CN102995463A - Manufacture process of shell fabric with memory function - Google Patents
Manufacture process of shell fabric with memory function Download PDFInfo
- Publication number
- CN102995463A CN102995463A CN2012105143322A CN201210514332A CN102995463A CN 102995463 A CN102995463 A CN 102995463A CN 2012105143322 A CN2012105143322 A CN 2012105143322A CN 201210514332 A CN201210514332 A CN 201210514332A CN 102995463 A CN102995463 A CN 102995463A
- Authority
- CN
- China
- Prior art keywords
- fabric
- minutes
- uniform velocity
- minutes time
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacture process of a shell fabric with a memory function. The manufacture process comprises the following steps of: implementing cloth matching by a springback yarn fabric with 50D, the total branch number of 281T, the warp density of 205T and the weft density of 76T; continuous annealing the fabric; desizing the fabric by adding 1g-4g of refining agent, 1g-3g of degreaser and 4g-6g of caustic soda flakes into the fabric; dyeing the fabric by adding 0.3g-1g of chelating agent, 1g-2.5g of leveling and dispersing agent, 0.3g-1g of mending agent, 0.3g-1g of pH conditioning agent and 1g-3g of carriers; performing reduction washing on the fabric by adding 1g-3g of acid reducing agent into the fabric; then dewatering, feeding clean water, and adding 0.3g-1g of glacial acetic acid into the fabric in 3-5 minutes; and spreading and sizing the fabric, and packaging the finished shell fabric after inspection is finished. According to the manufacture process, the fabric is processed and woven by springback yarns with recovery characteristics, corresponding auxiliaries are added into the fabric in the drying procedure, and thus the shell fabric is gorgeous, is flexible, smooth and comfortable in handfeel, is fluffy and thick and has the good memory function after being processed by special processes. When the surface of the shell fabric is grasped and washed, the crinkles on the surface of the shell fabric disappear after being wiped by hand, and the shell fabric is as smooth as before.
Description
Technical field
The present invention relates to textile technology field, be specifically related to a kind of manufacture craft with memory function lining.
Background technology
Along with living standard improves constantly, people are more and more higher to the functional requirement of clothing cloth, have the normal heat-preserving function except requiring clothes, also will require comfortable and easy to wearly, during with skin contact, the sensation of meat arranged, and have more high-comfort.What at first consider when making fabric at present, is the performance indications such as flexibility, water imbibition, wrinkle resistance of fabric.Folding crape phenomenon can appear in a lot of fabrics after washing, affect the aesthetic property of people's dress.The wrinkle resistance of fabric then is that the memory function by fabric embodies, and currently used manufacture craft with memory function lining is comparatively loaded down with trivial details, and production cost is high.
Summary of the invention
The technical problem to be solved in the present invention is the defective for prior art, and a kind of manufacture craft with memory function lining is provided.
For solving the problems of the technologies described above, the present invention adopts following technical scheme: a kind of manufacture craft with memory function lining is characterized in that: carry out according to the following steps:
1), adopt 50D, total number be 281T, through close for 205T, filling density be that the resilience yarn grey cloth of 76T is joined cloth;
2), connect with 30-60 yards/minutes speed and to move back, temperature is 90-100
0C;
3), destarch: add following auxiliary agent by every premium on currency amount in the destarch process, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds refining agent 1-4g within 5-8 minutes time; Within 3-5 minutes time, at the uniform velocity add degreaser 1-3g; Within 5-10 minutes time, at the uniform velocity add sheet alkali 4-6g; 95-110
0Kept 30-60 minutes under the temperature conditions of C;
4), dyeing: add following auxiliary agent by every premium on currency amount in the dyeing course, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds chelating agent 0.3-1g within 3-5 minutes time; Within 3-6 minutes time, at the uniform velocity add Disperse Leveler 1-2.5g; Within 5-8 minutes time, at the uniform velocity add healant 0.3-1g; Within 5-10 minutes time, at the uniform velocity add PH conditioning agent 0.3-1g; Within 5-8 minutes time, at the uniform velocity add dyeing accelerant 1-3g; 115-125
0Kept 90-120 minutes under the temperature conditions of C;
5), reduction is washed: reduction is washed in the process and is added following auxiliary agent by every premium on currency amount, and step is: first with water temp. heating to 80-85
0C, average rate adds acidic reduction agent 1-3g within 8-10 minutes time, is incubated 20-30 minutes; Then draining, the laggard clear water of draining adds glacial acetic acid 0.3-1g neutralisation treatment within 3-5 minutes time, turned round 10 minutes;
6), spread: the cloth open-width of rope form is become the open width shape, drop on Bu Chenei for following process, speed is 40-50 yards/minutes;
7), typing: be 130-135 in its room temperature
0C, speed is under 15-35 m/mins the condition cloth cover to be finalized the design;
8), become the inspection packing: cloth is tested pack after grading.
