CN103396093A - Red soil earthenware and manufacturing method thereof - Google Patents

Red soil earthenware and manufacturing method thereof Download PDF

Info

Publication number
CN103396093A
CN103396093A CN2013103413340A CN201310341334A CN103396093A CN 103396093 A CN103396093 A CN 103396093A CN 2013103413340 A CN2013103413340 A CN 2013103413340A CN 201310341334 A CN201310341334 A CN 201310341334A CN 103396093 A CN103396093 A CN 103396093A
Authority
CN
China
Prior art keywords
parts
red soil
earthenware
red
raised
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103413340A
Other languages
Chinese (zh)
Other versions
CN103396093B (en
Inventor
陈永定
陈国生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Dehua Yonghuier Red Soil Pottery Co., Ltd.
Original Assignee
陈永定
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陈永定 filed Critical 陈永定
Priority to CN201310341334.0A priority Critical patent/CN103396093B/en
Publication of CN103396093A publication Critical patent/CN103396093A/en
Application granted granted Critical
Publication of CN103396093B publication Critical patent/CN103396093B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses red soil earthenware prepared from the raw materials of, by weight: 48 parts of red soil earth, 6 parts of black earth, 3 parts of black limestone, 3 parts of dolomite, 40 parts of diatomite mud, and 0.5-1.5 parts of water glass gel. According to the description, compared with prior art, with the formula, the prepared red soil earthenware is ecological and environment-friendly, and is automatically weathered after several years of abandonment. The red soil earthenware is suitable for preparing various household earthenware products such as vases, flower pots, money tube, and animals or figures crafts. The earthenware can automatically adjust temperature, retain moisture, and remove odor. With the earthenware, harmful substances such as free formaldehyde, benzene and ammonia can be effectively absorbed.

Description

A kind of red soil pottery and preparation method thereof
Technical field
The invention belongs to ceramic field, relate to a kind of red soil pottery and preparation method thereof.
Background technology
Pottery is the general name of pottery and porcelain.Chinese have just invented pottery as far back as approximately B.C. 8000-2000 (Neolithic Age).Stupalith is oxide compound, nitride, boride and carbide etc. mostly.Common stupalith has clay, aluminum oxide, kaolin etc.The general hardness of stupalith is higher, but plasticity-is poor.In the use at feeder, decoration, in the development of science, technology, also play an important role.Ceramic raw material is that the original ample resources clay of the earth forms through quenching to get.And the character tool toughness of clay, it is plastic that normal temperature is met water, and micro-doing can be carved, the absolutely dry mill; Burning to 700 degree can become pottery can fill water; Burning to 1230 is spent porcelain, can not absorb water fully and corrosion-and high-temp-resistant.The elasticity of its usage, still have the application of various intention in culture today science and technology.
Summary of the invention
Main purpose of the present invention is to provide a kind of red soil pottery and preparation method thereof, and is not only energy-conservation on technique, and the Products Eco environmental protection.
The present invention adopts following technical scheme:
A kind of red soil pottery is made by the raw material of following weight part proportioning: 0.5~1.5 part of 48 parts of red soils, 6 parts, black earth, 3 parts, grey black stone, 3 parts of rhombspars, 40 parts of diatom oozes and water glass adhesive.
A kind of making method of red soil pottery is comprised of following steps:
1) by the raw material of following weight part proportioning: 3 parts of 48 parts of red soils, 6 parts, black earth, 3 parts, grey black stone and rhombspars, after mixing, add water and put into ball mill and grind 36 hours pulpings;
2) toward the diatom ooze that adds 40 weight parts in the slurry of step 1) gained, stir, then add the water glass adhesive of 0.5~1.5 weight part, again stir and obtain mud;
3) by step 2) mud of gained injects mould, and then the demoulding becomes base, then natural air drying 1~2 day, finally carries out repaired biscuit, swabbing and enters kiln;
4) after entering kiln, fire, first with 2h, temperature is raised to 200 ℃, then with 3.5h, temperature is raised to 800 ℃ from 200 ℃, finally with 2h, temperature is raised to 1080 ℃ from 800 ℃, cooling kiln discharge namely obtains the red soil pottery.
As can be known by the above-mentioned description of this invention, compared with prior art, the red soil pottery ecological, environmental protective that the present invention makes by adopting above-mentioned formula, weathering voluntarily after the discarded several years, be suitable for making household pottery series products, as vase, flowerpot, money cylinder, animal or human's thing artwork etc., temperature adjustment moisturizing voluntarily, elimination peculiar smell, can effectively absorb the objectionable impuritiess such as free formaldehyde, benzene and ammonia; Making method of the present invention adopts 1080 ℃ of easy fireds, and is energy-conservation and production cost is low, and by coordinating of above-mentioned formula and making method, the red soil of producing is made pottery yield rate more than 96%.
Embodiment
Below the invention will be further described by embodiment.
A kind of red soil pottery is made by the raw material of following weight part proportioning: 0.5~1.5 part of 48 parts of red soils, 6 parts, black earth, 3 parts, grey black stone, 3 parts of rhombspars, 40 parts of diatom oozes and water glass adhesive.
A kind of making method of red soil pottery is comprised of following steps:
1) by the raw material of following weight part proportioning: 3 parts of 48 parts of red soils, 6 parts, black earth, 3 parts, grey black stone and rhombspars, after mixing, add water and put into ball mill and grind 36 hours pulpings;
2) toward the diatom ooze that adds 40 weight parts in the slurry of step 1) gained, stir, then add the water glass adhesive of 0.5~1.5 weight part, again stir and obtain mud;
3) by step 2) mud of gained injects mould, and then the demoulding becomes base, then natural air drying 1~2 day, finally carries out repaired biscuit, swabbing and enters kiln;
4) after entering kiln, fire, first with 2h, temperature is raised to 200 ℃, then with 3.5h, temperature is raised to 800 ℃ from 200 ℃, finally with 2h, temperature is raised to 1080 ℃ from 800 ℃, cooling kiln discharge namely obtains the red soil pottery.
Above are only a specific embodiment of the present invention, but design concept of the present invention is not limited to this, allly utilizes this design to carry out the change of unsubstantiality to the present invention, all should belong to the behavior of invading protection domain of the present invention.

Claims (2)

1. red soil pottery is made by the raw material of following weight part proportioning: 0.5~1.5 part of 48 parts of red soils, 6 parts, black earth, 3 parts, grey black stone, 3 parts of rhombspars, 40 parts of diatom oozes and water glass adhesive.
2. the making method of red soil pottery is comprised of following steps:
1) by the raw material of following weight part proportioning: 3 parts of 48 parts of red soils, 6 parts, black earth, 3 parts, grey black stone and rhombspars, after mixing, add water and put into ball mill and grind 36 hours pulpings;
2) toward the diatom ooze that adds 40 weight parts in the slurry of step 1) gained, stir, then add the water glass adhesive of 0.5~1.5 weight part, again stir and obtain mud;
3) by step 2) mud of gained injects mould, and then the demoulding becomes base, then natural air drying 1~2 day, finally carries out repaired biscuit, swabbing and enters kiln;
4) after entering kiln, fire, first with 2h, temperature is raised to 200 ℃, then with 3.5h, temperature is raised to 800 ℃ from 200 ℃, finally with 2h, temperature is raised to 1080 ℃ from 800 ℃, cooling kiln discharge namely obtains the red soil pottery.
CN201310341334.0A 2013-08-07 2013-08-07 A kind of red soil pottery and preparation method thereof Expired - Fee Related CN103396093B (en)