Polymeric FoamsJosé Ignacio Velasco, Marcelo Antunes Advances in nanotechnology have boosted the development of more efficient materials, with emerging sectors (electronics, energy, aerospace, etc.) demanding novel materials to fulfill the complex technical requirements of their products. This is the case of polymeric foams, which may display good structural properties alongside functional characteristics through a complex composition and (micro)structure in which a gas phase is combined with rigid ones, mainly based on nanoparticles, dispersed throughout the polymer matrix. In recent years, there has been an important impulse in the development of nanocomposite foams, extending the concept of nanocomposites to the field of cellular materials. This, alongside developments in new advanced foaming technologies which have allowed the generation of foams with micro, sub-micro, and even nanocellular structures, has extended the applications of more traditional foams in terms of weight reduction, damping, and thermal and/or acoustic insulation to novel possibilities, such as electromagnetic interference (EMI) shielding. This Special Issue, which consists of a total of 22 articles, including one review article written by research groups of experts in the field, considers recent research on novel polymer-based foams in all their aspects: design, composition, processing and fabrication, microstructure, characterization and analysis, applications and service behavior, recycling and reuse, etc. |
Common terms and phrases
ability absorbent according acoustic addition agent analysis Appl applications authors average behavior building carbon cell cellular structure cellulose characteristics characterization chemical China coefficient compared Compos composite foams compressive conductivity CrossRef curves decreased degradation deionized water density determined effect electrical energy enhanced epoxy Equation expansion expansion ratio experimental fiber Figure fire flame retardant flame spreading foam composites function graphene heat higher impact improved increased indicates insulation layer loss mass materials matrix measured mechanical properties method modulus morphology nanocomposite nucleation observed obtained optimization particles peak performance phase Polym prepared presented PU foam range reaction reduced reinforced relative residue resistance respectively RPUF samples showed shown in Figure solid solution sound absorption specimens strength stress structure surface Table temperature thermal values Wang waste weight Zhang