The present invention adopts the special yarn (resilience yarn) with recovery characteristics, weave grey cloth through textile process, in dyeing process, in dye liquor, add corresponding auxiliary agent, process by special process, make that fabric is more gorgeous, feel is more soft, sliding tender, comfortable, have a fluffy solid sense, stronger memory function effect is arranged, cloth cover through grab gentle and washing after, handle flat wiping after, the wrinkle of cloth cover disappears, and is as before smooth.
The specific embodiment
Be described further below in conjunction with the specific embodiment:
Embodiment 1, and described manufacture craft with memory function lining is carried out according to the following steps:
1), adopt 50D, total number be 281T, through close for 205T, filling density be that the resilience yarn grey cloth of 76T is joined cloth;
2), connect with 30-60 yards/minutes speed and to move back, temperature is 90-100
0C;
3), destarch: add following auxiliary agent by every premium on currency amount in the destarch process, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds refining agent 1g within 5-8 minutes time; Within 3-5 minutes time, at the uniform velocity add degreaser 1g; Within 5-10 minutes time, at the uniform velocity add sheet alkali 4g; 95-110
0Kept 30-60 minutes under the temperature conditions of C;
4), dyeing: add following auxiliary agent by every premium on currency amount in the dyeing course, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds chelating agent 0.3g within 3-5 minutes time; Within 3-6 minutes time, at the uniform velocity add Disperse Leveler 1g; Within 5-8 minutes time, at the uniform velocity add healant 0.3g; Within 5-10 minutes time, at the uniform velocity add PH conditioning agent 0.3g; Within 5-8 minutes time, at the uniform velocity add dyeing accelerant 1g; 115-125
0Kept 90-120 minutes under the temperature conditions of C;
5), reduction is washed: reduction is washed in the process and is added following auxiliary agent by every premium on currency amount, and step is: first with water temp. heating to 80-85
0C, average rate adds acidic reduction agent 1g within 8-10 minutes time, is incubated 20-30 minutes; Then draining, the laggard clear water of draining adds glacial acetic acid 0.3g neutralisation treatment within 3-5 minutes time, turned round 10 minutes;
6), spread: the cloth open-width of rope form is become the open width shape, drop on Bu Chenei for following process, speed is 40-50 yards/minutes;
7), typing: be 130-135 in its room temperature
0C, speed is under 15-35 m/mins the condition cloth cover to be finalized the design;
8), become the inspection packing: cloth is tested pack after grading.
Embodiment 2, and described manufacture craft with memory function lining is carried out according to the following steps:
1), adopt 50D, total number be 281T, through close for 205T, filling density be that the resilience yarn grey cloth of 76T is joined cloth;
2), connect with 30-60 yards/minutes speed and to move back, temperature is 90-100
0C;
3), destarch: add following auxiliary agent by every premium on currency amount in the destarch process, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds refining agent 3g within 5-8 minutes time; Within 3-5 minutes time, at the uniform velocity add degreaser 2g; Within 5-10 minutes time, at the uniform velocity add sheet alkali 5g; 95-110
0Kept 30-60 minutes under the temperature conditions of C;
4), dyeing: add following auxiliary agent by every premium on currency amount in the dyeing course, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds chelating agent 0.7g within 3-5 minutes time; Within 3-6 minutes time, at the uniform velocity add Disperse Leveler 2g; Within 5-8 minutes time, at the uniform velocity add healant 0.7g; Within 5-10 minutes time, at the uniform velocity add PH conditioning agent 0.7g; Within 5-8 minutes time, at the uniform velocity add dyeing accelerant 2g; 115-125
0Kept 90-120 minutes under the temperature conditions of C;
5), reduction is washed: reduction is washed in the process and is added following auxiliary agent by every premium on currency amount, and step is: first with water temp. heating to 80-85
0C, average rate adds acidic reduction agent 2g within 8-10 minutes time, is incubated 20-30 minutes; Then draining, the laggard clear water of draining adds glacial acetic acid 0.7g neutralisation treatment within 3-5 minutes time, turned round 10 minutes;
6), spread: the cloth open-width of rope form is become the open width shape, drop on Bu Chenei for following process, speed is 40-50 yards/minutes;
7), typing: be 130-135 in its room temperature
0C, speed is under 15-35 m/mins the condition cloth cover to be finalized the design;
8), become the inspection packing: cloth is tested pack after grading.
