Summary of the invention
At the weak point that exists in the above-mentioned technology, it is low and handle and the prescription of the simple natural mineral matter dyeing industrial sewage of the technical process of purifying waste water treatment agent and preparation method thereof to the invention provides a kind of cost of manufacture.
For achieving the above object, the invention provides a kind of prescription of natural mineral matter dyeing industrial sewage treatment agent, formed by kaolinite, Tai-Ace S 150, sheet alkali, iron(ic) chloride and calcium carbonate, wherein, described each component obtains by following weight proportion: kaolinite accounts for 15%-25%, Tai-Ace S 150 30%-40%, sheet alkali 15%-30%, iron(ic) chloride 10%-15%, calcium carbonate 10%-15%.
Preferably, described each component obtains by following weight proportion: kaolinite accounts for 20%, Tai-Ace S 150 35%, sheet alkali 20%, iron(ic) chloride 13%, calcium carbonate 12%.
For achieving the above object, the invention provides a kind of making method of natural mineral matter dyeing industrial sewage treatment agent, comprising:
Kaolinite is carried out roasting and is ground into powder;
Sheet alkali is carried out powdered to be handled;
Get sheet alkali, iron(ic) chloride and the calcium carbonate that the kaolinite that carries out roasting and pulverization process, Tai-Ace S 150, powdered of formulation weight handle and mix successively, stir;
Pack is sealed to finished product.
The invention has the beneficial effects as follows: compared with prior art, prescription of natural mineral matter dyeing industrial sewage treatment agent provided by the invention and preparation method thereof, the deficiency of currently available products and the difficult problem that dyeing industrial sewage is handled have been solved, easy to use and production cost is low, can solve the pollution that dyeing industrial sewage causes from the source, purify dyeing industrial sewage, reached the sewage drainage standard of national regulation, can not cause secondary pollution to nature.
Embodiment
In order more clearly to explain the present invention, below the present invention is done to describe further.
Embodiment 1
1) kaolinite is carried out roasting and be ground into powder;
2) sheet alkali being carried out powdered handles;
3) getting above-mentioned components by weight percent of carrying out roasting and pulverization process is that 25% kaolinite, components by weight percent are 40% Tai-Ace S 150, above-mentioned to carry out components by weight percent that powdered handles be that 15% sheet alkali, components by weight percent are that 10% iron(ic) chloride and components by weight percent are that 10% calcium carbonate mixes successively, stirs;
4) pack is sealed to finished product.
Embodiment 2
1) kaolinite is carried out roasting and be ground into powder;
2) sheet alkali being carried out powdered handles;
3) getting above-mentioned components by weight percent of carrying out roasting and pulverization process is that 15% kaolinite, components by weight percent are 30% Tai-Ace S 150, above-mentioned to carry out components by weight percent that powdered handles be that 30% sheet alkali, components by weight percent are that 15% iron(ic) chloride and components by weight percent are that 10% calcium carbonate mixes successively, stirs;
4) pack is sealed to finished product.
Embodiment 3
1) kaolinite is carried out roasting and be ground into powder;
2) sheet alkali being carried out powdered handles;
3) getting above-mentioned components by weight percent of carrying out roasting and pulverization process is that 15% kaolinite, components by weight percent are 30% Tai-Ace S 150, above-mentioned to carry out components by weight percent that powdered handles be that 30% sheet alkali, components by weight percent are that 10% iron(ic) chloride and components by weight percent are that 15% calcium carbonate mixes successively, stirs
4) pack is sealed to finished product.
Embodiment 4
1) kaolinite is carried out roasting and be ground into powder;
2) sheet alkali being carried out powdered handles;
3) getting above-mentioned components by weight percent of carrying out roasting and pulverization process is that 20% kaolinite, components by weight percent are 35% Tai-Ace S 150, above-mentioned to carry out components by weight percent that powdered handles be that 20% sheet alkali, components by weight percent are that 13% iron(ic) chloride and components by weight percent are that 12% calcium carbonate mixes successively, stirs;
4) pack is sealed to finished product.
The dyeing industrial sewage treatment agent finished product that embodiment 4 is obtained is applied in the dyeing industrial sewage storage pool in hotel, carries out every test, and test process is as follows:
Test item: the CODcr in the water sample, BOD5, SS, NH3-N, TP, pH value.
Detected result such as following table (unit: mg/L)
Sample |
CODcr |
BOD5 |
SS |
NH3-N |
TP |
Sewage before handling |
650 |
300 |
362 |
60 |
8 |
Sewage after the processing |
45 |
9 |
10 |
6 |
1 |
The pH value of sewage is 9 before handling, and the pH value of handling back sewage is 7.In conjunction with last table as can be seen, dyeing industrial sewage treatment agent of the present invention has extraordinary treatment effect.
More than disclosed only be several specific embodiment of the present invention, but the present invention is not limited thereto, any those skilled in the art can think variation all should fall into protection scope of the present invention.