying 1 ~ 2 day, finally carries out repaired biscuit, swabbing and enters kiln;
4) after entering kiln, fire, first with 2h, temperature is raised to 200 DEG C, then with 3.5h, temperature is raised to 800 DEG C from 200 DEG C, finally with 2h, temperature is raised to 1080 DEG C from 800 DEG C, namely cooling kiln discharge obtains red soil pottery.
Above are only a specific embodiment of the present invention, but design concept of the present invention is not limited thereto, all changes utilizing this design the present invention to be carried out to unsubstantiality, all should belong to the behavior of invading scope.
Claims (1)
1. a making method for red soil pottery, is made up of following steps:
1), by the raw material of following weight: red soil 48 parts, 6 parts, black earth, 3 parts, grey black stone and rhombspar 3 parts, after mixing, add water and put into ball mill grinding 36 hours pulpings;
2) in the slurry of step 1) gained, add the diatom ooze of 40 weight parts, stir, then add the water glass adhesive of 0.5 ~ 1.5 weight part, again stirring obtains mud;
3) by above-mentioned steps 2) mud of gained injects mould, and then the demoulding becomes base, then natural air drying 1 ~ 2 day, finally carries out repaired biscuit, swabbing and enters kiln;
4) after entering kiln, fire, first with 2h, temperature is raised to 200 DEG C, then with 3.5h, temperature is raised to 800 DEG C from 200 DEG C, finally with 2h, temperature is raised to 1080 DEG C from 800 DEG C, namely cooling kiln discharge obtains red soil pottery.