Embodiment 3, have the manufacture craft of memory function lining, carry out according to the following steps:
1), adopt 50D, total number be 281T, through close for 205T, filling density be that the resilience yarn grey cloth of 76T is joined cloth;
2), connect with 30-60 yards/minutes speed and to move back, temperature is 90-100
0C;
3), destarch: add following auxiliary agent by every premium on currency amount in the destarch process, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds refining agent 4g within 5-8 minutes time; Within 3-5 minutes time, at the uniform velocity add degreaser 3g; Within 5-10 minutes time, at the uniform velocity add sheet alkali 6g; 95-110
0Kept 30-60 minutes under the temperature conditions of C;
4), dyeing: add following auxiliary agent by every premium on currency amount in the dyeing course, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds chelating agent 1g within 3-5 minutes time; Within 3-6 minutes time, at the uniform velocity add Disperse Leveler 2.5g; Within 5-8 minutes time, at the uniform velocity add healant 1g; Within 5-10 minutes time, at the uniform velocity add PH conditioning agent 1g; Within 5-8 minutes time, at the uniform velocity add dyeing accelerant 3g; 115-125
0Kept 90-120 minutes under the temperature conditions of C;
5), reduction is washed: reduction is washed in the process and is added following auxiliary agent by every premium on currency amount, and step is: first with water temp. heating to 80-85
0C, average rate adds acidic reduction agent 3g within 8-10 minutes time, is incubated 20-30 minutes; Then draining, the laggard clear water of draining adds glacial acetic acid 1g neutralisation treatment within 3-5 minutes time, turned round 10 minutes;
6), spread: the cloth open-width of rope form is become the open width shape, drop on Bu Chenei for following process, speed is 40-50 yards/minutes;
7), typing: be 130-135 in its room temperature
0C, speed is under 15-35 m/mins the condition cloth cover to be finalized the design;
8), become the inspection packing: cloth is tested pack after grading.
Below the present invention is described in detail, the above only is the present invention's preferred embodiment, when not limiting practical range of the present invention, namely allly does impartial change and modify according to the application's scope, all should still belong in the covering scope of the present invention.
Claims (1)
1. manufacture craft with memory function lining is characterized in that: carry out according to the following steps:
1), adopt 50D, total number be 281T, through close for 205T, filling density be that the resilience yarn grey cloth of 76T is joined cloth;
2), connect with 30-60 yards/minutes speed and to move back, temperature is 90-100
0C;
3), destarch: add following auxiliary agent by every premium on currency amount in the destarch process, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds refining agent 1-4g within 5-8 minutes time; Within 3-5 minutes time, at the uniform velocity add degreaser 1-3g; Within 5-10 minutes time, at the uniform velocity add sheet alkali 4-6g; 95-110
0Kept 30-60 minutes under the temperature conditions of C;
4), dyeing: add following auxiliary agent by every premium on currency amount in the dyeing course, step is: first with water temp. heating to 30-40
0C at the uniform velocity adds chelating agent 0.3-1g within 3-5 minutes time; Within 3-6 minutes time, at the uniform velocity add Disperse Leveler 1-2.5g; Within 5-8 minutes time, at the uniform velocity add healant 0.3-1g; Within 5-10 minutes time, at the uniform velocity add PH conditioning agent 0.3-1g; Within 5-8 minutes time, at the uniform velocity add dyeing accelerant 1-3g; 115-125
0Kept 90-120 minutes under the temperature conditions of C;
5), reduction is washed: reduction is washed in the process and is added following auxiliary agent by every premium on currency amount, and step is: first with water temp. heating to 80-85
0C, average rate adds acidic reduction agent 1-3g within 8-10 minutes time, is incubated 20-30 minutes; Then draining, the laggard clear water of draining adds glacial acetic acid 0.3-1g neutralisation treatment within 3-5 minutes time, turned round 10 minutes;
6), spread: the cloth open-width of rope form is become the open width shape, drop on Bu Chenei for following process, speed is 40-50 yards/minutes;
7), typing: be 130-135 in its room temperature
0C, speed is under 15-35 m/mins the condition cloth cover to be finalized the design;
8), become the inspection packing: cloth is tested pack after grading.